By T. Kamata, S. Takemoto, H. Takeuchi, M. Takayanagi, Y. Akahori, I. Jimbo

"A cooperative research work on the silver recycling process is underway between Matsuda Sangyo Co., Ltd. and Tokai University in Japan. Silver wastes treated here are mainly from photograph industries where the concentration of minor element is steadily increasing in the recent years. The waste materials are concentrated and the impurities are removed by evaporation and slagging. In this paper, the industrial practice of wastes treatment is introduced and the result of the laboratory studies on the removal of antimony and tin from the binary and ternary alloys will be discussed. Characteristics in the behavior of antimony and tin during the process are also discussed with the observation of practical operation.1. IntroductionPrecious metals such as gold and silver primarily come from mining practice and the byproduct in copper smelting. However, the recycled amount of these precious metals have been increased 1 along with the environmental restriction and the widely accepted idea of saving resources on the earth in the recent years.· Though the recycle process of precious metals are comparatively simple from other metals refining, the process has been getting more complicated as wastes treatment has to deal with more impurity elements which are intentionally added to the products. Among these additives, antimony is used in the film materials in the photography industries to suppress its inflammability. Tin is another concern ,that is also coming from photography wastes; These minor elements have become problematic during the recycle.The removal of these minor elements has been in operation at Matsuda through a traditional oxidation refinement process using a reverberatory furnace. However, the complexity of the charge makes the recycle process more tedious and troublesome. In order to investigate the minor element behavior in the complicated materials system during the silver recycling processes, a cooperative research work is undertaken between Matsuda Sangyo Co., Ltd. and Takai University in Japan. Silver wastes treated here are mainly discharged from photograph industries where the minor element contents such as antimony, tin and bismuth in those wastes are steadily increasing in the recent years. The liquid wastes containing silver are concentrated and then treated pyrometallurgically with solid wastes from other sources, where the impurities are removed ·by evaporation and slagging. The purpose of this study is to investigate detailed behavior of impurity elements in the silver. containing systems."

Jan 1, 2000

By Anne Kvithyld

Silicon solar cells, that convert the energy of sunlight into electric energy, are attractive sources of energy. In the production line wafers of solar cells are sliced from a multicrystaline ingot solidified unidirectionally. Recycling scrap from top and sides of such ingots is addressed. SiC and Si3N4 inclusions are a major problem. Scrap from Scan Wafer ASA is melted in a high vacuum furnace at around 1500ºC. The filters, from commercial producers, are C and SiC with 10, 20 and 30 ppi. Characterisation of inclusions before and after filtration, and in the filter itself, is performed by microscopy. Dissolution of silicon in acid and counting of the un-dissolved inclusions is also carried out. In the filter Si3N4 needles and SiC inclusions were identified. The amount of these inclusions in the filtered silicon is much less than in the input. In conclusion, filtration using SiC and C filters in vacuum system in argon atmosphere removes SiC and Si3N4 inclusions from solar cell scrap. Flow of metal through the filters is not a problem. These results are promising with scale-up to industrial application in mind.

Jan 1, 2006

By Mark Tsirlin

Kinetics of the initial oxidation stages of diffusive silicide coatings on 8 molybdenum and niobium at 1100 - 1700 and under the pressure of 400 and 1330 Pa has been studied using methods of gravimetry and gas phase analysis of oxygen, as well as by SEK, XRD and EDMA methods. The first oxidation stage described by asymptotic equation in case of NbSi coating changed over to the stage described by parabolic equation. The asymptotic law was shown to depend on non - stationary conditions on the oxide layer boundaries. Interconnection between silicides and quartz structures, on the one hand, and peculiarities of oxidation kinetics, on the other, is [discussed. The possibility of estimation oxygen atom jump frequency in quartz and fractions of oxygen reacting with metal and with silicon proceeding from the analysis of the kinetic data was ascertained. Conditions of oxidation kine- tics transfer from asymptotic (or parabolic) stage to a non - protective "linear" stage, associated with volatile ~roduct formation, are also discussed.

