By Jean Igor Margem, Lucas Barbosa de Souza Martins, Frederico Muylaert Margem, Noan Tonini SImonassi, Sérgio Neves Monteiro, Rômulo Leite Loiola

"Fibers of giant bamboo (Dendrocalmus Giganteus) are amongst the strongest lignocellulosic fibers. Although studies have been already performed, limited information exists on the mechanical properties of polymeric composites reinforced with continuous and aligned giant bamboo fibers. This work evaluates the tensile strength of this type of composite. Standard tensile specimens were fabricated with up to 30% of fibers aligned along the specimen's length. The fibers were press molded with a commercial epoxy resin mixed with a hardener and cured for 24 hours at room temperature. The specimens were tested in an Instron machine and the fracture surface analyzed by scanning electron microscopy. The tensile strength increased significantly with the amount of giant bamboo fiber reinforcing the composite. This performance can be associated with the difficult of rupture imposed by the fibers as well as with the type of cracks resulting from the bamboo fiber/epoxy matrix interaction, which prevents rupture to occur.IntroductionDue to growing concern about the ambient impacts from industrial activities, our society is ever more using environmentally friendly materials. In this regard, cellulose-based natural fibers, known as lignocellulosic fibers, become a promising solution. Nowadays, they are being considered as a substitute for synthetic fibers, such as glass fiber, used by the industry on a large scale [1-5]. The application of these natural fibers is also motivated by many advantages like good toughness and less wear of equipment used in the processing of composites. In addition, such composites are environmentally friendly because they are renewable, biodegradable and neutral with respect to C02 emissions, the main responsible for global warming and climate changes. [3,5,6].Lignocellulosic fibers also have some disadvantages in relation to synthetic fibers such as the difficulty of coupling with polymer matrices, due to the hydrophilic character of fiber and the hydrophobic nature of the matrix, as well as dimensional heterogeneity [ 4,5]. This last one is characteristic of the nature of this material and constitutes an obstacle to the use of these fibers in certain projects, especially those that aim high performance. The above mentioned disadvantages are worrisome reasons for the occurrence of reduction in the strengthening capacity, as indicated by the rule of mixtures for composites [7]."

Jan 1, 2013

By Miaoyong Zhu, Sen Luo

"A two-dimensional CAFD model was developed for simulating the solute diffusion-controlled dentritic growth in the low Peclet number regime. Mass conservation and local equilibrium at the solid/liquid interface were solved to determine the growth velocity of interface with consideration of constitutional and curvature undercooling. The modified decentered square growth proposed by Wang et al was adopted to capture the first eight neighboring cells. The comparison between the classic Lipton-Glicksman-Kurz (LGK) analytical model for steady state tip variables and the simulated values showed that the present model was capable of quantitatively determining the dendritic growth, and the simulation tests demonstrated that the effects of the mesh anisotropy in growth kinetics and crystallographic orientation were eliminated. The numerical simulations were performed to the dendritic growth ofFe-0.6%C binary alloy in undercooled melt, and the results showed that the present model could predict the dendrite morphology with artificial growth orientation in acceptable level.IntroductionDuring the solidification of metals and alloys, the dendrite grows from the substance or the undercooling melt and solute redistributes between the dendrite and the interdendritic liquid. The solidification microstructure is close related to the phase and solute evenness and has a close linkage with the properties of final production.In the past few decades, various kinds of deterministic and stochastic models have been developed to predict the evolution of microstructures in solidification, with the fast development of computer power. Among these methods, Phase Field (PF) model [1, 2] has been known as one of the most adequate deterministic models for directly simulating the dendritic growth. However, there is a vital drawback that the PF method requires considerable computation time and is limited to simulate very small domains with a few dendrites [3]. On the other hand, stochastic models, such as Monte Carlo (MC) method [4, 5] and Cellular Automaton (CA) method [6-8], have been usually applied to predict the solidification microstructure evolution. Comparing with the MC method, the dendritic growth kinetics is explicitly integrated in the CA model, while the MC model doesn't. Therefore, the CA method is more reasonable to predict the dendritic growth during the solidification of melt."

