By Barry D. Lichter, Pierre Sommelet

High-temperature heat contents of InAs and GaAs were measured over the temperature range 400°K to temperatures above the melting points using a di-phenyl ether drop calorimeter. Smoothed values of the thermal properties have been derived and tabulated at even temperature interuals . The heats of fusion of InAs and GaAs were determined as, respectively, 8790 ± 200 and 12,590 ± 300 cal per g-atom at the respective melting points of 1210º ± and 1513º ± 1°K, yielding entropies of fusion of 7.26 * 0.16 and 8.32 ± 0.20 cal perºK per g-atom, respectively. A general discussion of the thermal properties of III-V com-pounds is given. THE low-temperature heat capacities of InAs and GaAs have been determined by Piesbergen.1Using a dynamic temperature modulation technique, Miller2 has determined the heat capacities of the compounds as well as GaSb and Ge between room temperature and 650°K; however, it has been observed that values determined by drop calorimetry for GaSb3 and for germanium4 are consistently about 5 pct lower than Miller's results. Cox and Pool10 report values for the heat content of InAs and GaAs and the heat of fusion of InAs. No value for the heat of fusion of GaAs appears to have been previously reported. This paper reports results of high-temperature heat content investigations of InAs and GaAs measured in the range 400" to above 1500°K employing a diphenyl ether drop calorimeter. These results, together with our previous results on III-Sb compounds3 as well as heat-content measurements5 of solid InP and Gap, are used in a general discussion of these compounds. EXPERIMENTAL PROCEDURES High-purity samples of the compounds, stoichio-metric to ±0.1 at. pct, were supplied in the form of crushed crystal fragments by Dr. Carl Thurmond of the Bell Telephone Laboratories. The sample preparation, description of the calorimeter, and details of the heat content measurement have been previously described.3 Samples were sealed in evacuated silica capsules and suspended by a Pt-Rh wire in a Pt-wound vertical tube furnace, heated to temperature

Jan 1, 1970

By K. R. Evans

The deformation mechanisms occurring in polycrys-talline, commercially pure titanium and a Ti-8 pct A1 alloy have been investigated and compared to earlier results by Levine on high-purity titanium single crystals and by Conrad on commercially pure titanium. In accord with Levine, two consecutive deformation mechanisms are observed to exist below 500°K with the transition temperature between mechanisms, Tc, strongly dependent upon interstitial composition. T, is found to be 210°. 375° -430°, and 450°K for alloys A large number of investigations have been conducted to determine the rate-controlling mechanisms of plastic deformation occurring in fcc and bcc metals. Very few investigations of a similar nature have been conducted for hexagonal metals. In fact, until very recently, magnesium is the only hexagonal metal which has been systematically investigated for determination of the rate-controlling deformation mechanisms.1"3 From these investigations, it was concluded that basal slip below 420°K occurs by the intersection of forest dislocations,1'3 while for prismatic slip the Peierls mechanism is rate-controlling at low temperatures with interstitial compositions of 0.024, 0.42, 0.61, and 1.13 at. pct expressed in terns of oxygen equivalents. The low-temperature mechanism is found to be an impurity obstacle mechanism in contrast to Levine's earlier conclusion of the Peierls barrier. Measurement of the activation parameters for deformation and estimation of the force-distance profile of the obstacles show their retarding force to be effective over longer distances from the obstacle as the interstitial composition increases. and thermally activated cross slip at higher temperatures. 2 The potential technological importance of titanium alloys has prompted recent studies of the deformation and fracture characteristics of titanium and its alloys. 4-8 Levine' systematically investigated the low-temperature deformation behavior of high purity titanium single crystals oriented for either basal or prismatic slip. It was concluded that the Peierls mechanism was rate-controlling at temperatures below 210°K, while above this temperature an undefined mechanism was rate-controlling. Conrad 7,8 concluded from an analysis of the composition dependence of the critical shear stress at 0°K and measurement of the activation parameters that the low-temperature deformation of titanium is controlled by an impurity

Jan 1, 1969

By C. Y. Cheng

THE purpose of this note is to show that the dislocation mechanism controlling the creep of Fe-4 pet Si alloy1 may equally account for the behavior of a-Fe2 over the same temperature range. A recent study of the creep behavior of a-Fe has been made by Ishida et al.2 Their results were in agreement with the mechanism of nonconservative motion of jogged screw dislocations over the entire range of temperatures investigated, from 480° to 1045°K. However, the observed creep rate was much higher than that which could be accounted for by the above model unless the authors assumed that pipe diffusion became significant below 775°K. More recently, Cheng et al.1 inves-gated the creep of Fe-4 pet Si alloy over about the same temperature range and found that the results could be correlated fairly well with a dislocation climb mechanism as represented by Eq. [l]. Proceeding as shown previously,1 if creep is controlled by a single climb mechanism, at intermediate stresses, the shear creep rate, y, can be represented by where n and K are material constants {K is independent of the temperature but dependent on the structure, that is, K decreases during the primary stage and reaches a steady-state value over the secondary stage of creep), t is the applied shear stress, G is the shear modulus, gc is the free energy of activation for creep (usually equal to that for self-diffusion, gd), and RT has the usual meaning. By solving for y, the apparent activation energy for creep, Q which can be determined experimentally, is given by where hc is the enthalpy of activation for creep which usually is also equal to that for self-diffusion, h^. By using Eq. [2], the data in Fig. 2 of Ref. 2 can be re-plotted as shown in Fig. 1. By comparing the two figures, it is seen that the slight increase in the apparent activation for creep over Region II, as noted in Fig. 2 of Ref. 2, is due to the influence of temperature on the shear modulus rather than of the stress on the