Jan 1, 1995

By Sven Reutzel

Investigations show that Co-based melts embedded by glass flux in a crucible can be under- cooled nearly as strong as samples processed containerlessly by electromagnetic levitation. This allows to measure magnetic susceptibility on undercooled melts while combining the use of a Faraday-balance and undercooling technique. The magnetic susceptibility of Co and Co-based alloys (such as Co-Pd and Co-Cu) is investigated as a function of temperature from superheated to undercooled state. This is done by measuring the change of magnetic force F, on a sample in a constant magnetic field Bo and an additional gradient field by means of a Faraday-balance. When liquid Co-based alloys are undercooled the magnetisation steeply rises if temperature approaches the Curie temperature. The magnetisation is measured for some Co-based alloys in liquid state as a function of alloy system and its concentration. The results show that the magnetic susceptibility of the liquid undercooled samples follows a Curie-Weiss behaviour, from which Curie temperature and magnetic moments for the liquid state are inferred.

Jan 1, 2002

By J. B. Wiskel, H. Henein

"A study was conducted to establish the effective heat transfer coefficient for a single molten droplet moving in a gaseous medium. Towards this objective, a series of quench experiments were performed on molten droplets of AA6061 aluminum generated with the Impulse Atomization technique (IAP). IAP is a single fluid atomization process capable of producing powders with a predictable mean particle size and a relatively tight standard deviation under controlled atmospheric conditions. Microstructure analysis of the atomized powder was used to establish the extent of pre-quench solidification. A mathematical model was then employed to correlate the Ranz-Marshall and Whitaker equations with the observed particle cooling behaviour. These equations were found to provide a reasonable estimation of the heat transfer conditions only when the variation in gas thermophysical properties across the boundary layer was accounted for in the model. This model formulation of droplet heat transfer has important implications with regards to active sprays and atomization processing operations IntroductionAn understanding of droplet cooling is important in atomization powder production. It is well understood that dendrite arm spacing is inversely proportional to cooling rate during solidificationl1l. Through modification of the heat transfer conditions during metal atomization, the microstructure of a powder maybe tailored to the end user. However, owing to the complexity of gas flow it is difficult to determine a heat transfer coefficient for a moving droplet. This difficulty is further compounded when complex jets and/or streams and their interactions are considered. To provide a base for these more complicated types of analyzes, two approaches have been employed to calculate the effective heat transfer conditions for a single droplet. In one approach, Megardis [ZJ developed a numerical model to investigate the heat transfer process of a free falling droplet undergoing laminar convective cooling. The effective heat transfer coefficient as a function of angular position was determined by numerically solving the fluid and energy equations for the system."

Jan 1, 1999

By J. P. Downey, T. Salisbury, M. Berlin, E. Rosenberg, G. Pinson, R. Christianson, K. Gleason, W. Gleason, S. Davis

"Direct digital manufacturing offers promise as a technique for fabricating complex hydrogen purification membrane support structures. Free form fabrication methods can produce parts with complex structures, and sintering parameters can be controlled to adjust the density, pore structure, pore pathways and strength in catalytic substrate constructs. Efforts are underway to define the influence of selected process variables on the chemical and mechanical properties.IntroductionThe Center for Advanced Mineral and Metallurgical Processes (CAMP), in collaboration with the Metallurgical and Materials Engineering Department at Montana Tech and the Chemistry Department at the University of Montana, is engaged in the development of new methods and materials for hydrogen purification membrane production. Because hydrogen readily passes through palladium, a structurally sound palladium-based membrane is capable of separating relatively pure hydrogen from other gases. In order for this technology to succeed, a suitable substrate material must be identified.High purity hydrogen is produced by various means. A common method involves a two-stage process for separating hydrogen from a hydrocarbon gas stream: 1) hydrogen-rich syngas is produced by the catalytic reaction of natural gas or another light hydrocarbon gas with steam, and 2) hydrogen is separated from the other syngas components by pressure swing adsorption (PSA) (US. Energy Information Agency, 2011). In PSA, gases enter a column that is packed with a material that absorbs gases as the chamber is filled and pressurized. As the pressure is slowly relieved, the absorbent material releases hydrogen at a higher pressure than the impurity gases. PSA processes produce 99.99% pure hydrogen at a high recovery rate. These systems typically demand a high capital investment due to the high pressure and multiple stages (columns) needed to attain high hydrogen production rates.Research geared toward reducing hydrogen production cost is focused on the development of improved catalysts and adsorbent materials as well as more effective single-stage separation processes. An interesting method combines hydrogen reduction catalysis and filtration. Nascent hydrogen is separated from other gases as it selectively permeates the filter. Catalyst filters may be made of gold, silver, platinum, palladium or precious metal alloys (Davis, 2009)."

