By Yuanbo Zhang, Xiaoming Mao, Zhixiong You, Zhenyu Fan, Tao Jiang

"It is generally known that the formation of calcium ferrite is favorable during the iron ore sintering, which dominatingly contributes to the improvement of strength and reducibility of the finished sinters. In this study, effects of roasting temperature and 02 content of inlet gas on the sintering mineralization properties of typical iron ores, including hematite, limonite, specularite and magnetite, were investigated. The results showed the amount of calcium ferrite initially increased then decreased with the increase of the roasting temperature. The temperature of maximum calcium ferrite generation amount for different iron ores was determined as follows: hematite and limonite was 1275 °C, whereas specularite and magnetite was 1250 °C. Increasing 02 content of inlet gas was advantageous to the generation of calcium ferrite during the sintering. The sequence of 02 content affecting the mineralization properties of different iron ores was determined as follows: magnetite > hematite > specularite > limonite.IntroductionThe mineralization property of iron ore plays a significant role in the mineral composition and microstructure of finished sinters, which determine the quality and output of the sinters [1-2]. The mineralization process of sinters is composed of solid-phase reaction, formation of liquid-phase and crystallization. The formation and crystallization of liquid-phase is the foundation to the mineralization as the quality of the sinter is poor when concreted by solid-phase consolidation [3-4]. With respect to the iron ore sintering, liquid-phase regarded as bonding phase is generated between the iron ores and fluxes at high temperature [5]. Calcium ferrite is the most favorable liquid-phase among the bonding phases which dominatingly contributes to the improvement of strength and reducibility of the finished sinters [6-8]. Especially for high iron-low silicon sintering and high basicity sintering, making sure sufficient calcium ferrite quantity and reasonable distribution is crucial to the sinters [9-10]. Therefore, carrying out the researches on the high temperature reaction properties of iron ores is of great significance [11]."

Jan 1, 2013

By Shichao Zhao, Ke Xie, Qijie Zhai, Wenbin Xia, Yuanyi Guo, Changjiang Song

"This paper investigated the structure evolution and phase formation ofFe-(11,13,15wt.%)Mn alloy under near-rapid solidification conditions. It is found that the area ratio of equiaxed zone in the Fe-13Mn alloy is the largest. And the primary dendrite arm spacing of Fe-(11,13,15wt.%)Mn alloy increased clearly with increasing distance from the surface. The volume percentage of HCP phase increased with increasing manganese content in the range from 11 pct to 15pct.IntroductionThe developing trend of automobile is the energy conservation, enviromnent protection, light weight, and high security. So the material would be required to the higher strength, higher plasticity and more likely to processing of automotive steel. Fe-Mn based alloys is considered as a potential material to the third generation automobile steel for its high damping performance [1], good mechanical properties [2-3], and high young's modulus [4]. And it is important that metastable HCP phases of Fe-Mn based alloys, which attracts technological interest for theoretical and experimental research [5-6].Metastable materials have been extensively used in the area of iron steels. Among various fabrication methods for high performance materials, rapid solidification is one of most popular ways to produce advanced materials by obtaining metastable phases. The solidification of metals in metastable phases provides access to an extended range of materials properties with novel properties [7]. Thus, in this work, Fe-Mn alloy metastable materials prepared by near rapid solidification is studied."

Jan 1, 2013

By Yuanbo Zhang, Zhixiong You, Daoxian Duan, Guanghui Li, Tao Jiang, Xiaohui Fan

"Presently, high-grade manganese oxide ores are usually utilized by a coal-based reduction roasting process. However, there were some obvious drawbacks, including serious environmental pollution, high energy consumption, etc. The reduction temperature is relatively high (850-900 °C). In this study, a kind of biomass, pine black charcoal, was used as a reductant to reduce low-grade manganese oxide ores. Under the optimal conditions of reduction temperature of 600~650 °C, roasting time of 30~45 min and ratio of ore to reductant 5:1, the leaching efficiency of manganese reached more than 98%. Compared with the traditional coal-based reduction process, the reduction temperature is reduced by 250-300 °C.IntroductionManganese plays a very important strategic role in the national economy, and it is widely used not only in the metallurgical industry, but also in the light industry, chemical industry, medicine, agriculture, etc [1]. The average grade of manganese ores in China is evenly about 21%, which belongs to typical low-grade manganese ores [2]. Therefore, large quantity of high-grade manganese ores is required to import in order to meet the rapid development of Chinese manganese industry. As reported, the conventional treatment of reduction roasting has been widely applied for processing manganese oxide ores, in which coals or reducing gases (CO, H2 or CHi) were usually used as reducers [3]. However, there were some insuperable problems, such as high energy consumption, poor operating conditions, serious environmental pollution, etc [ 4-9]."