Jan 1, 1969

By W. C. Knopf, G. Samsel

For several years International Minerals & Chem-ical Corp. has used a radiation method to assay potassium content of products from potash and feldspar beneficiation. The procedure is rapid, accurate, and inexpensive and is easily handled, if necessary, by nontechnical personnel. Data are presented to show the accuracies that may be expected if the technique is used for control of pilot plants or large-scale plants. Natural potassium is composed of three isotopes —K, K and K. Five other isotopes, artificially produced, have been detected. In natural potassium only the K isotope, with a half life of 1.4x10 years, is radioactive. Its modes of decay are beta and gamma rays, positrons, and x-rays. Only the more abundant beta rays, however, are important in radiation measurements using geiger tubes. Barnes and Salley' measured radiation of potassium salts in solution in 1943. Gaudin and Parnell2 first reported the use of solid salts arranged in a vessel surrounding the ß counter in 1948. Later, Scheel used the method to assay potassium content of various crude and finished potash salts. Experimental: Dip-type Geiger-Muller tubes (TGC-5) supplied by Tracerlab Co. were used in all radiation counting measurements. The tube was encompassed by a glass container about M in. larger in diameter than the tube. This container, which served as a sample holder, was closed at the bottom with a rubber stopper to facilitate removing the samples. Samples were not weighed, but about 40 g of sample were needed for each test. Electrical impulses from the tube were counted on either a Tracerlab scaler or a rate meter. To obviate the need for constant attendance, preset features were incorporated into the scalers, so that at a predetermined time or count the units were automatically deactivated. When rate meters were used, counting rates were read directly from instrument or from a recorder used in conjunction with the rate meter. Each tube was calibrated, according to the manufacturer's instructions, to determine the correct operating voltage to insure reproducible results. A linear calibration plot of percent K2O vs counting rate was also obtained for each tube by recording the counting rate plus background count of several standards of different K2O content chemically analyzed by the chloroplatinate method.' These standards were of approximately the same particle size distribution as samples to be assayed. Specific background count caused by cosmic rays and other surrounding radiation was checked periodically by counting a sample of pure NaCl. Fig. 1 is a representative calibration plot. Assays were determined directly from the standard plot or calculated by subtracting the background count from the counting rate, then multiplying by the slope of the line. Chemical assays of the test samples were made by the Sherril method," a flame photometric technique, or the chloroplatinate method. Data: The radiation assay method has been used for three years by International Minerals & Chemical Corp. in the laboratory and in pilot plants processing ores containing potassium. These dry concentration plants process sylvinite and langbeinite ores at Carlsbad, N. M., and feldspar ores at Top-sham, Maine. Sylvinite ore is predominantly a mixture of syl-vite (impure KCl) and halite (impure NaCl). Contaminants include sulfates, such as langbeinite (2MgSO - K2SO4), kieserite (MgSO H2O), poly-halite (MgSO4.K2SO, 2CaSO, . 2H2O), and slimes. Langbeinite ore is predominantly langbeinite and halite with small amounts of sylvite, sulfates other than langbeinite, and slimes. Several variables, in addition to correct calibration and standardization of tubes, were found to be important in obtaining reproducible results. Particle size distribution of standard samples should be

Jan 1, 1959

Edward K. Landis, Philadelphia, Pa.: In studying Mr. Thackray's paper it seemed that a critical comparison of the results from different methods therein reported would he of interest. For this purpose Table I. was constructed by grouping all determinations made by the same method, and the probable errors were calculated. In this table all chemists titrating with permanganate (A1, E, F, G and 0 of Mr. Thackray's paper) are classed under "Emmerton;" those titrating with nitric acid (C, J, S and Y) under " Handy; " those re Probable error of result: a, ±0.0008996; b, ±0.000694; c, ±0.00107; d, ±0.00115; e, ±0.000674; f, ±0.000473; g, ±0.003675; h, ±20.0007959; i,0.000.5098; k, ±0.0008303. Probable error of single determination: a, ±0.001989; b, ±0.001547; c, ±0.00214; d, ±0.0023;e, ±0.00116;f, ±0.000818;g, ±0.0019;h, ±0.00224; i, 40.00143; k, ±0.00234. The formula for calculating the probable error is 0.6745, where N (N— 1)' S is the sum of the squares of the differences from the mean and N is the number of determinations.

Jan 1, 1897

By Glenn C. Waterman

Richard Strong (Oliver Iron Mining Div., U. S. Steel Corp.)—Mr. Waterman states (p. 59, Trans., January 1954): "Core-sludge combining factors have been calculaied for any combination of core-sludge recovery on the basis of several logical assumptions: 1—The sludge sample loses reliability geometrically as sludge recovery drops. 2—The sludge sample should not be used if the percentage of sludge return is less than the percentage of core recovered. 3—A core sample should receive a weighting at least equal to the percentage of core recovery." Assumptions 1 and 2 seem justified at Chuquicamata and most geologists would agree to the validity of assumption 3. However, contrary to the statement quoted above, the core sample does not in general receive a weighting at least equal to the percentage of core recovery when the Chuquicamata methgd is used. Furthermore, the basic Chuquicamata method is identical to the Longyear or relative volume core-sludge assay combining method. Finally, the Chuquicamata method does not, in its present form, reflect true geometric loss in sludge sample reliability according to the relationship L = AR (N-1) The basic equations representing the two steps of the Chuquicamata method can be combined algebraically as follows (using the symbology of the original article except as noted): Vol A + B Assay 2 = ASA = Assay 1 Vol A VolB Core Assay [I] Vol A CA.F + ASA (100 —F) Combined grade =[21 100 Pct where F and (100 — F) are the core and adjusted sludge assay factors from Fig. 3. Substituting Eqs. 1 and 2 and collecting terms Combined grade = Vol B Vol A + B CAF (100—-F) + Assay 1 (100-F) Vol A Vol A 100 pct Eq. 3 is a unified and general statement of the Chuquicamata method. The true core factor includes not only the factor F from Fig. 3 but also the quantity VolB ------------- (100 — F), which is implicit in the value of Vol A the adjusted sludge assay. This quantity is real and positive for all values of F and core recovery less than 100. Therefore the true core factor is always less than F except when F is equal to 100. If sludge recovery is 100 pct, Eq. 3 can be further simplified as follows: Let F = percentage of core recovered. Let Vol A = Vdh (100 Pct — Pct CR) where Vdh is the total volume of the sampled interval and let Vol B = (Vdh — Vc.) Pct CR where V, is the core volume in the sampled interval at 100 pct core recovery. Then combined grade = Vo V. CA Pct CR- + Assay 1, 100 Pct — Pct CR Vdh Vdh [4] 100 Pct Eq. 4 shows that when sludge recovery is 100 pct the laboratory sludge assay receives significant weight in the Chuquicamata method, even at 100 pct core recovery. The maximum weight assigned to the laboratory sludge assay depends on drillhole size, as follows: Eq. 4, with suitable changes in symbology, is identical to Royce's formula 8,' which is a statement of the Longyear or relative volume method of combining core and sludge assays. If Mr. Waterman's assumption 3 is of paramount concern to the geologist, the Royce method (for core recoveries of 60 pct and above) or a method employing the percentage of core recovered as a core weighting factor are the only recognized methods known to the writer which achieve the desired result. A modification of the latter method embodying Mr. Waterman's assumptions 1 and 2 would result from applying the factors from Fig. 3 directly to the laboratory core and sludge assays.