Jan 1, 2013

By Qing-Yun Huang, Xiao-Yi Zeng, Bing Xie, Hong-Yi Li, Jia-Rong Yan

"In order to utilize vanadium resource in vanadium-titanium magnetite ore efficiently, vanadium distribution ratio between hot metal and slag should be improved during BF process, meanwhile the precipitating of Ti(C,N) in slag must be minimized. Effects of temperature, Ti02 content in the slag and basicity on vanadium distribution between slag and hot metal were investigated by experiment and thermodynamic calculation. The results indicated that high temperature, low Ti02 content and high binary basicity of slag were beneficial to increase the vanadium distribution ratio. The effects of temperature and Ti02 content in slag on vanadium distribution were stronger than that of slag basicity.IntroductionVanadium is an important element that is widely used in industrial fields. Most of vanadium resource is hosted in vanadium bearing titanomagnetite [l]. Vanadium bearing titanomagnetite is thus one of the domainate raw materials to produce the vanadium products. In other words, the comprehensive utilization of vanadium bearing titanomagnetite is beneficial for vanadium resource utilization. Vanadium bearing titanomagnetite sources are abundant in Pan Xi of China [4]."

Jan 1, 2013

By Guo-hua Bai, Hong-jing Yuan, Qian Li, Yong-bin Yang, Tao Jiang, Yan Zhang

"The effect of different additives on the bio-oxidation of arsenic-bearing gold ores has been carried out to solve the problems such as long period of leaching, low oxidation rate. The oxidants strengthen the cathodic reaction and thus improve the leaching rate by the increase of electron transfer. Meanwhile, silver catalysis is also effective for the decomposition of arsenicbearing gold ores due to the strengthening of anode reaction. Co-intensification by oxidants and Ag (I) is more efficient to the bio-leaching and the conversion of As (III) because the anode and cathodic reaction of biological oxidation of sulphide ores were both strengthened. The leaching rate reached to 63.94% after bio-leaching 13days by co-intensification of Ag (I) and Fe(III).IntroductionWith the worsening global ecological problems and the gradual exhaustion of available gold resources, metallurgical technology of refractory gold ore has received more and more attention and become possible due to its good advantage of the economic effects and negative effects to the environment. Refractory gold ore, the direct cyanide leaching rate of that is defined as less than 70%, has become an important raw material in gold extraction industry, in which sulfide bearing gold ore represents a large proportion, pyrite and arsenopyrite (FeAsS) is a common gold-bearing mineral. Since the gold is often encapsulated in the crystal lattice of these minerals, destruction or alteration of the ore to liberate the submicron and/or structurally bond gold is necessary[l]. Even if the ultrafine grinding approach also is generally not sufficient for these refractory ores and additional techniques like roasting, pressure oxidation and bacterial oxidation are used to liberate the gold [2]. In the three pretreatment processes, bacterial oxidation is characterized by its new ideas, low cost, no pollution, simple equipment and operation, high leaching index and become the most promising process which has received much attention over time [3-5]. But its further application is limited by some of its own shortcomings, such as long pretreatment time and the toxic effects of arsenic to bacteria on bio-leaching limit."

Jan 1, 2013

By Jie Li, Liangxing Jiang, Yexiang Liu, Junfeng Gui, Bo Hong, Xiaocong Zhong, Yanqing Lai, Xiaoying Yu

"Pb-based alloys with Pr and Ag were prepared in vacuum electromagnetic induction furnace. The tensile strength, corrosion rate and anodic potential in sulfate solution were measured, and the experimental data were analyzed according to the metallographic phases of alloys, the micromorphology and composition of their oxide films. The results show that, with the addition of Pr, the ultimate tensile strength and corrosion rate of pure lead were increased, and the anodic potential decreased. The extra addition of Ag can improve the properties of alloy further. Comparing with Pb-Ag0.8 alloy which is widely used in zinc electrowinning industry, the ultimate tensile strength of Pb-Ag0.6-Pr2.0 alloy was increased by 31.75%, the anodic potential under 50mA/cm2 was decreased by 30m V.IntroductionIn zinc electrowinning industry, the Pb-Ag (0.5-1.0 wt.%, 0.8wt.% normally) anode is widely used as an insoluble anode['l. It can meet the basic requirements, but still has several problems such as high oxygen evolution over-potential (about 860mV), unsatisfactory corrosion resistance, lead contamination of the cathode product and high consumption of Ag etc.In order to reduce the energy consumption, enhance the corrosion resistance, improve the product quality and reduce the consumption of Ag (or even dispense with it), much research has been done, mainly focusing on Pb-based alloy anodes and Ti-based coated anodes. Detailed investigations have already been carried out on binary alloys (Pb-Ca and Pb-Co), ternary alloys (Pb-Ag-Ca, Pb-Ag-Ti, Pb-Ag-Sn, Pb-Sr-Sn, and Pb-Ca-Sn) and quaternary alloys (Pb-Ca-Sr-Ag, Pb-Ca-Ce-Ag, and Pb-Ag-Sn-Co)[Z-4l, Although these anodes can effectively reduce the consumption of Ag, only the Pb-Co and Pb-Ag-Sn-Co anodes perform well with regard to reducing the anodic potential. However, their complicated manufacturing conditions restrict further commercial use.Besides its application in nonferrous metal electro-winning industry, Pb-based alloy is also used as grid alloy for lead-acid battery, serving as active materials supporter and current collector. In order to enhance the corrosion resistance and deep-cycling performance, reduce the impedance of the corrosion film, the addition of appropriate rare earth elements into anodic grid alloys has become a research focus. Studies proved that RE can enhance the mechanical strength of grids, inhibit the formation of anodic Pb(II) film on the surface of grids and then reduce the impedance of the film[ 10-12l."