Jan 1, 2013

By Lin Yang, Minjun Tang, Shuishi Liu, Jianfeng Zhou, Linjiang Qing, Xiaolei Song, Yufeng Guo, Tao Jiang

"The dynamics of oolitic hematite magnetic roasting was studied. The results show that oolitic hematite magnetic roasting was controlled by the internal diffusion, and the diffusion coefficient was 9.018x10-7 m2·s-1when the oolitic hematite was roasted at 650°C. Magnetic susceptibility improves when temperature increases and roasted time prolonges under the condition of roasting at 650°Cfor 50min, with the magnetic susceptibility is 39.88%. CaF2 and Na2C03 can significantly improve the magnetic susceptibility at the same roasting condition, and the magnetic susceptibility was 63.35% and 57.99% respectively, thus the reduction of oolimic hematite was promoted.IntroductionWith the continual depletion of free-milling iron ores and its rising price, developing the abundant resources of oolitic hematite has become one of the main research areas. The oolitic hematite accounts for 10% of China's iron ore reserve, and it also accounts for 30% of red ore reserve in China [1]. In order to exploit the oolitic hematite, there are many beneficiation research methods, including fine grinding/selective flocculation/high intensity magnetic separation or flotation, high-gradient magnetic separation, low intensity magnetic separation/high intensity magnetic separation/reverse flotation, chloridizing roasting/acid pickling, magnetic roasting/leaching process etc [2]. However, the oolitic hematite is easy to slim and the valuable mineral is covered by the slim, because of the tiny granule of value mineral, then the ooides are formed due to the state of layer morphology formed by iron ore and ganaue minerals [3, 4]. Fairly good separation indexes were hard to be obtained by traditional separation due to its structural features, so the magnetic property of the iron minerals will be changed with the use of the magnetic roasting [5, 6], which result in hematite variably altered to magnetite and simplified technological process so that a good separation indexes will be obtained by using the low intensity magnetic separation. Therefore, in order to provide theoretical direction of how to use the oolitic hematite effectively through the magnetic roasting, the oolitic hematite of GuiZhou province was studied, which emphasized on researching the dynamics of oolitic hematite magnetic roasting."

Jan 1, 2013

By JiaPeng Xu, Brian Lo, Uday B. Pal, Yihong Jiang, Soumendra N. Basu

"The Solid-Oxide Oxygen-Ion-Conducting Membrane (SOM) electrolysis process has been successfully tested on a laboratory scale, producing silicon directly from silica in a cost-effective and environmentally friendly way. A yttria-stabilized zirconia (YSZ) tube, closed at one end was employed to separate the molten salt containing dissolved silica from a liquid metal anode placed inside the YSZ tube. When the applied electric potential between the liquid tin cathode in the molten salt and the anode exceeds the dissociation potential of silica, oxygen ions are pumped out of the molten salt through the YSZ membrane and oxidized at the anode while the silicon cations in the flux are reduced to silicon at the liquid tin cathode. The presence of high-purity silicon crystals on the surface of liquid tin cathode was confirmed by scanning electron microscopy (SEM) and energy dispersive x-ray spectroscopy (EDS). Silicon crystals were extracted from tin cathode by chemical etching.IntroductionPhotovoltaics (PV) generate electrical power by using solar cells, and dramatically reduce the emissions of greenhouse gases (GHG). Through 2006 to 2011, it grew the fastest of all renewable technologies with operating capacity increasing an average of 58% annually [l]. However, the cost of manufacturing solar-grade silicon (SoG-Si) for high-efficiency solar energy production represents a major barrier to achieving the industrial goal for solar power of $1/Wp (watt at peak exposure) which would enable widespread grid parity. The current contract price of silicon to PV manufacturers is $50-$60/kg, with the spot market in 2007-2008 showing prices as high as $300/kg [2]. This makes the development of low cost and environmentally friendly manufacturing of high purity silicon very important."