Jan 1, 1956

By C. Norman Cochran, James L. Brandt

ALTHOUGH gas in aluminum and its effect on aluminum products have been the subject of a number of papers, not many quantitative determinations of the hydrogen content of solid aluminum and its alloys have been recorded in the literature. For solid aluminum samples, four investigators have reported hydrogen contents which appear reasonable compared with the hydrogen solubility of 0.7 ml per 100 g, STP, in molten aluminum at 660°C established by Ransley and Neufeld' and verified by Opie and Grant' and Ransley and Talbot. Sloman," who used a vacuum fusion procedure, reported the hydrogen content of some high purity aluminum as 0.66 ml per 100 g, STP. Griffith and Mallett, employing the tin fusion method, reported the internal hydrogen content of six different aluminum alloys as ranging from less than 0.1 ml per 100 g, STP, for 1100 alloy to 0.7 ml per 100 g, STP, for 4043 alloy (previously 43S, a 5 pct Si alloy). Eborall and Ransley," using a solid extraction of the gases at 600°C, reported hydrogen contents ranging from 0.1 ml per 100 g, STP, to 1 ml per 100 g, STP. Ransley and Talbot reported that several thousand analyses on 99.2 pct and higher purity aluminum as well as Duralumin type alloys indicated hydrogen contents ranging from 0.1 ml per 100 g, STP, to 0.5 ml per 100 g, STP.

Jan 1, 1957

Ahrenholz, Herman William, Jr., Student, Lehigh Univ Bethlehem, Pa. '35 Allen, Carl A., Student, Colorado School of Mines Golden, Colo. '35 Allen, Paul W., Student, Mass. Inst. of Tech Cambridge, Mass. '35 Allen, R. M., Jr., Student, Virginia Polytechnic Inst., "G" Co Blacasburg, Va. '35 Amberger, K. H., Student, Michigan College of Min. & Tech Houghton, Mich. '35 Andersen, Burton Lee, Student, School of Mines, Univ. of Washington Seattle, Wash. '35 Anderson, Joseph S., Student, Univ. of Texas El Paso, Tex. '35 Anderson, R. C., Student, Univ. of Washington Seattle, Wash. '35 Ansel, Gerhard 627 Clyde St., Pittsburgh, Pa. '34 Anutta, Frederick P., Student, Michigan College of Min. & Tech Houghton, Mich. '35 Apsouri, Constantin N., Graduate Student, Univ. of Arizona Tucson, Ariz. '35 Arakelian, Haig Mark, Student, Mass. Inst. of Tech Cambridge, Mass. '34 Archer, George K 1420 Court Pl., Denver, Colo. '34 Argall, George O., Jr., K. E. House Golden, Colo. '35 Argiielles, Alfredo, Student, Univ. of Texas El Paso, Tex. '35 Atwater, Ralph, Student, South Dakota School of Mines Rapid City, S. D. '35 Austin, Robert B., Miner, Page Mine, Federal Min. & Smelt. CoSpokane, Wash. '34

Jan 1, 1934

By K. N. Han, H. Lee, M. C. Fuerstenau

An investigation of the recovery of finely-divided cassiterite and silica particles less than 1 µm (1200 mesh) in size has been carried out using packed and fluidized beds. The bed particles used included cassiterite and silica particles ranging from 44 to 210 µm (325 to 70 mesh). Effects of various system parameters on the recovery and selectivity of cassiterite fines were investigated. System parameters included pH of the slurry solution, superficial velocity, slurry concentration, and bed particle sizes. High recoveries of cassiterite fines were obtained at pH 4.0 and slow slurry flow rates. In a packed bed system, recovery of cassiterite fines was greater than 95%, while that of silica fines under the same conditions was about 35%. Although the total recovery per pass is not as good as the packed bed, the fluidized bed system exhibits good recovery in general and an excellent selectivity of cassiterite fines. There is an optimum superficial velocity, vo, for the rate of fine particle uptake and the apparent rate constant has the form of Kvo1/2- K'vo, where K and K' are system constants.

Jan 1, 1985

By D. Argyriades, G. Derge, G. M. Pound

The electrical conductance of molten FeS was studied as a function of temperature and composition. It was found that stoi-chiometric FeS (36.5 pct S) shows a minimum specific conductance of 400 ohm-1 cm-1. For the Fe-rich melts the conductivity increases with increasing amount of iron to about 4850 ohm-1' cm-I at 26 pct sulfur. For the sulfur-rich melts the conductivity increases with increasing amount of sulfur until it reaches a maximum of 1300 ohm1 cm-1 for 37.4 pct S and decreases to 800 ohm-1 cm-1 for 38.3 pct sulfur. It is concluded that molten stoichiometric FeS is an intrinsic semiconductor in which the forbidden gap in the electron energy level diagram is quite narrow. Excess sulfur acts as an acceptor impurity in providing a component of positive hole conduction, while excess iron acts as a donor impurity to increase the n-type conduction. K. Bornemann and G. von Ftauschenplatl used a four-terminal, direct-current cell to study the electrical conductance of molten copper sulfide. Their measurements showed a high conductivity, of the order of 100 ohm-1 cm-" and a positive temperature coefficient. From electrolysis studies, Savelsberg2 concluded that molten Cu2S and molten FeS are electronic conductors. Further. he found that molten FeS has a high specific conductance, of the order of 1500 ohm-' cm-', and a small negative temperature coefficient. Pound, Derge, and Osuch,3 using an ac Kelvin circuit and a four-terminal cell, measured the specific conductance of molten Cu,S, molten FeS, and various mixtures. They found that the specific conductance of the solutions followed a roughly additive rule of mixtures. Yang, Pound, and Derge4 showed from electrolysis measurements that the mechanism of electrical conduction in molten Cu2S, FeS, and mattes is primarily electronic. Further, they observed that small additions of CuCl suppress the electronic conduction whereupon the system behaves ionically.