Jan 1, 2013

By Minjun Tang, Jianfeng Zhou, Feng Chen, Linjiang Qing, Xiaolei Song, Yufeng Guo, Tao Jiang

"Reduction swellability index (Rsn and low temperature reduction disintegration index (RDI) of vanadium-titanium magnetite oxidized pellets are harmful to the processing of ironmaking, for example, causing serious gas permeability, decreased yield, higher coke ratio and more furnace dust. Thus, the improvements of RSI and RDI of vanadium-titanium magnetite oxidized pellets were investigated in this paper, including the pretreatment of raw material, additives of dolomite or boric acid, pellets treated in chloride solution and so on. The results showed that damp milling as pretreatment and boric acid added in pelletizing were conducive to the RSI which decreased 5% and 7% respectively, while they were not efficient enough in improving RDI. Dolomite was efficient in improving RSI, but had negative effect on RDI. There was no evidence to show that RSI and RDI would be improved when pellets were treated in chloride solution. Pursuing this further, the mechanism of those improvements were investigated.IntroductionIn the world, vanadium-titanium magnetite utilization is investigated around how to recover iron, titanium, vanadium, and divided into blast-furnace method and non-blast-furnace method according to respective characteristics. Blast furnace method [1, 2] can recover iron and vanadium effectively, but Ti02 cannot be recycled. Non-blast-furnace methods include rotary kiln-electric furnace method, pre-reduction electric furnace method, reduction- grinding method and sodium vanadium-rotary kiln-electric furnace method and so on. [3-7]Comparing to the Non-blast-furnace method, the method of blast furnace smelting has been put into industrial applications. And it has the following advantages: First of all, effective recycling iron and vanadium; Second, technical problems of high titanium slag in blast furnace smelting; Third, it has mature technology in blast furnace smelting."

Jan 1, 2013

By Robert Fritzsch, Ragnhild E. Aune, Mark William Kennedy, Behzad Mirzaei

"The quantitative particle concentration can give important information about the cleanliness of melts for quality control in primary and secondary production of aluminum. Manual quantification of the particle concentration is normally a time consuming process and human control can bias the acquired images and particle count.The present paper explains the automated image-processing steps for the quantification of SiC-particles, with equivalent diameters from 2 to 25 µm, in solidified A356. A total of 700 micrographs, acquired with a standard white light microscope with 10 x magnification, were analyzed. The applied software (Image Pro-Plus 7.0 from MediaCybemetics®) allows for programming of macros which in tum provides the user with a higher degree of control. The automated results are compared with the results obtained by manually counting the particles in the same micrographs. The impact of the automated results on the estimated filtration efficiency was established to be only -3%.IntroductionInclusions are both indigenous and exogenous particulates that are present in commercial metals such as aluminum. If large individual or large numbers of inclusions are present, they can have a significant negative impact on the appearance, mechanical and chemical behavior of products produced from the metal. Aluminum is known to contain large numbers of inclusions: =50 µm in size, e.g. typically <l ppm by volume or <100,000 inclusions of>20 µm per kg of metal as detectable using a Liquid Metal Cleanliness Analyzer, LiMCA [1]. Depending on the final application of the aluminum, inclusions can render the metal 'not fit for purpose', and result in serious economic consequences to metal producers.It is not surprising that the aluminum industry has developed a number of treatment processes to improve metal cleanliness, given the large number of high value products whose quality can be adversely affected by inclusions. CFFs are the most commonly applied filtration process and have been used to filter >50% of the world production of aluminum since the 1990's [2].Inclusions in aluminum may be particles, bifilms [3] or clusters of: oxides (Al2O3 , SiO2), spinels (MgO· Al2O3), carbides (SiC, Al4C3), nitrides (AlN), borides (TiB2), sulfides, phosphides and intermetallics [ 4]."