Jan 1, 2013

By Zhucheng Huang, Lingyun Yi, Bin Chai, Tao Jiang

"A high iron content manganese ore was reduced at 900~1200°C and followed by a magnetic separation process. SEM and EDS analyzes were employed to examine the transformation of microstructure and phase in reduced sample and the mechanism was revealed. Results showed that elements enriched during reduction. Iron existed in the metal iron phase and most of oxygen formed compound with manganese. Consequently a clear distinguish between iron phase and manganese minerals formed, which was beneficial to the separation of iron and manganese. But the iron phase can not be monomer dissociation in grinding process and manganese compounds turned into magnetic product as package and mechanic inclusion due to the isomorphism of iron and manganese and the small particle size. And MnO could be found partially in iron phase, which hindered the further separation of manganese and iron.IntroductionManganese is widely used in industry. The amount of manganese used in steel industry is very huge and 90% manganese is used in steel industry. Manganese ore resources are rich in China, yet with fewer rich ore but more low-grade ore which accounts for 93.6% and fine refractory ore. The constitution of the ore is very complex and more than 73% of all the manganese ore contains iron[l,2]. With the increasing of consumption of steel, the demand for manganese is becoming larger and larger and the imported ore accounts for more than 50%. Therefore, how to use the manganese ore efficiently has very significant meaning. The main method is manganese residual, which is simple and stable. However, the development of the method is limited by the quality of manganese ore, the huge amount of manganese residual, the technology of blast furnace process and economics[3,4]. Chemical benefication which may pollute environment and is difficult to recover iron is still being researched[5,6]. The paper investigated the process in which anthracite coal was the reducing agent for coal-based direct reduction and magnetic separation of the ore, and SEM with EDS measurements were employed to examine the transformation of phase in reduced sample and the mechanism was revealed[7,8]."

Jan 1, 2013

By Suman Das, Justin J. Gambone, Rohan Bansal, Ranadip Acharya, Paul Cilino

"This paper focuses on generating a quantitative microstructure prediction model for Scanning Laser Epitaxy (SLE) process based on coupled flow-thermal modeling using Finite Volume method. SLE is a laser-based additive manufacturing process for the deposition of equiaxed, directionally solidified and single-crystal nickel superalloys through the melting of alloy powders onto superalloy substrates. In the current work, the detailed effects of natural and Marangoni convection on the flow field are studied and the results are analyzed in terms of the temperature gradient, vorticity parameter, melt pool dimensions and mushy region extent. The detailed property data of the processed superalloy and the laser scan path are incorporated in the model to predict the microstructure in realistic scenario. An optimization study is carried out to evaluate the critical parameter values at which the columnar-to-equiaxed and the oriented-tomisoriented transition take place. This work is sponsored by the Office of Naval Research through grant N00014-11-1-0670.IntroductionSLE is a laser-based additive manufacturing process for the creation of structures in equiaxed, directionally solidified and single-crystal nickel superalloys through the selective melting and resolidification of superalloy powders. In SLE, a tightly focused laser beam is guided by a highspeed galvanometer scanners allowing for tight control of the amount of energy being applied to the top of the powder bed, as well as the speed at which the melt pool moves across the substrate. Under the proper operating conditions and with sufficient substrate meltback, the solidification microstructure follows the morphology of the underlying substrate, allowing for directional and even SX growth.Several reports on the modeling aspects of laser cladding-based additive manufacturing approaches can be found in the literature. Approaches based on Finite Element Methods (FEM) and Finite Volume Methods (FVM) are employed for the thermal modeling of the system [1, 2]. Gaumann coupled the Columnar to Equiaxed Transition (CET) modeling with the Rosenthal solution in earlier work based on laser cladding [3]. Rappaz et. al. provided a detailed modeling of the microstructure/columnar orientation based on the solidification velocity and crystalline orientation [4]. This approach is based on the selection of the growth direction that closely follows the melt pool normal direction. Later on, substrate orientation is also taken into account [5, 6]."