Jan 1, 1960

By J. L. Weeks, K. F. Smith

IN order to determine the magnitude of thermal conductivity changes resulting from alloying vanadium with titanium and a few other elements, several sam~les were PrePared and measured. The thermal conductivity -values reported herein in Table I were determined with an apparatus previously described.' As in recently reported2 determinations on uranium and uranium alloys, whose thermal conductivities are in the same range as vanadium," the accuracy of the values was checked by using synthetic sapphire." The error in the measurement is estimated to be '-3 pct or 0.003 cal sec-1 cm-l "C-1, whichever is larger. The vanadium used in preparing the samples was the calcium-reduced type and was supplied by the Electro Metallurgical Co. as 99.6+ pct pure. All alloying elements used in the preparations were 99+ pct pure. A nonconsumable tungsten electrode arc furnace was used for melting the alloys and, without opening the furnace, each ingot was re-melted a number of times to insure homogeneity. The samples as prepared by the Armour Research Foundation were machined from as forged material without annealing. Acknowledgment The note is based on work performed under the auspices of the AEC. References 'J. L. Weeks and R. L. Seifert: Apparatus for the Measurement of the Thermal Conductivity of Solids. Review of Scientific Instruments (1953) 24, pp. 1054-1057. 2 J. L. Weeks: Thermal Conductivity of Uranium and Several Uranium Alloys. Trans. AIME (1955) 203, p. 192; Journal of Metals (January 1955). 3C. A. Hampel: Rare Metals Handbook. (1954) p. 593. New York. Reinhold Publishing Corp. Thermal conductivity of vanadium is given as 0.074 cal sec-1 cm- '°C-1 at 100°C. 4 J. L. Weeks and R. L. Seifert: Note Regarding the Thermal Conductivity of Synthetic Sapphire. Journal Amer. Ceramic Soc. (1952) 35, p. 15. At 70°C, K = 0.071 cal sec-l cm-l °C-1.

Jan 1, 1956

By K. E. Starling

Phase equilibria data were used to develop an equation-of-state correlation for complex hydrocarbon mixtures, thereby circumventing difficulties associated with use of pressure-volume-temperature data. Equilibrium phase data for two condensate reservoir fluids were used to determine equation-of-state parameters for hydrocarbons as heavy as C22H46 in a modified form of the Benedict-Webb-Rubin equation of state. Comparative tests of K-values from the resultant correlation were made with data for condensate reservoir, separator and gas plant absorber mixtures. Generally, for temperatures above OF and computed liquid densities below 0.55 Ib-mole/cu ft, the modified BIVR equation predicted K-values in close agreement with the experimental data. INTRODUCTION Accurate predictions of thermodynamic behavior for complex hydrocarbon mixtures are necessary for many calculations in the petroleum industry. Because of the relatively high cost of extensive experimental data, many correlations for prediction of phase behavior have been developed. Some of these, such as the correlation of K-values presented in the NGAA Equilibrium Ratio Data Book, are totally empirical.l Others, such as the Benedict-Webb-Rubin (BWR) equation-of-state method, are semitheoretical.2-4 Unfortunately, published correlation methods often do not accurately predict the phase behavior of complex hydrocarbon mixtures, principally because of inadequate representation of the effects of components heavier than decane. This paper presents a new approach to this problem in which basic equation-of-state relations including heavy hydrocarbon effects are applied. Equilibrium phase data for two condensate reservoir fluids containing hydrocarbons as heavy as C22H46 are used to correlate component K-values. The BWR equation was chosen as the prototype equation of state for this study because of its proven capability for accurately predicting phase behavior and thermodynamic properties of light - hydrocarbon mixtures? Research was directed toward development of BWR parameters for the heavy hydrocarbons and modifications of the mathematical form of the BWR equation for application to complex hydrocarbon mixtures. The new equation-of-state approach presented differs considerably from previous methods in that phase equilibria rather than PVT data are used for determination of equation-of-state parameters. It is an explicit approach since the parameters are determined directly from mixture data. As such, it does not encounter problems inherent in the implicit method used by Benedict, Webb and Rubin 2-4 and numerous other investigators—one in which mixture parameters were postulated to be functions of the pure component parameters. The pure component BWR parameters, in turn, were determined from experimental PVT data. This method has been limited to mixtures containing components lighter than decane because of lack of vapor phase PVT data. Studies have been reported in which BWR parameters have been determined explicitly from PVT data for binary mixtures.6-8 However, since small concentrations of heavier components have only a minor effect on PVT behavior, it is doubtful that these explicit methods would yield useful results for condensate systems. Ellington and Eakin9 have shown that the accuracy of K-values predicted by an equation of state developed from mixture PVT data probably would be more than an order of magnitude lower than the accuracy of the PVT data. On the other hand, an equation of state utilizing parameters developed from phase equilibria data should predict K-values with accuracy comparable to the accuracy of the experimental phase compositions. This work applies this explicit approach with the objective of improving hydrocarbon mixture phase behavior predictions. Results are evaluated by comparing predicted and experimental K-values at reservoir, separator and gas plant