Jan 1, 2013

By Xinhua Wang, Qiangqiang Wang, Yubin Li, Shusen Li, Lifeng Zhang

"Numerical simulation on the fluid flow in a Flow-Control Mold (FC-Mold) were performed. The motion of inclusions were calculated. With FC-Mold, the flow pattern and surface velocity become more symmetrical, and at higher casting speed the velocity of liquid steel in the top region of the mold was largely reduced with the highest velocity of the meniscus reducing from 0.65 mis to 0.4 mis, and the meniscus shape became flatter. With FC-Mold, more inclusions approached to the surface of the slab and the amount of inclusion in the center of mold became fewer. Larger inclusions were easier to remove, however, the EM filed of the FC-Mold could hardly improve the removal of inclusions from the molten steel.IntroductionElectromagnetic brake technology is an effective method to control the flow pattern within continuous casting mold, together with other casting parameters, nozzle design and mold geometry [1-5]. Due to the interaction between the applied magnetic flux and the conductive molten steel inside the mold cavity, a force is generated in the direction opposite to the jet flow, which can decelerate the high speed steel jet from the SEN ports. The potential benefits include fewer surface and internal defects, fewer inclusion especially at higher casting speed. However if used imperfectly, electromagnetic forces can have opposite effect [6]. Numerical models are the best tool to optimize electromagnetic flow control. In the current study, numerical simulation was performed to investigate the flow field in a continuous casting FC-Mold, and the effect of different operation parameters on the flow, surface level and velocity in FC-Mold were discussed."

Jan 1, 2013

By Dmitri Nassyrov, In-ho Jung

"All relevant thermodynamic and phase diagram data in the CaO-Fe10-CaF2 system were critically reviewed. One set of model parameters describing the Gibbs energy of all phases has been obtained as a result of critical evaluation of the available data and optimization of the model parameters. The Modified Quasichemical Model was used to describe the interactions in the liquid phase. All calculations were performed using the FactSage thermochemical software.IntroductionSlags contaimng CaF2 are of significant interest to the steelmaking community. Notable examples of slags containing significant amounts of CaF2 include Electro-slag Remelting (ESR) slags [1] and mould flux for continuous casting [2]. The role of these slags is, among other things, to refine steel by absorbing inclusions and dissolved impurities. During slag-steel interaction, some iron from the steel will inevitably get oxidized and form iron oxides which will dissolve into the slag. With this in mind, it is important to understand the interaction between CaF2 and Fe,0 for accurate prediction of slag composition and process optimization. A thermodynamic optimization of the CaO-FetO-CaF2 was thus undertaken."

Jan 1, 2013

By F. Rivard, L. Rao, P. Carabin

"Advances in thermal plasma torches have resulted in this technology becoming a commercially viable solution for chemical and metallurgical processes. The main advantages of plasma are its ability to control process chemistry and to build small footprint reactors due to its high energy density and reactivity of the free radicals that are produced. This paper focuses on thermal plasmas produced by DC torches and their applications for waste treatment, production of high purity metals, and nanomaterials. Both transferred and non-transferred torches have been used as either a source of heat or as a reagent in various industrial processes. Retrofitting plasma torches in place of fuel oil burners lead to lower operating costs, capital cost and greenhouse gas emissions.INTRODUCTIONPlasma technology has become an ideal solution for many industrial chemical, metallurgical and mechanical processes [!]. Thermal plasma powered systems are typical used for their unique characteristics such as high energy densities, high temperatures, small installation sizes, rapid start-up and shutdown features, controlled process chemistry and use of electrical energy as a heating source resulting in decoupling the heat source from the oxygen flow rate [2]. Depending on the nature of the main plasma forming gas used, thermal plasma systems offer a high temperature heating source coupled with a highly reactive plasma plume rich in free radicals and ions which promote otherwise hard to drive chemical reactions, as well as high heat transfer rates."