Jan 1, 2012

By Sang Han Son

The vapor pressures of FeCL2 and ZnCL2 in the FeCL2?ZnCL2 system were measured by the transpiration method at 873K and 9I7K, The vapor pressure data were interpreted to indicate the formation of complex ions in the FeCL2?ZnCL2 melts, It is presumed that the complex molecule FeZnCl4 as well as FeCL2 and ZnCL2 exists in the vapors in equilibrium with molten FeCL2-ZnCL2 mixtures, The activities in the FeCL2-ZnCL2 system are shown a negative deviation from Raoult's law. These results suggest the formation of complex ions such as ZnCL14 in molten FeCI2?ZnCL2 mixtures.

Jan 1, 2003

By Z. Sun, H. A. Davies

"Current understanding of the mechanisms by which glassy and crystalline thin ribbons are formed in high speed continuous casting processes is considered. A computer model of the combined heat and momentum transfer during melt spinning has been developed. The influence of roll velocity and of heat transfer coefficient (between the melt and the roll) on the temperature and velocity distributions within the melt puddle is analysed and the thickness of the extracted ribbon computed. The relative importance of heat and momentum transfer under different conditions is assessed and differences between the casting of crystalline and amorphous strip highlighted.IntroductionHigh speed continuous casting of thin metallic ribbon and strip is currently of considerable interest both to metal processers and to those studying process mechanisms. The practical interest arises both from the potential economic benefits to be gained from a shorter and more energy-efficient production route and from the ability to obtain extended and uniform thin strip having a metastable microcrystalline or amorphous structure with enhanced or unique properties. The latter arise from the rapid solidification associated with the cooling of very thin sections of melt brought into intimate thermal contact with one or two rapidly moving heat sinks.The principal processes for casting thin strip include free jet, chill-block melt-spinning (GBMS) (1), melt drag (MD) (2), planar flow casting (PFG) (3) and twin-roll casting (TRG) (4). For the first three of these, all essentially variants of melt-spinning, melt flows through a nozzle onto the circumferential surface of a rapidly rotating roll, whereas for TRG the melt passes into the nip between two contra-rotating rolls. We shall be concerned in this paper with the single-roll melt spinning processes only. For these, a puddle is established where the melt contacts the roll surface and the length of this puddle l is a function of the process conditions, notably the circumferential velocity of the roll Us and the volumetric flow rate of the melt Q. The contact time between any point on the roll surface and this puddle, or residence time eR(= l /Us) determines the thickness of ribbon t extracted from the puddle. This thickness, in turn, partly governs the cooling rate T and the amount of undercooling in the melt and thus the microstructure of the solidified ribbon."

Jan 1, 1986

By Wenming Wang

Recycling of retired cadmium telluride (CdTe) photovoltaic (PV) modules has attracted attention due to new European environmental regulations. Recycling tellurium from CdTe PV modules is becoming more important because of the low availability of this metal. We investigated several treatment paths for reclaiming tellurium from solutions obtained from leaching fragments of CdTe PV modules. Our experiments showed that conventional soda ash neutralization/hydrolysis methods recovered only 50~60% of tellurium. However, by appropriately combining neutralization and sulfide precipitation, almost all the tellurium present in the leaching solution was precipitated and recovered; the concentration of tellurium in the processed solution was reduced from 900-1000 mg/L to less than 1 mg/L, yielding a tellurium recovery greater than 99%. This method can be incorporated in the scheme of recycling spent CdTe PV modules and manufacturing wastes. It may be also an alternative to the current operations for removing tellurium from copper anode slime leaching solutions.