Jan 1, 1967

By Richard W. Markley

A centralized online data acquisition system has been developed by the U.S. Bureau of Mines Pittsburgh Mining and Safety Research Center for rapidly digitizing, storing, and processing experimental signals originating up to 1100 feet away from a central computer. This system, which services seven laboratories, is currently based on a CDC System 17 1/- computer with 56K of semiconductor memory, four disk drives (one shared online with a CDC 1700), two magnetic tape drives, high-speed A/D hardware, and other input/output peripherals. The laboratories are linked to the central computer by 15-pair cables and signal conditioners and to the computer's communications controller by modems and current loops. The A/D throughput rate is approximately 30,000 samples per second (9 bit plus sign resolution) and permits scanning about 30 instruments once every millisecond for up to 100 seconds, being limited only by disk capacity. The laboratories serviced by this facility conduct explosions research and include such facilities as an Experimental Coal Mine Explosion Facility (45 channels), a Constant Volume Combustion Laboratory (4 channels), and a Simulated Coal Mine Laboratory (15 channels). Personnel support includes one systems analyst, two applications analysts, one operator, and a hardware technician. The system has performed adequately for burst-type data acquisition, but due to a lack of long-term reliability (24 hours) of the real-time multiprogramming operating system and unpredictable power failures, slow phenomena signals are generally digitized and stored offline. This latter data is input to the computer through peripherals such as a high-speed paper tape reader, or high-speed asynchronous communications ports. Processing of data is done either in real-time (as soon as data is collected) or in batch mode. Smaller batch jobs are run on this computer, and all others are transmitted by means of the system's high-speed UT 200 terminal simulator to a CDC-6000 series computer.

Jan 1, 1977

By P. Wynblatt, J. E. Dorn

The effect of strain rate, temperature, and interstitial impurity concentration on the flow stress was investigated in a poly crystalline Fe-2 pct Mn alloy. The temperature dependence of the flow stress was found to be independent of the interstitial impurity concentration, removal of interstitials merely decreasing the atherma1 stress level. Below 160%, the large temperature dependence of the flow stress was interpreted in terms of the Dorn-Rajnak theory of the Peierls mechanism of plastic deformation. Above 160"K, some other thermally activated intrinsic meckanisln seems to be operating. The strong temperature dependence of the flow stress of bcc iron at low temperatures has been studied by numerous investigators and interpreted in terms of several different thermally activated dislocation mechanisms. The following mechanisms have been proposed: a) interaction of dislocations with interstitial impurity atoms1 or with solute atoms in general; b) interaction of dislocations with clusters of impurity atoms;3 c) resistance to the motion of dislocations due to jogs on screw dislocations;* d) resistance to the motion of dislocations due to the Snoeck effect;' and e) interaction of dislocations with the intrinsic resistance of the bcc lattice or Peierls "hills". In previous work: it was found that the plastic behavior of polycrystalline iron containing 2 wt pct Mn (and 100 ppm C + N) is in good agreement with predictions based on the Peierls mechanismlo from 77" to 160°K whereas from 160" to about 370°K another as yet unidentified thermally activated mechanism is operative. The purpose of the present investigation was to determine the effect of interstitial impurities on the temperature dependence of the flow stress, by purifying the previously investigated alloy with respect to interstitial impurities. The investigation revealed that removal of the interstitial impurities to a level that eliminated Cottrell locking and the Portevin-LeChatelier effect (i.e., serrations in the stress-strain curve due to dynamic strain aging) affects neither the strong temperature dependence of the flow stress at low temperatures nor the general characteristics of the higher-temperature behavior. Such purification, however, lowered the athermal yield stress. I) EXPERIMENTAL PROCEDURE AND RESULTS The material used in this investigation consisted of an Fe-2 wt pct Mn alloy having the following additional elements present: 0.004 pct C, 0.006 pct N, 0.05 pct 0, 0.004 pct S, 0.003 pct P, and 0.001 pct Si. This was the same material as that studied in the previous investigation and will henceforth be referred to as the "impure material". The as received -jr by 2 in. hot-rolled bars were cold-rolled to 0.08-in. thickness, recrys-tallized under argon for 30 min at 80O0C, and further cold-rolled to 0.053-in. thickness. Flat tensile specimens 3 in. wide having a 1.625-in.-long gage section were machined from the sheet and then purified. The first stage of purification consisted of holding the specimens at 850°C for 24 hr in a stream of hydrogen saturated with water vapor at room temperature. Material prepared in this fashion will subsequently be referred to as "wet hydrogen purified material". It has been estimated that this type of treatment reduces the carbon content of iron to less than 5 ppm.' The second stage of purification consisted of holding the specimens in a closed system through which hydrogen was circulated past the heated specimens as well as a zirconium hydride getter. The specimens were held at 850°C and the getter at 800°C. The process was continued for 212 hr. The starting material for this process was wet hydrogen purified material. Material prepared in this manner will be referred to as "ZrHz purified material". The technique used was substantially the same as that described by Stein et al.' who have shown that the carbon level at the end of the process is reduced to about 5 parts per billion. The mean grain size of the three materials was found to be -60 C( for the impure material and -160p for the wet hydrogen and ZrHz purified materials. All tensile testing was carried out on an Instron Testing Machine either in controlled-temperature baths or at fixed-point baths such as boiling liquid nitrogen, and so forth. When fixed points were used the temperature was kept constant to better than *1°C whereas in all other tests the temperature variation was less than *2°C. Test of Purity. It was not possible to determine the purity achieved at each stage of the purification because the resulting level of interstitial impurities was near or below the limit of sensitivity of standard analytical techniques. It was possible, however, to obtain a qualitative measure of the extent of purification from the appearance of the stress-strain curves for the three materials. Fig. 1 shows the stress-strain curves for the three different materials tested at 300°K. It can be seen that the effect of wet hydrogen