Jan 1, 2013

By Zhonglin Ye, Yifeng Shi

"This paper has outlined forms of Au & Ag losses in copper smelting process and methods for increasing Au & Ag recovery, analyzed factors influencing Au & Ag recovery in copper converting process, presented Au & Ag behavior in copper electrorefining process, and reviewed effect of current density/electrolyte circulation rate during electrolysis and surface finish of cathode on Au & Ag losses. Measures and research direction for decreasing Au & Ag losses in electrolysis have also been introduced. Based on Au & Ag behavior in copper electrorefining process and previous studies by others, new approach for increasing Au & Ag recovery in copper smelter has been discussed. And brief comparison has made between continued multiplication method and equilibrium method application in the case of calculation of Au & Ag recovery in copper smelter.IntroductionAs gold and silver are the major by-products from copper smelting process, efficient Au & Ag recovery has become one of the key approaches for copper producers to increase economic efficiency. With similar physicochemical properties, Cu, Au and Ag belong to the first subgroup of elements in the same periodic table. Au and Ag will be enriched into Cu phase firstly when both matte-slag phase and copper-matte phase appear in copper smelting process. However, great changes have taken place in Au & Ag proportions into individual phase due to changes of physicochemical conditions in each smelting process. Metallurgists at home and abroad have carried out a great deal of pilot plant tests and laboratory tests in order to increase Au & Ag the former Soviet Union with regard to Au & Ag losses in copper smelting process in the 1970s and 1980s, and he proposed solutions to increase Au & Ag recovery in copper metallurgical plants. As more than 20 years passed, Jingchun Lu's paper, Discussion on Increasing Au & Ag Recovery in Copper Smelting System, remains as a literature of the most comprehensive study. Based on Jingchun Lu's literature, the authors of this paper discussed new approaches to increase Au & Ag recovery in copper metallurgical plants with combination of many researches done by other researchers for over 20 years."

Jan 1, 2013

By M. A. Barron, D. Y. Medina, R. T. Hernandez, I. Hilerio

"Chromium Nitride (CrN) thin fihns were deposited on steel AISI 316 substrates with reactive magnetron sputtering method. CrN films were produced under two different conditions. In the first one, the substrate was heated by a d.c. source. At the second coating was applied a negative substrate bias voltage. X ray diffraction, quantitative energy dispersive and scanning electron microscope, were employed to characterize their phases, chemical composition and microstructure. Additionally microhardness was evaluated using a microhardness tester. The results show that the phase formation of CrN thin films in the first case (with temperature) is better. Both coatings presented homogeneous surface. Their compositions shows differences though that gases flow are same. In attention to their hardness, presents an increment if it's compared with hardness substrate.Nomenclature.P Ar =Argon gas pressure during coating.PN2 = Nitrogen gas pressure during coating.Ts = Substrate temperature during coating.T f = Coating melting temperature. (CrN = 1050°C).E=Potential difference.t =Coating time.P=Target power (Cr) in magnetron sputtering de.HV = Vickers hardness.F = Applied charge.d= Average length of longitude of the two diagonals (mm)Introduction.Wear causes losses in materials surface, generating that components of mechanical systems suffer irreversible changes in their properties, causing a faulty operation of the system. It is important to control their effects, measuring and interpreting their causes clearly."

Jan 1, 2013

By Dan Wang, Qian Li, Yong-bin Yang, Tao Jiang

"Thiosulfate is one of the most promising non-cyanide lixiviants for gold leaching. However, the undesirable reaction between thiosulfate and copper (II) gives rise to increased reagent consumption, which results in high cost and huge limit to its development. This paper presents study on the effect of ammonia, copper (II) and Cu(NH3)l+ ions on the oxidative decomposition of thioulfate. It shows that the presence of copper (II) and Cu(NH3)l+ can significantly increase the thiosulfate oxidation, while ammonia is relatively unaffected. The oxidation of thiosulfate by copper(II) in the absence of ammonia is fast at first and then decreases as time increased within a certain time, which can postulate that an intermediate product is responsible for the decreased consumption. The effect of ammonia is depended on the interaction with copper (II), which was found to significantly affect the consumption of thiosulfate.IntroductionFor over one century cyanidation is widely used in industrial production of gold, due to its simplity of process and low cost of production. However, cyanide is a highly toxic chemical reagent used dangerously and brings serious environmental pollution. What's more, cyanidation has slow speed of leaching gold and poorly leaching effective for refractory ores. With the exhausting of free-milling gold ores and promoted environmental protection requests, the disadvantage of cyanidation becomes a growing problem. In recent years, more and more research activities have been focused on alternative processes using non-cyanide lixiviants. Among the non-cyanide lixiviants, thiosulfate is considered as the most promising one[l-5].Compared to cyanide, thiosulfate is an inexpensive, nontoxic and less-pollution reagent, which can form complexes with many metal ions. Thiosulfate leaching of gold has an acceptable leaching rate and is insensitivity to impurities. Moreover it presents advantage on the treatment of refractory gold ores such as carbonaceous gold ores, copper gold ores, complex arsenic and sulfur gold ores, and so on[6]."