Jan 1, 2006

By Hiromichi Ohla

Precise thermal properties of molten materials are essentially required for analyzing the metal production process. These properties are also important as a clue to consider the dynamic structure of liquid materials. However, it is difficult to obtain the precise thermal diffusivity values of molten oxides at high temperature because of the experimental uncertainties arising from the bubble formation or the severe separation of radiative and conductive heat components. Recently a novel laser flash method has also developed for measuring thernnal diffusivity of molten oxides at high temperature. In this new technique, the sample is melted in a metal crucible and heated to the desired temperature. A single laser pulse is flashed on the bottom of the metal crucible and the infrared ray irradiated from the same bottom surface is measured for obtaining the temperature decay, from which the thennal diffusivity of the liquid sample can be estimated. The usefulness and validity of this new laser flash technique have been confirmed by obtaining the thermal diffusivity values of silicate melts in the wide temperature range between 773 and 1673 K.

Jan 1, 2003

By Gaifeng Xue, Lijun Lu, Honghui Fang, Jiannyang Hwang

"Steel slag has been stockpiled in many steel mills due to its poor performance in various construction related applications. Free lime in steel slag has been considered as a major barrier for its utilizations. Composite of steel slag and powders of granulated blast furnace slag have been found an excellent cementitious material for concrete. Portland cement is not required in this kind of concrete. Concretes with various amounts of steel slag and powders of granulated blast furnace slag additions have been investigated. Physical and chemical properties of the products were examined. High performance concrete can be obtained. Field testing of the concrete products was conducted for various applications, including buildings and pavements, and the results demonstrated the soundness of the concrete. Drill cores of field tested concrete, with ages up to 26 years, were examined for the microstructures under SEM.IntroductionIn the steel industry, a major source of the solid waste is steel slag. Steel slag has poor stability in construction applications. This is a major reason that only a small amount of steel slag has been utilized. Some of the reported applications include the land filling/creation in the sea, road base materials, soil treatment for acid neutralization and micronutrients supply, and sintering aid in the sintering plant of the steel industry [1].To solve the stability problem for using steel slag as construction materials, the common approach is to find a method capable of depressing or eliminating the expansion of steel slag. Free lime in steel slag is the major component that causes the expansion. Aging and hydration pretreatment of free lime in steel slag are the well known methods for increasing the steel slag stability. However, there has been limited success on these approaches due to that a large portion of free lime is locked in the grains during the pretreatment process."

Jan 1, 2012

By Ernie M. Crist, Laurentiu Nastac, Frank Spadafora

"This paper describes the modeling techniques and the experimental and computer results for two casting processes that are under development and optimization. These processes are described as follows:1) Electromagnetic stirring (EMS) during casting of Ti-6Al-4V round ingots using the plasma arc cold hearth melting (PAM) process: The purpose of EMS is to establish a singlemelt PAM process capable of consistently producing as-cast ingots without helium porosity and also having no need for surface conditioning prior to secondary processing.. The modeling approach is based on the numerical solution of Maxwell's equations, fluid flow, and heat transfer equations, and mesoscopic modeling of the grain structure.2) Casting of Ti-6Al-4V slabs using the single-melt PAM process: The purpose of slab casting is to improve yield by eliminating an intermediate blooming step for converting round ingots to slabs. The modeling approach is based on the numerical solution of fluid flow and heat transfer equations. The effects of pouring and mold temperatures on the pool and temperature profiles were studied. Also, the torch effects (such as the torch standoff and its traversing path) on the pool and temperature profiles were investigated and the best-case scenario was used in the experiments. Evaluation results at RMI Titanium Company showed that the plates made from the slabs met the mechanical properties and microstructure requirements.Acknowledgment. This work was conducted by the National Center for Excellence in Metalworking Technology (NCEMT) operated by Concurrent Technologies Corporation (CTC) under contract No. N00014-00-C-0544 to the US. Navy as part of the US. Navy Manufacturing Technology Program. Dr. K. b. Yu from RMI and my colleagues from CTC are acknowledged for their comments on this work."

Jan 1, 2004

By M. Tomita

One of the most essential factors for a custom smelter to strengthen its competitive power is to Improve its comparative standing in purchase of concentrates from the world market. It is especially critical for Japanese smelters who depend almost 90% of their raw materials on import. In order to accomplish this breakthrough, the development of the new technology which enables us to treat concentrates containing higher Impurities is inevitable. Nippon Mining Company Ltd. made an intensive research on processing complex ore for three years from 1979, and successfully developed an original hydrometallurgical process to treat converter dust for eliminating impurities from the copper smelting circuit. The commercial plant was constructed at the Saganoseki Smelter & Refinery in 1982, and its nine years operation has been satisfactorily proven the advantages of the technology. The concept of this process and its operational performance are discussed.