Jan 1, 1967

By Larry Kaufman, Joan B. Berkowitz-Mattuck, Edward V. Claugherty

The oxidation characteristics of hafnium and zirconiunr diboride were measured between 1200 and 2200'K by a thermal- conductivity method which continuously ttzeasures the rate of reaction of oxygen with the diboride and by a metallographic air oridation method zuhich provides a measure of the total arr7ount of bovide conuerted to oxide for a given time interval. The oxidized specimens obtained from the tl~eritaal-coi~ductitrity method were also examined by quantitatire metal-lographic procedares. The significant results obtained in this investigation reveal that metal-rich compositions of lzafi~iutil diboride proride the most oxidation-resistatzt material up to 2000°K; hafnium diboride is tmre oxidation- resistant titan zirconium diboride at all tempevatures examined; the morphology of the oxide formed on H/B2 and Llie temperature coefficient qi. the oxidation rate constants change at the temperature of ttze monoclinic to tetragonal phase transition] in HfO2; the oxidation of neither HfB2 nor ZrB2, results iN catastrophic Jazlure at lorc. oxygen pressures; and pvefevetztial gvaLti boundary oxidation was not obsevued for either HfBi or ZYB, A comprehensive study of the high-temperature characteristics of refractory transition-metal di-borides is currently in progress. This program has included investigation of the physical, thermal, and thermodynamic properties of TiB2, ZrB2, HfB2, NbB2, and TaB2. In addition, aspects of the synthesis and fabrication of such materials have been studied. In view of the diverse nature of this research, a number of other laboratories have actively participated and contributed specific capabilities for analysis and characterization of these materials. As a consequence, an extensive description of the relevant properties of these compounds has emerged which is central in evaluating their high-temperature (1200" to 2500°K) performance. To date, information on thermodynamic stability, specific heat, and vaporization characteristics,1 hot hardness and electrical resistivity,1, 3 therma1 expansion:'4 and thermal conductivity 1, 5 has been presented. This information has been generated on materials of the highest purity (98.5 to 99.9 wt pct Me + B) and density currently available. Samples fabricated by zone melting6 and high-pressure hot pressing"3'7 techniques have been used to generate suitable specimens for all of the aforementioned studies. dation characteristics of the most oxidation-resistant of these materials, hafnium and zirconium diboride, is presented and a description of the synthesis and the experimental procedures used to prepare and characterize specimens is given. The high-temperature range under consideration (1200" to 2200°K) and the known dependence of oxidation characteristics on sample chemistry, density, and oxidation conditions required a close coupling of the synthesis, fabrication, and evaluation procedures.8 This was accomplished by continual surveillance of chemical composition of starting materials before and after specimen fabrication and by evaluation of density, phase constitution, and microstructural features prior to and after oxidation exposure. I) PROCUREMENT AND CHARACTERIZATION OF STARTING MATERIALS In view of the current state of the art in fabricating refractory boride materials, the methods used in preparing samples for the present study are given in detail as follows: starting materials were purchased in high-purity powder form and fabricated by high-pressure hot pressing into 0.40 by 1.00 in. bars from which oxidation specimens were obtained. The hafnium diboride used in this study was purchased from Wah Chang Corp.; the zirconium diboride from U.S. Borax and Chemical Co. These powders were routinely characterized by quantitative chemical analyses for metal, boron, carbon, oxygen, nitrogen, and iron, by qualitative emission-spectrographic analysis for trace impurities, by X-ray procedures for extraneous phase identification, and by powder densitometry for comparison with X-ray (theoretical) density. Hafnium and zirconium metal and elemental boron were also purchased as high-purity powders and characterized for impurities by emission-spectrographic analyses. The hafnium diboride was procured in three shipments which were designated as HfBl.g7(1), HfB1.88(2A), and HfB2.12(2). The indicated stoichiometry is based on the atomic ratio of total boron to total hafnium; the number in parentheses identifies the shipment number. Shipment 1 was 5 1b, shipment 2A, 1 1b, and shipment 2, 8 1b. The zirconium diboride was procured as a 20-1b shipment and designated as ZrB1.89(1). A small quantity of purified zirconium diboride was also supplied and designated ZrB1, 9(P). The averaged results for chemical analyses which were generally performed according to the procedures set forth in the compilation by KrieGe9 are presented in Table I. Qualitative spectrographic analyses indicated that Ca, Cr, Ti, Si, Zr (in H~B~), and A1 were present at levels between 0.01 and 0.10 wt pct. Other metallic elements were found to be less than 0.01 wt pct. Since it is virtually impossible to purchase these materials in the desired quantities (5 to 20 lb) as single-phase compounds it is necessary to obtain

Jan 1, 1968

By Y. A. Rocher, J. E. Dorn, L. A. Shepard

Creep activation energies for single aluminum crystals favorably oriented for shear by (010) [101] glide were detemined over the temperature range from 78" to 900°K. Observations of slip bands on the specimen surface were made in conjunction with the investigation. From 78" to 780°K, the activation energies obtained in this imestigation agreed closely with those previously found for creep by (111) [101] slip. Between 78" and 140°K, the activation energy was identified with the Peierls process, while between 260°and 780°K the activation energy was close to that for cross-slip. The coarse wavy slip bands nominally parallel to the (010) plane observed above 260°K were attributed to fine cross-slip. From 800" to 900°K, unusually high apparent activation energies ranging from 28,000 to 54,000 cal per mole were obtained. These apparent activation energies were attributed to re crystallization. AS illustrated in Fig. 1, a recent investigation1 has shown that creep of aluminum single crystals by the (111) [i01] mechanism is controlled by three unique processes, each of which is characterized by a single activation energy which is independent of the applied stress and the creep strain. A comparison of the observed activation energies with theoretically calculated values permits a fairly clear identification of the three operative creep processes. Below 450°K, where the activation energy for creep is 3,400 cal per mole, the deformation is controlled by the Peierls process, the activation energy for creep agreeing well with that calculated by seeger2 for the energy required to nucleate the motion of a dislocation loop against the atomic forces of the lattice. Between 590° and 750°K, the observed activation energy for creep of about 28,000 cal per mole agrees well with the energy necessary to induce cross-slip. Seeger and schoeck3 estimate that the activation energy is about 24,000 cal per mole whereas Friedel4 recently calculated this activation energy to be 28,000 cal per mole. Above 800°K the activation energy of 35,500 cal per mole that was observed for creep agrees well with that estimated for self-diffusion in aluminum.= In this range the operative rate-controlling slip process has been clearly identified as that arising from the climb of edge dislocations. The objective of this investigation is to ascertain whether a single crystal of aluminum favorably oriented for simple shear in the [loll direction on the (010) plane might exhibit uniquely different activation energies for creep from those obtained previously for (111) [101] slip. Whereas the exis- tence of such unique activation energies would constitute incontrover table evidence for new mechanisms of slip, the absence of any new activation energies might suggest that slip of aluminum is confined to the (111) [loll mechanism. Several factors prompted the selection of the (010) [101] orientation for study. First, there are more reported observations of (010) [loll slip than of any other nonoctahe-dral mechanism.8-10Secondly, Chalmers and Martius1l have concluded from considerations of the energies of dislocations that (010) slip is the second most favored mechanism in face-centered-cubic metals. Finally, favorable orientations for simple shear by the (010) [loll mechanism provide the least favored orientation for slip by the (111) [101] mechanism. EXPE-RIMENTAL PRO-CEDURE The high-purity aluminum stock, specimen preparation, shear fixture, extensometry, and experimental technique used in this investigation were the same as those previously reported.' Single-crystal spheres grown from the melt of 99.995 pct pure Al* were _ *The high-purity aluminum used in this investigation was graciously given by the Aluminum Company of America. oriented, carefully machined into dumbbell-shaped shear specimens, annealed, and chemically polished. The finished specimen had a central reduced section 0.190 in. wide and 0.590 in. in diam and 1/4-in. grip sections at both sides, 0.690 in. in diameter. The specimen was oriented in the stainless steel grips of the shear fixture with the (010) plane perpendicular to the dumbbell axis and the [loll direction parallel to the stress axis within 2 deg. Creep activation energies were calculated in the previously described manner1 from determinations of the instantaneous change in shear strain rate produced by an abrupt 15 to 20 deg increase or decrease in test temperature. If is the instantaneous strain rate at strain y and temperature T1, and ?2 the instantaneous rate at y and T2,