Jan 1, 2013

By M. M. Sadawy

"The increased rate of exploitation of iron ores has resulted in a rapid depletion of high-grade iron ore deposits in Egypt. New iron reserves have to be discovered to secure the iron ore for steel production. This paper aims to study the characterization and magnetic separation of low grade Aswan iron ore. The results showed that Aswan iron ore is composed of oolitic hematite, goethite, quartz and kaolinite. The screen analysis indicated that Aswan iron ore had a uniform distribution of iron and silica in the different particle size fractions and there is no any particle size has high amount of iron or low content of silica. On the other hand the results of dry high intensity magnetic separation illustrated that this technique is not suitable for upgrading this ore.IntroductionIron is one of the common metals used in industry, as well as being the fundamental raw material used in iron-steel industry; products are wide spread even in daily uses. The total iron ore reserves of the world have been estimated as 3 70 billion tones; 160 billion tones is classified as economical, while 210 billion tones as potentially economical [1]. An estimated 98% of the iron ore exploited in the world is used in the manufacture of pig iron and steel, which are non-substitutable backbones of modem society. The rapid increase of world steel production over the last few years have required an equal increase in iron ore production, from 876.8 Mt in 2006 to 948.1 Mt in 2007 [2]. The increased rate of exploitation of iron ores has resulted in a rapid depletion of known high-grade iron ore deposits. This, in turn, has led to a dramatic increase of prices. In the absence of any major new discoveries of high-grade iron ore deposits, mining companies have turned to lower-grade materials to assess their beneficiation potential to expand their production base and beneficiation capacity, in order to satisfy future demand. Egypt is going to face shortage in iron production, consequently new iron reserves have to be discovered to secure the iron needed for the country [3]. Exploitation of low grade ores requires special equipments and techniques for recovery of minerals values. High gradient magnetic separators offer promise and great potential of application both technologically and economically in the processing of fine particles containing weakly or feebly paramagnetic components [4-6]. Within this existing framework, this research was initiated to assess the beneficiation potential of low-grade Aswan iron ore by high intensity magnetic separation."

Jan 1, 2013

By Sylwia Zymankowska-Kumon, Rafal Danko, Józef Danko, Mariusz Holtzer

"Burning of ceramic materials is carried out at temperatures 900+ 1300°C, in dependence of the required functional properties. The Faculty of Foundry Engineering together with the Faculty of Material Engineering and Ceramics developed the technology of production of burned ceramic materials with using spent moulding and core sands. The mentioned above waste materials of the foundry industry fulfilled -in plastic masses intended for obtaining ceramic materials -the role of the addition weakening clay raw materials. The laboratory investigations were fully verified by the results of industrial tests. It should be pointed out that none negative effects were observed at the stage of mixing raw materials and preparation of plastic masses. The measurements of exhaust gases emissions performed during burning the products containing spent moulding sands as well as during the normal production did not exhibit any significant differences, which could have indicated the harmful impact on the natural environment.IntroductionSands are used by the foundry industry to make metal casting molds and are a mixture of silica sand, bentonite clay and carbonaceous additives or resins. During the casting process, the molten metal cause thermal decomposition of carbonaceous additives or resins, which results in the formation of potentially hazardous organics, that are emitted to the atmosphere and condense in the molding sand. Each year the U.S. foundry industry landfills about 10 million tones of sand because it is no longer suitable to make metal casting molds. A large high-silica sand content in spent foundry sands (SFSs) generates rational premises for their reuse in other than foundry practice fields. Efforts to divert the SFSs from landfills and encourage their beneficial use in manufactured soils, geotechnical applications, the construction industry (road construction, highway construction), the building materials industry (cement, bricks, limestone manufacture), in the filling of mining cavities or in landfill construction (roads on landfills, permanent covers) are make [1-7]."