Jan 1, 1992

By Mikiya Tanaka, Mikio Kobayashi, Kazuya Koyama, Yoshihiro Nishisu

Preparation of multicomponent powders are very useful and important for producing the materials with complicated and homogeneous structure. Therefore multicomponent powders have a lot of attention in the field of advanced value-added materials. The aqueous processing in hydrometallurgy has a broad potential for producing multicomponent homogeneous precipitates. Furthermore the aqueous processing has a future potential for integrating the separation, precipitation and synthesis processes. In this presentation the precipitation from homogeneous solution including rare-earths and/or common metals is presented. These precipitates probably consist of almost monodispersed, multicomponent and spherical particles by precisely controlling several reaction factors, reaction temperature, concentrations of starting materials, pH and so on. The separation of the nucleation stage and the growth stage of the particles is very important and how to control the reaction factors to realize enough separation is discussed. In this presentation the systems of Y-Eu-0, Y-Fe-0 and Y-Al-0 are mainly presented. In addition the precipitation-stripping method from organic phase is presented focusing the synthesis of multicomponent powders of Ni-La-0 system. These precipitates have multicomponents homogeneously and so they are converted to multicomponent ceramic powders by calcination. They are important compounds as phosphor, opto-magnetic materials, optical materials, hydrogen storage alloy or as the related precursors. In this presentation some characterization of these particulate materials is included.

Jan 1, 1998

By T. Iriyama, Y. Fujita, R. Omatsuzawa, T. Nishio, N. Okochi

Sm-Fe-N hard magnetic materials are good candidates for high performance bonded magnets. Rapid-quenching method should be highly favorable for the fabrication of isotropic magnet powder with high coercivity. We report here the magnetic properties of Sm-Fe-N powders produced by a few kinds of rapid-quenching processes. Sm2Fe17 powders were prepared by gas-atomization (GA), rotating-disk atomization (RDA), or melt-spinning (MS) method. The Sm2Fe17 GA powder had dendritic solidification structure, while the RDA powder had micro crystalline structure with size of 3-5 µm. Coercivities (HcI) of their nitrides were 56 (for GA) and 217 ka/m (for RDA). The H cI of nitrided Sm2Fe17 MS powder with wheel velocity (V5) of 5-20 m/s, which had also microcrystalline structure, was 53 to 509 Wm. These coercivity values are not sufficient for bonded magnet applications. From the study of additive effects, it was found that C, C-Si, C-Ga, or C-Al addition decreased the crystal size of quenched Sm2Fe17 powder. Consequently, high coercivity was obtained; the HcI of nitrided Sm2Fe1C1Si1 MS powder with V5 of 10 m/s was 898 kA/m, and 708 kA/m for the nitrided Sm2Fe15C1Si1 RDA powder. The compression-molded bonded magnet made from Sm2Fe18Si0.1Nx MS powder showed a high (BH)max of 82.7 kJ/m3.

Jan 1, 2000

By Lauri Pajunen

DSA-anodes are widely used in metal electrowinning. In zinc electrowinning the electrolyte solution contains manganese ions, and the deposition of manganese dioxide happens on the anode. This manganese dioxide layer cannot be removed without losing the active coating of the DSA-anode. The same problem can be found with hybrid anodes. In hybrid anodes mixed metal oxide coated titanium mesh is attached to a lead base material. In this study, the effect of dissolved manganese on anode behaviour is studied with three different anodes. These anodes are lead anode with 0.6% silver, hybrid anode and DSA-mesh. Methods of study include polarization, galvanostatic and potential mapping experiments.

Jan 1, 2003

By Andrew L. Puwis

Methodologies were presented for computing the thermal gradient associated with single crystal solidification in macroscopic computer modeling. The. heat transfer, and solidification of a shaped investment casting model were simulated using properties from three different alloys. Following the simulation of solidification, the resultant thermal gradients (G) and rates of solidification (R) from representative points were extracted in various ways and compared: It was discovered that alloy properties have a strong influence on the computed thermal gradient and rate of solidification for the three methods investigated. Data also showed that the computed gradient for each model was very different depending on the temperature range used to compute these values.