Jan 1, 2013

By Zhang Jianliang, Zuo Haibin, Gao Bing, Wang Zhe

"As a result of the shortage of coking coal and the quality decrease of coke, it is important to know how to make better use of highly reactive cokes. The co-gasification behavior of highly and lowly reactive coke for blast furnace is investigated. The results show that: In the middle stage of reaction, the weight loss ratio of highly reactive coke reacted together with lowly reactive coke is higher than that of it reacted individually. However, the weight loss ratio of lowly reactive coke is lower. The weight loss ratio of highly and lowly reactive coke is almost the same as that of the weighted average. The scanning electron microscope analysis indicated that the reaction degree of surface and interior of lowly reactive coke is relatively uniform with the reaction time increased. And the reaction degree of surface of highly reactive coke is obviously higher than that of interior.IntroductionIn blast furnace iron making process, coke functions as heat supplier, reducing agent, carburizer and skeleton. With development of blast furnace iron making technology, the skeleton function of coke is becoming more and more important in requirements of large scale furnace and high pulverized coal injection. High reactivity coke is usually produced by cheap coal with bad quality, and is not good for blast furnace process. The reactivity of coke is mainly determined by the coals used, and the resource of good quality coking coal is limited and is non-renewable. In order to fulfill the need of blast furnace, a lot of research have been done to improve coal matching using new kinds of coal to enlarge resource, in which coking coal and fat coal are reduced, whereas low price coal with bad caking property are used to lower the cost, and this would inevitably increase the reactivity of coke [1-4] Blast furnace iron making would still be the main stream for a predicted future, and high reactivity coke would correspondingly be used more and more, so it has great importance to study how to use high reactivity coke in blast furnace."

Jan 1, 2013

By Gowda H. S. Desai, A. Herbert Mervin, P. G. Mukunda

"The mechanical properties of cast iron depend on the graphite morphology and characteristics of metallic matrix. In spheroidal graphite iron these properties are affected by the nodule count, nodule percentage, nodularity, nodules per square mm, nodule types and size distribution. In this work an attempt is made to study of the effect of centrifugal and gravity casting process on the morphology and mechanical properties. A comparison of microstructure and mechanical properties of specimens of the cast are studied. It has been observed that the centrifugal effect produces an increase in rupture strain but hardness is unaffected. In microstructure it has been observed that the centrifugal effect produces an increase in the number of bigger nodules and decrease in the number of smaller nodules and an increase of nodules per square mm. It has no effect on nodularity percentage. The centrifugal casting process produces better mechanical properties.IntroductionCast iron, the first man-made composite, is at least 2500 years old. It remains the most important casting material, with over 70% of the total world tonnage [1,7]. The main reasons for cast irons longevity are its wide range of mechanical and physical properties coupled with its competitive price [l]. Gray cast iron is traditionally used in many industries because it is characterized by a flexibility of use, excellent castability, low cost, wide range of achievable mechanical properties. Gray cast irons are selected according to their tensile strength, high modulus of elasticity, good wear resistance and good machinability are desired and for this a high-strength cast iron is selected [2].Flake Graphite and Spheroidal Graphite irons are predominantly being used to manufacture heavy automobile components throughout the world. The properties of gray iron castings are much dependent on foundry practice. Perhaps the most interesting feature of the family of cast irons is the morphology of the graphite phase, which occurs as a result of changes in chemical composition, melting, melt handling techniques and the process of solidification and subsequent cooling. The significance of these differences through graphite morphology is observed primarily in their effect on the physical and mechanical properties of the iron, but in the foundries these are also known to influence the ability to manufacture sound and dependable castings."