Jan 1, 2013

By San-chuan Tang, Wen Chen, Shun-ming Ning, Kan-ping Yu, Qiang Zhao, Xue-yong Xing

"A new type of desilication agent (PA-2) was selected by experiment based on the analysis of the characters of silica gel, and the influence of desilication type, desilication dosage, pH value, temperature and aging time on the desilicating effect was studied. The test results showed that on the conditions that pH was 2.0, temperature was 20""C, aging time was12 hours and the dosage of desilication agent was 0.23%, the desilication rate was higher than 93% in solution.IntroductionVanadium is an important strategic resources, which applies to steel industry and petrochemical industry. The main materials for vanadium product are steelmaking vanadium slag, stone coal and containing vanadium waste catalyst, etc. And stone coal is a low-grade carbonaceous silicified vanadium resource, which is unique material for vanadium extraction in China. Meanwhile, our stone coal reserves is No.l throughout the world.The silica acid solution containing vanadium is produced by acid leaching of raw stone coal or its roasted ore. The silica content of this solution is mostly high, besides, when pH is higher than 2 , the solution is unstable. Furthermore, it is very easy to generate gel substance with the increasing of pH value and standing time. 'Ibis silica gel is composed of colloidal particles with the size in 0.001 - 0.1 um. As a result, it is very hard even impossible for the following operation of solution."

Jan 1, 2013

By Jian Li, Guo Chen, Bingguo Liu, Hongying Xia, Jinhui Peng, Libo Zhang

"Decomposition of ammonium tetramolybdate to prepare Mo03 using silicon carbide crucible in microwave fields was investigated. The results were analyzed Using TG-DTG and X-ray diffraction. Meanwhile, the effects of heating rat, material thickness, socking time, socking temperature on the structure of preparing Mo03 were studied. TG-DTG curves show that the decomposition process of ammonium tetramolybdate is only one stage, in the temperature range 300-350°C, whose begin to decompose when temperature increases beyond 300°C. The molybdenum trioxide was prepared by thermal decomposition. The quality ofMo03 was not affected under the heating rat is 12°C/min. It was beneficial for decomposition ratio with the lower material thickness, longer soaking time, and higher soaking temperature. XRD curves showed that it is viable method for preparation of Mo03 by decomposition from ammonium tetramolybdate in microwave fields.IntroductionMolybdenum is widely used in national defense, aviation, industrial and agricultural production as rare refractory metal. Molybdenum trioxide is vital raw materials for the process of preparation of molybdenum. The traditional production technology of molybdenum oxide is that ammonium tetramolybdate is calcined in rotary kiln or 4-tube furnace [J,2J. But the longer production time, the higher production cost, the lower furnace thermal efficiency, and bigger the energy consumption, especially the powder is easy to leak, the working environment is poor by using rotary kiln [ 3 l _ The particle of molybdenum oxide is non-uniform by using 4-tube furnace because of the uneven temperature of every tube and the poor exhaust of boat bottom [4l _ However microwave heating is quick and uniformity, it is a meaningful research that the microwave is used in the process of calcining ammonium tetramolybdate."

Jan 1, 2013

By Bing Gao, Zhe Wang, Xiangdong Xing, Xueqi Zhang, Shan Ren, Jianliang Zhang

"In sintering, the flame front speed (bed permeability) and sinter qualities are greatly depended on the feed size, especially coke breeze and limestone particle size. It is well known that coke breeze provides sinter bed with heat to meet the demand of partial fusion and diffusion bonding while limestone reacts with iron ore to generate bonding phase in the sintering process. Accordingly, it is necessary to find the optimum combination of different particle size of coke breeze and limestone to yield sinter associated with better qualities. In this study, sinter was produced in the sinter pot with varying coke breeze and limestone particle size together in sintering of a coarse hematite iron ore. The sintering productivity was measured and all of the result sinters were examined by microstructure analysis and reduction degradation test (RDI test). For the sintering of a coarse hematite iron ore, it was found that the optimum mean particle size combination of coke breeze and limestone was 1. 71mm and 1.55mm in the sinter mix. On such a circumstance, sintering productivity was higher and the properties of sinter were better.IntroductionNowadays, as the main iron bearing burden material of modem blast furnaces, sinter has a great influence on the blast furnace operation. Sintering is a greatly complex process involving various chemical reactions to form kinds of mineral phases [1, 2]. In the sintering process, coke breeze is used for fuel and it generates heat to raise the green bed temperature. Limestone serves as flux and it reacts with iron ore to produce various mineral phases. On one hand, during the sintering process, the particle size of coke breeze can have an effect on temperature, atmosphere, the flame front speed and all of them act on the microstructure and mineral constitutions of sinter [3, 4]."