Jan 1, 1960

By H. C. Theuerer

GeC14 may be purified by extraction with HCI and chlorine. The process is as effective for the removal of AsCI:, as the more cumbersome distillation methods usually used for this purpose. GERMANIUM for semiconductor use contains impurities at levels no higher than a few parts in ten million. Material of this quality is obtained from highly purified GeC1, by hydrolysis to the oxide and reduction of the oxide in hydrogen. When purifying GeCl,, AsC1, is the most difficult impurity to remove. This is usually accomplished by multiple distillation procedures.1-3 AsC1, may also be removed from GeC1, by extraction with HC1.1-4 Reducing the arsenic to low concentrations is not practicable, however, because of the large number of extractions needed. This paper discusses a new method for the removal of arsenic from GeC1, by extraction with HC1 and chlorine. The method is rapid, leads to little loss of germanium and is at least as efficient as the distillation procedures currently being used. Theory of Extraction Procedures In the simple extraction of GeC1, with HC1, the following reaction occurs ASCl8G8C1 D AsCl3rc1 at equilibrium CA/Cn= K, where K is the distribution coefficient, and C, and C,, are the molar concentrations of AsC13 in HC1 and GeCl,, respectively. The materials balance equation for this reaction is VACA + vncn = VnC,, where V, and Vn are the volumes of HC1 and GeCl4, respectively, and C, is the initial concentration of AsC13 in GeC1,. From this it can be shown that for multiple extractions where C,, is the concentration of AsC13 in GeC14 after n extractions, and r is the ratio of V, to V,,. It is assumed that r is maintained constant, that equilibrium is established during each extraction, and that K is independent of the AsCl3 concentration. By saturating the system with chlorine, the following reaction occurs in the aqueous phase AsCl3 + 4H2O + Cl2 D H5AsO4 + 5HC1 at equilibrium K' = ------------ ai - a4 h2u - aet2 where a is the activity of the various components. The effect of this reaction is to reduce the concentration of the AsC1, in the aqueous layer and, therefore, to promote further extraction of this component from the GeC1, layer. If the arsenic acid remains entirely in the aqueous phase, the net effect of this reaction is to promote the removal of arsenic from the GeC11. The materials balance equation for extraction with HC1 and chlorine with the foregoing reaction is, then, VaCC + VACA + VACn = VnCo where C,. is the molar concentration of H3AsO, in the HC1. With the added assumptions that the activities of AsC13 and H8ASO4 in the aqueous phase are equal to their molar concentrations, it can be shown that for n extractions Cn/Cu = (1/rkK + rK + 1) n where k - K1 a4h2o - acl2/aoncl. It can be seen by comparing Eqs. 1 and 2 that if k is large, the removal of AsC1, by HC1 extraction will be greatly improved by the addition of chlorine. Dilution of the HCI used in the extraction with chlorine would also favor the separation. This, however, would increase the loss of GeCl,, which is undesirable. Experimental Procedure Germanium prepared from oxide of semiconductor purity is n-type with resistivities greater than one ohm-cm. The resistivity is controlled by the donor concentration, which is —lo-: mol pct. Germanium prepared from material with added arsenic will have lower resistivity commensurate with the arsenic concentration. With such material, at arsenic concentrations above 10-1 mol pct the resistivity is controlled by the added arsenic, and effects due to other impurities initially in the oxide are negligible. In this investigation GeO, of semiconductor purity was converted to GeCl,, and -0.01 mol pct As was added. This material was used for the extraction experiments and the purification attained determined by a comparison of the resistivity data for samples of germanium prepared from the initial and purified GeC1,. A method for calculating the arsenic concentration from the resistivity data is discussed later. The details of the experimental procedures used are as follows: Two hundred and thirty cu cm GeC1, were prepared by the solution of GeO, in HC1, followed by