Jan 1, 2013

By Wei-ling Wang, Ryosuke O. Suzuki, Xiang-ning Meng, Miao-yong Zhu

"A finite-element thermal-stress model of continuous casting mold is conducted to predict deformation of copper plates and its change with different cooling structure. The results show that deformation behavior of copper plates is mainly governed by cooling structure and thermal- mechanical conditions, deformation amount is related to structure geometry, and a small deformation mutation occurs in cooper-nickel boundary due to different properties. The maximum deformation of hot surface centricities of wide face locate at 100 mm below meniscus and that of narrow face locate at meniscus and terminal of water slots and significant curvature fluctuations on both sides of copper-nickel boundary. The maximum deformation of centricities is increased up to 0.05 mm with thickness increment 5 mm of copper plates, and maximum deformations are only depressed 0.01 mm and 0.02 mm with increments of 1 mm nickel layer thickness and 2 mm water slot depth respectively.IntroductionIn conventional continuous casting of steel, a large amount of sensible and latent heat of molten steel dissipate in primary cooling zone and make continuous casting mold under enormous heating load giving rise to thermal stress, deformation, high-temperature fatigue and creep not only depress mold life-span, but reduce casting stability [1] Many studies focused more on heat transfer, solidification and shrinkage of solidifying shell to provide inverse proposals for optimizing cooling system and even designing new taper of mold [2,3], but it is generally useless to those of having been manufactured or being put into production. Therefore, mold-related forward problems show necessity to be discussed deeply, and stress and deformation distributions based on special thermal conditions in mold should be analyzed in order to explore suitable cooling structure of mold directly. Samarasekera et al. [4] examined heat flow and distortion of two-dimensional longitudinal sections and investigated effect of cooling water velocity, copper plates thickness and carbon content on formation of rhomboidity and longitudinal comer cracks. O'Connor et al. [5] developed a three-dimensional mathematical model to compute thermo-mechanical state in thin-slab mold and calculated temperature and deformation of mold wall to assess roles of various process parameters on impacting mold life. Thomas et al. [6] predicted temperature, distortion and residual stress in mold and indicated increased distortion requires increased remachining, which reduces mold life and increased residual stress increases the probability of a catastrophic crack failure. Park et al. [7l determined heat-flux profiles in funnel-shaped and parallel thin-slab molds based on an inverse heat conduction model and thermocouple temperature measured in-plant and put them into three- dimensional finite-element thermal-stress model to predict temperature, distortion and residual stress of mold wall. Korie et al. [SJ focused on prediction of temperature, distortion and residual stress in mold and in particular to clarify that mold life is significantly affected by temperature and its rigidity, but little effect by mechanical including clamping force, bolt prestress, friction and ferrostatic pressure. Meng et al. [9l predicted temperature and thermal stress in a slab mold and analyzed effect by cooling system geometry and casting speed quantitatively. In present study, a three-dimensional finite-element thermo-mechanical model with type-switched element is transformed from previous heat-transfer finite-element model [9l, and mold deformation is simulated in order to shed light on thermo-mechanical behavior with special thermal conditions and different mold geometry at high casting speed."

Jan 1, 2013

By Girley Ferreira Rodrigues, Crocce Denise Romano Espinosa, Victor Bridi Telles, Eduardo Junca, Jorge Alberto Soares Tenorio

"Steel sector is responsible for the generation of solid waste, liquid and gaseous effluents. The Solid waste are mainly composed of slag, dust, sludge and scrap. The industry generates approximately 650kg of solid waste per tonne of steel. Approximately 10% of this waste is in the form of dust and mud. The basic oxygen furnace dust is a waste generate by steel sector. Each tonne of produced steel generates 10 to 20 kg dust. Thus, the aim of this paper is study the reduction of pellets made with BOF dust using hydrogen and study kinetic during the reduction. The tests were performed in a netzsch thermobalance to obtain the data of lost mass. This loss mass is coming from iron oxides present in the BOF dust.IntroductionThe generation of solid waste is a problem for many companies in the steel sector. The main solid wastes generated are slag, dust, sludge and scrap [1]. Beyond solid waste liquid and gaseous effluents are also generated.The basic oxygen furnace is responsible for 60% of all steel produced. This sector is the second largest generator of solid waste from an integrated steel mill, contributing with 27% of solid waste generated in a plant ( 5-7 million tons of waste generated annually worldwide) [2,3,4]."