Jan 1, 2013

By Bohumir Jelinek, Sergio Felicelli, Mohsen Eshraghi

"We present a parallel lattice Boltzmann - cellular automaton model of the two-dimensional dendritic growth during solidification of binary alloys. The model incorporates effects of solute and energy transport under melt convection. The parallel performance of the algorithm is assessed. A loss in the parallel efficiency is observed when multiple computational cores per processor are utilized. Excellent strong scaling up to thousands of computing cores is obtained across the nodes of a computer cluster, along with the near-perfect weak scaling up to forty thousand cores. The presented solidification model shows a good scalability up to centimeter size domains, including millions of dendrites.IntroductionLattice Boltzmann method (LBM) is an attractive numerical technique for solving fluid dynamics problems. Its advantages are simple formulation and locality, with locality facilitating parallel implementation. In the present model, interface kinetic is driven by the difference between local actual and local equilibrium liquid composition [1]. The cellular automaton (CA) technique is deployed to track the solid-liquid interface [2]. A serial version of the present LBM-CA model with a small number of dendrites was validated against theoretical and experimental results in the previous publications [3, 4]. In this work, it is the first time that simulations with millions of dendrites were performed, something not possible with the computationally much more costly phasefield method [5].This research effort examines a technique for simulations of millions of dendrites in centimeter size domains, including thermal, convection, and solute redistribution effects. Nearly ideal scaling properties of the model are demonstrated. This extensively large landmark was achieved because of• the CA technique being two orders of magnitude faster than alternative, phase-field methods [5]• highly parallelizable LBM method, convenient for simulations of flow within complex and time dependent boundaries• availability of the powerful NSF Extreme Science and Engineering Discovery Environment (XSEDE) supercomputing resources"

Jan 1, 2013

By Cheng Gong-jin, Chu Man-sheng, Liu Zheng-gen, Zhang Yong, Liu Jian-xing, Xue Xiang-xin

"High chromium vanadium-titanium magnetite is one kind of Fe-V-Ti-Cr composite ore resources, which owes high utilization value. Owing to lacking systematic study on the sintering of this ore home and abroad, effects of carbon addition and basicity on sintering process and sinter metallurgical properties, such as sinter yield, vertical sintering speed, tumbler strength, sinter machine utilization coefficient, and low temperature reduction degradation were investigated systematically under laboratory conditions in the paper. The results shows that, when high chromium vanadium-titanium magnetite proportion is kept unchanged as 13% in sintering feeds, sintering process index and metallurgical properties are the optimum under carbon addition 5.0% and basicity 2.70, which meets the requirements of blast furnace burdens. This research provides technical parameters for practical sintering production of high chromium vanadium-titanium magnetite.IntroductionHigh chromium vanadium-titanium magnetite (hereinafter abbreviated as hi§h-Cr V-Ti magnetite), in which Fe is closely symbiotic with Ti and isomorphous with V and Cr1'- l, is one kind of typical vanadium-titanium magnetite resources with high comprehensive utilization value but the difficulties are extremely high due to complex chemical composition and mineral structure. At present, the feasible and mainstream utilization process of high-Cr V-Ti magnetite should be the route of agglomeration-blast furnace smelting. Thus, sintering production is the foundation for high-Cr V-Ti magnetite utilization. However, till now there are few research documentations on high-Cr V-Ti magnetite sintering home and abroad. Under the above background, this study focused on detailed researches of high-Cr V-Ti magnetite sintering. Sintering process uses the powders or fine iron ores to produce artificial rich ore with good metallurgical properties 4l Solid fuel provides 90% heat requirement during sintering15J. The appropriate amount of fuel and flux should be added during sintering in order to provide necessary heat and maintain the desired basicity16l. That is to say, carbon addition and basicity are two key factors affecting metallurgical properties of sintering products17J. Therefore, the effects of carbon addition and basicity on sintering process and metallurgical properties, including sinter yield, vertical sintering speed, tumbler strength, sinter machine utilization coefficient, and low temperature reduction degradation, are systemically investigated under laboratory conditions in the study, on purpose to achieve the optimization of sintering process for high-Cr V-Ti magnetite."

Jan 1, 2013