Jan 1, 1957

By W. G. Pfann

In zone-melting, a small molten zone or zones traverse a long charge of alloy or impure metal. Consequences of this manner of freezing are examined with impurerespect to solute distribution in the ingot, with particular reference to purification and to prevention of segregation. Results are expressed in terms of the number, size, and direction of travel of the zones, the initial intermsofsolute distribution, and the distribution coefficient. IF a charge of binary solid-solution alloy is melted and then frozen slowly from one end, as for example in the Bridgman method of making single crystals,' coring usually occurs, with a resulting end-to-end variation in concentration. Such coring, or normal segregation, is undesirable where uniformity is an object. On the other hand, for certain systems, it can be utilized to refine a material by concentrating impurities at one end of the ingot.'. ' In the present paper a different manner of freezing will be examined with respect to the distribution of solute in the ingot. A number of procedures will be indicated which have in common the traversal of a relatively long charge of solid alloy by a small molten zone. Such methods will be denoted by the general term zone-,melting, while the process described in the preceding paragraph will be called normal freezing. It will be shown that, in contrast to normal freezing, zone-melting affords wide latitude in possible distributions of solute. Segregation can either be almost entirely eliminated or it can be enhanced so as to provide a high degree of sttparation of solute and solvent. A number of simplifying assumptions will be invoked which, while not entirely realizable in practice, nevertheless provide a suitable point of departure for more refined treatments. Moreover, our own experience with zone-melting has shown that, for certain systems at least, the analysis holds quite well. The present paper will be confined to a discussion of principles and a general description of procedures. Comparison with experiment is planned for later publication. Normal Freezing Before considering zone-melting, segregation during normal freezing will be reviewed briefly. If a cylinder of molten binary alloy is made to freeze from one end as in Fig. 1, there usually will be a segregating action which will concentrate the solute in one or the other end of the ingot. If the constitutional diagram for the system is like that of Fig. 2, then the distribution coefficient k, defined as the ratio of the concentration in the solid to that in the liquid at equilibrium, will be less than one and the solute will be concentrated in the last regions to freeze. If the solute raises the freezing point, then k will be greater than one and the solute will be concentrated in the first regions to freeze. The concentration in the solid as a function of g, the fraction which has solidified, can be expressed by the relation: C = kC0 (1-g)k-1 [I] where C, is the initial solute concentration in the melt. Eq 1 is based on the following assumptions: 1—Diffusion in the solid is negligible. 2—Diffusion in the liquid is complete (i.e., concentration in the liquid is uniform). 3—k is constant. Concentration curves representing eq 1 for k's from 0.01 to 5.0 are plotted in Fig. 3. This equation, in one form or another, has been treated by Gulliver,³ Scheuer,4 Hayes and Chipman5 for alloys and by McFee2 for NaCl crystals. It is derived in Appendix I. It should be pointed out that the k which is calculated from the phase diagram will be valid only in the ideal case for which the stated assumptions are correct. In all actual cases, the effective k will be larger than this value for solutes which lower the melting point, smaller for solutes which raise the melting point, and will probably vary during the beginning of the freezing process. For simplification it will be assumed that the ideal k is valid. Zone-Leveling Processes The processes of this part are designed to produce a uniform, or level, distribution of solute in the ingot. Single Pass: Consider a rod or charge of alloy whose cross-section is constant and whose composition, C2, is constant, although permissibly varying on a microscopic scale." Such a charge might be a rapidly frozen casting or a mixture of crushed or powdered constituents. Cause a molten zone of

Jan 1, 1953

COLUMBIA SECTION Holds four sessions during year. Annual meeting in September or October. S. S. FOWLER, Chairman, J. C. HAAS, Vice-Chairman, LYNDON K. ARMSTRONG, Secretary-Treasurer, 720 Peyton Bldg., Spokane, Wash. W. H. LINNEY, J. F. MCCARTHY. A special meeting of the officers of the Columbia Section was held in Spokane, Wash., Jan. 10, 1918, for the purpose of organizing and nominating members to the principal committees of the Section. Present: J. C. Haas, Vice-chairman; W. H. Linney, Past Chairman; and L. K. Armstrong, Secretary. J. F. McCarthy, Wallace, Idaho, was appointed fifth member of the Executive Committee. The following were appointed to the Membership Committee: R. M. Betts; for Oregon; W. J. Hall, for Idaho; J. M. Porter, for Washington. A member for British Columbia will be appointed later. The following were appointed to the Committee on Papers: Prof. F. A. Thomson, Moscow, Idaho; Prof. L. 0. Howard, Pullman, Wash.; H. S. Lee, Rye Valley, Ore. A fourth member, representing British Columbia, is to be appointed later. The following members were appointed representatives on the Executive Committee of the Spokane Engineering and Technical Association: J. C. Haas, W. H. Linney, F. A. Ross, L. K. Armstrong. The Treasurer reported a deficit, resulting from the participation of the Section at the Northwest Mining Convention in 1916. It was recommended that the Institute be petitioned to make good this deficit, in addition to the usual annual allowance. The members of the committee who were present expressed their desire to be of greater service in the present war, and discussed at some length the possible means of carrying out their desires. It was later decided to reopen the subject at a subsequent meeting of the Section, or to present it to the Executive Committee of the Spokane Engineering and Technical Association for discussion and cooperative action. L. K. ARMSTRONG, Secretary.

Jan 3, 1918

By J. M. McCormack, R. K. Saxer, J. R. Myers

ThE Knudsen effusion technique was used to determine the chemical activities of copper and platinum in binary Cu-Pt alloys in the temperature range 1542" to 1673°K. Wiebke and Matthes1 previously obtained chemical activities of copper and platinum in this system at 673° and 923°K by the electromotive-force measurement method. They reported that the copper activities exhibited negative deviation from Raoult's law at all compositions. The chemical activities of platinum were found to change from a positive to a negative deviation at 923°K. Myles2 recently studied this system in the temperature range 1265° to 1356°K by means of the torsional-effusion technique. His results indicated that both copper and platinum exhibited negative deviation from ideality at all compositions. The use of the Knudsen effusion technique to obtain the vapor pressure of metals and alloys is well-known.3 In this work, Knudsen cells were fabricated from seamless tantalum tubing of 1-in. OD and 0.020-in. wall thickness; cell bases and covers were cut from 0.010-in.-thick tantalum sheet and welded to the cells in an argon atmosphere. Orifices were drilled and reamed to approximate a knife-edge of 30-deg included angle. Calculation based on Balson's4 derivation showed the orifice to be nearly ideal. All temperature measurements were made with a Leeds and Northrup disappearing-filament-type optical pyrometer at the orifice of the cell, which closely approximated black-body conditions and eliminated the need for emissivity corrections. Details of the experimental techniques used, and the necessary correction factors required during this investigation are essentially those previously described.5,6 Before investigating the Cu-Pt alloys, vapor-pressure measurements were obtained over specimens of pure (OFHC) copper. The pure-copper data5 served to assure the accuracy of the experimental apparatus and technique.

Jan 1, 1967