Jan 1, 2013

By Jean Igor Margem, Rômulo Loiola, Sergio N. Monteiro, Foluke S. de Assis, Frederico M. Margem

"Fibers extracted from the ramie plant have been traditionally used in textile and are now being considered as polymeric composite reinforcement owing to their superior strength. Recently the mechanical behavior of ramie fiber reinforced polyester composites was investigated but no significant improvement was found. Therefore, the objective of this work was to carry out a similar investigation by changing the type of polymeric matrix. Specimens with up to 30% in volume of ramie fibers incorporated into epoxy were bend-tested until fracture. The results showed a moderate improvement with a tendency of decreasing stress for higher amounts of ramie fibers due to the weak interface developed with the epoxy matrix.IntroductionThe engineering application of natural fibers extracted from cellulose-containing vegetables, also recognized as lignocellulosic fibers, is presently considered an environmentally correct alternative to replace more expensive, non recyclable and energy-intensive synthetic fibers [1-3]. In fact, composites reinforced with traditional fibers such as coconut, sisal, jute, hemp, etc ... are already on the market in substitution for common glass fiber automobile components [4-6]. Even less known fibers like curaua from the Amazon region are being industrially used [7]. Economical and environmental reasons sustain a promising future trend for natural fiber composites. In comparison with the less expensive glass fiber among energy-intensive synthetics, lignocellulosic fibers are approximately five times cheaper. For the current situation of our planet, natural fibers are regarded as ""green"" environmentally friendly materials. They are abundant, renewable, biodegradable, and recyclable, above all, neutral with respect to carbon dioxide emission, associated with global warming.Several relatively unknown lignocellulosic fibers such as piassava [8], sponge gourd [9], sugar cane bagasse [10], buriti [11] and ramie [12], with simple and limited applications, or just byproducts, are now being investigated for their potential as composite reinforcement. This could widen the offer of new lignocellulosic fibers for composite reinforcement. The banana fiber, in particular, has a tensile strength around 700 MPa [13], which is comparable to the strongest lignocellulosic fibers used as composite reinforcement.In addition to polyester, the epoxy is another relatively strong polymer used as composite matrix. Therefore, the objective of the present work was to assess the mechanical properties obtained by flexural test, for epoxy composites reinforced with different amounts of banana fibers."

Jan 1, 2013

By Emanuel Negrao Macedo, Edinaldo Cunha, Mauro Oliveira, Jose Antonio da Silva Souza

"This paper presents the study of the increasing addition influence of the bauxite waste in some properties of polymeric matrices composites reinforced with natural fiber: Curaua (Ananas Erectifolius smith). There were evaluated properties as density, tensile and flexural resistances. The high pH provided by the waste is used as hydrolysis agent, providing the pectin cement dissolution of the fiber bundles, and therefore, improving the mechanical adhesion in the fibermatrix interface and the increase of the fiber bundles aspect ratio. Furthermore, the content of silico-aluminous material in the waste provides increase in the composite abrasivity, which is destined to civil and naval construction. The fact of being a low-cost and highly available waste turns the red mud in a high potential material as polymeric composite filler.IntroductionRed mud is an insoluble residue, originated from the bauxite refining through the Bayer Process [1]. It is an Iron Oxide rich material [2] (substance responsible for the red brick color), it has a complex chemical composition [3], and its composition is highly dependent of the type of bauxite used in the process [4]. It has high alkalinity (pH= 10 - 12.5) and a very small solids size distribution (95% diameter< 44µm) [1], what turns the red mud a serious environmental pollutant.The utilization of fillers on composite materials is done after many necessities; however, one of the major necessities is the cost reduction [5]. Furthermore, mechanical and thermal properties of polymers usually are improved by the addition of inorganic fillers [6], being an example of this improvement the reduction of the flammability of polymer matrixes due to the addition of functional clays [7]. In this way, the red mud becomes potential filler for composites, since cheap and easily available fillers (like red mud) are a good option to reduce costs [8]."