Jan 1, 1994

By Alexander V. Derevyanko, Victor P. Popov, Alexander I. Raitchenko

"If an electric current flows along some electroconductive suspension in columnar form the solid particles are 'experienced thermal, mechanical, and electromagnetic influences.The objects were suspension Sn (liquid) - Ni-Cr-Mo-W alloy (solid particles). This is refractory alloy on the Ni base. The direct constant current (with density -106 A/m2 ) flowed through the named suspension during 180+300 sec. At the beginning of experiments samples were ones containing particles suspended uniformly in volume. Although density of solid particles was ~9x103 kg/m3 , i. e. higher than density of liquid Sn (-6.8x103 kg/m3 ), after end of this processing, the non-uniform distribution of particles in volume of samples was observed: concentration of Ni-alloy particles in lower part was smaller than their concentration in upper part of samples, and simultaneously their concentration is increased near outer surface. There was probably the natural convection of Benard-Rayleigh type which had carried, so lid particles upwards, and, in same time, there was the action of spatial Lorentz-forces directed to center forcing the radial movement.The knowledge of named phenomena can be useful for elaboration of technology of gradient dispersed materials and development of some materials science fields.IntroductionThe liquid metal with the electric current or under the alternating magnetic field is experienced compression. This action causes the pressure within metal and the change of the surface of the metal column (see, for example, [1-4]). One of results of such an electromagnetic compression is extraction of the foreign solid particles from a cylindrical liquid sample to surface in the radial directions. However, more complicated paths of the inclusions are observed under some conditions of electric treatment."

Jan 1, 1999

By Chris T. Vild

"ABSTRACT NOT AVAILABLEPRESENTATION SUMMARYIntroductionToday, light gauge aluminum scrap is melted in sidewell furnaces using natural gas reverberatory burners. The scrap is introduced into the sidewell adjacent to the combustion chamber through a submerged archway. Super-heated metal is then pumped into the sidewell where it aids in melting the scrap. From the sidewell, the flow is returned to the combustion chamber through a second submerged archway at some lower temperature. Normally, the burners are set at a designed high fire level and the scrap is introduced at a rate to attempt to mat.ch the burner input. A thermocouple in the bath is programmed to throttle back the burners to low fire if a high temperature limit is exceeded.Jn many cases the thermal efficiencies of these furnaces can be very low. With inadequate circulation, air and natural gas furnaces run at a dismal 18% thermal efficiency. If a circulation system· is added, the efficiency can jump to 28%. For a $100 million lb/yr recycling facility, and natural gas prices reaching $4.50 per million Btu, fuel cost at 18% efficiency can reach $1 million per year. A 10% increase in thermal efficiency saves $350,000 a year in fuel costs.With an increase in thermal efficiency, furnace utilization also increases. A 10% increase in thermal efficiency would result in a 20 million Btu furnace producing 12,000 lb/hr up from 8,000 lb/hr or 35 million lb more produced per year. This is a 33% increase in output.Most current furnace development has focused on burner technology using oxy-fuel, regenerative burners, etc. However, thermal efficiency is also largely effected by the molten metal circulation rate and how well the scrap is mixed into the superheated metal. Therefore, the flow dynamics should be optimized first, before installing of more thermal power.Jn an effort to understand the effect of these variables, a series of computer models were made and the critical factors studied with the goal of demonstrating an increase in thermal efficiency and production. Large-scale graphical representations of these models will be presented."

Jan 1, 2000

By R. A. Spitz, R. Leiby, M. Bricker

Electrochemistry plays a significant role in minimizing wastes at East Penn's secondary lead smelter. East Penn has been recovering spent battery acid for reuse in new batteries since 1992. East Penn also produces a fertilizer feedstock from sulfur dioxide in the smelter stack gases. The success of these processes is, in large part, due to the installation of electrochemical cells. The cells in the acid recovery plant allow the waste from this process to be concentrated into less that 10% of the original spent acid. The cells in the fertilizer plant treat the solution to remove dissolved metals prior to sale to fertilizer manufacturers.

Jan 1, 2000