Jan 1, 2013

By Jun Li, Lin Chen, Tian-zu Yang, Wei-feng Liu, Wan-da Bin

"The Chinese bismuth production accounts for more than 80% all over the world in 2011. The main raw materials of bismuth smelting are bismuth concentrate and by-products of Cu or Pb smelting process. Many traditional methods of bismuth smelting in china was reviewed in this paper, such as reverberating furnace smelting, blast furnace smelting, fire-refining, ferric chloride leaching-hydrolysis, slurry electrolysis, and so on. But all the traditional pyrometallurgy or hydrometallurgy process have such shortages of low recovery, poor environment, and high cost. Therefore new technologies are introduced into the smelting process of bismuth concentrate, such as low-temperature alkaline smelting and side-blown bath smelting with oxygen-enrichment. These technologies have got great progress on energy saving, emission reduction, and friendly environment. Finally the development direction of new technology on bismuth smelting was prospected.IntroductionAs a green metal, bismuth has a wider applications, just extending from the traditional medicine, metallurgical-chemical engineering, low-melting alloys, solders, catalyst, and electronics to cosmetics, flame retardant, storage battery, semiconductor, supper conductor and nuclear energy etc[1,2,3,4,5,6,7]. This will increase the production of bismuth and promote the development and progress of bismuth smelting technology. At present, The major bismuth-product countries are China, Mexico, Peru, KZ, Bolivia and Canada etc, and China are dominating. A survey from the USGS[8] showed that Chinese bismuth production were 12,500 tonnes and got 80% of the world's in 2011. Thus the technology of Chinese bismuth smelting have a great representativeness."

Jan 1, 2013

By Zhihao Yue, Honglie Shen, Yahui Teng, Ye Jiang

"In this paper, manganous nitrate [Mn(NO3)z] was used to assist the etching of silicon wafer in hydrofluoric acid (HF) for the antireflective application, and alumina (Al2O3) layer was deposited on the surface of the etched sample by atomic layer deposition method for further antireflection. The surface morphological and compositional studies of these samples were performed by scanning electron microscopy attached with an energy-dispersive X-ray spectrometer. The surface reflectance measurements were carried out using UV-Vis-NIR spectrophotometer. Binary structures of pyramids and nanopores were obtained by etching the alkaline textured monocrystalline silicon wafer in HF and Mn(NO3)z mixed solution for not more than 15 min. But excessive increase of etching time of up to 30 min resulted in the whole destruction of pyramids. The average reflectances of the 5-min-etched sample before and after being coated with 75-nm-thick Al2O3 layer are 4.62% and 3.47% in the range of 200-1000 nm, respectively.1. IntroductionAs we know, the reflectance of silicon wafer after being sliced is so high that the maximal photoelectric conversion efficiency of silicon based solar cells is limited. Therefore, alkaline texturization process was used for silicon solar cell in industrial production. But the reflectance of this alkaline textured wafer is still greater than 10% and this process can only be used for monocrystalline silicon solar cell."

Jan 1, 2013

By Huimin Lu, Lian Zhou, Qiang Li

"A three-dimensional mathematical model is developed for the regenerative rotary hearth furnace with 40 meters medium diameter. The influence of combustion switchover and outlet pressure on the fluctuation and distribution of temperature and pressure is studied with numerical simulation method. The results showed that the temperature field and flow field is suitable for requirement of industrial production; the fluctuation of the temperature field and pressure is acceptable; the influence of outlet pressure on the furnace pressure is great.IntroduceRotary hearth furnace which is originally utilized as heat treating and reheating industrial furnace, now is also used for carbon based DRl production. With the need of market and the concern of resource recycling and environmental issues, the DRl production from ore or from waste material by rotary hearth furnace attracts more and more attentions from steel industry [1,2].When rotary hearth furnace works, the feed pellets are charged on the hearth and rotate within an annular furnace chamber with the process of reduction. For the sake of rapid reduction, usually the depth of the pellet is one or two layers, accounting for less than 90% of the volume of furnace. As result, the exhaust gases carry away a lot of heat, so that energy utilization efficient is low [3]. Currently, in order to reduce the consumption of energy and improve the production efficiency, many methods have been adopted. The regenerative combustion technology is one of the most promising."

Jan 1, 2013

By Xie Zhang, Jiang Diao, Xin Qiu, Lu Jiang, Bing Xie, Hong-Yi Li

"Duplex converter process, in which the first converter is used for removing phosphorus from hot metal (De-P), is an important way to produce low P-content and ultra-low P-content steels. In order to improve phosphorization removal and formation of slag with high basicity at relatively low temperature during dephosphorization converter process, effects of temperature, silicon content in hot metal and varied compositions of the De-P converter slag on phosphorus distribution between the slag and hot metal were investigated with thermodynamic calculations and by laboratory scale experiments in present work. Results showed that phosphorus distribution ratio between slag and metal was varied in 10.6~26.6 when basicity of the slag was in the range of 1.5~2.1 at 1370, and the distribution ratio was increased with increasing basicity and Fe10 content in the slag.IntroductionIt is known that phosphorus exists in steel in the form of solid solution, which can significantly improve strength and hardness of steel at room temperature. However, the plasticity and toughness of steel, especially the low temperature plasticity is sharply reduced and leads to high ductile-brittle transition temperature. This phenomenon is commonly known as cold brittleness of steel [1~3]. Hence, phosphorus should be removed as much as possible in the steelmaking process, because it is generally harmful to the iron and steel products."

Jan 1, 2013

By Naixiang Feng, Shaohu Tao, Zhihui Wang, Yuezhong Di

"A novel vacuum aluminothermic reduction lithium process was developed in present work which used lithium carbonate, alumina and calcium oxide as raw material. The process mainly contained three steps. The first step is that LiA102 clinker is prepared in ambient environment, then metal lithium is vacuum extracted from LiAl02 clinker with aluminum power as reducing agent, and the last step is that alumina is leached from the reduction residue with a mixture of sodium hydroxide and sodium carbonate. The results show that the lithium reduction ratio can be over 95% under the conditions of reduction temperature 1423K, reduction time 3h, and aluminum excess 20%. The main components of reduction residue are CaO· Al203 and 12Ca0·7Alz03. The alumina leaching rate of calcium aluminate in residue is over 80%. High-whiteness aluminum hydroxide can be obtained by carbonation precipitation of the reduction slag leaching solution.IntroductionWith a density about half of water, lithium is with the lowest density of all solids, mere 0.5 g/cm3 at 20 °C [l]. Lithium is widely used in aerospace, aviation, nuclear-generated power and electric battery industry. Nowadays, over 90 % of the world's primary lithium is produced by molten salt electrolysis [2-4]. But the development of molten salt electrolysis will be effected by some factors: cost, environment, and so on. Vacuum thermal reduction may be used extensively in future because of its low-energy consumption, high-purity and short-cycle."

Jan 1, 2013

By Donghai Li, Cheng Pan, Xuewei Lv, Mei Liu, Enguang Guo

"Phosphorite is the main raw material for the production of phosphorus in chemical industry. More attentions have been drawn to the phosphorite concentrate beneficiated from low-grade phosphorite due to the decrease of high-grade phosphorite. For another, the agglomeration process is necessary for the phosphorite concentrate after beneficiation process. The mineralogy and sintering process of the phosphorite from Leshan, China were studied in this work. The result shows that the main phases in the phosphorite are fluorapatite (Ca3(P04)3F), hydroxylapatite (Cas(P04)3(0H)), quartz (Si02) and dolomite (CaMg(C03)2). The yield of the sinter increases with increasing the carbon dosage to 7%, and then decreases when it continuously increases. Similar regularities were found for the strength and the content of P20s of the sinter. The best strength of the sinter as well as its P205 content were discovered when the carbon dosage is 7%. Fluorapatite ((Ca5(P04)3)F) is the main phase in the sinter while fuggerite (Ca2MgSiz01) is the main binder phase.IntroductionPhosphorus is an important foundation industrial raw material of national defense industry, food industry and chemical industry, where it is used to produce red phosphorus, phosphonium hydroxide, phosphorus pentasulfide and phosphoric anhydride[l-2]."

Jan 1, 2013

By Zhiqiang Han, Anil K. Sachdev, Baicheng Liu, Guomin Han, Alan A. Luo

The growth of precipitate phase ,B-Mg11Al12 in Mg-Al alloy is closely related to interface anisotropy and elastic interaction. The aim of this work is to investigate the effects of the interface anisotropy and elastic interaction on the morphology evolution and growth kinetics of the precipitate. In the work, the precipitation of ,B was studied using phase field modeling. In the model, the chemical free energy of the precipitate and the matrix were obtained via thermodynamic calculation. It is demonstrated that the interface anisotropy results in lath-shaped precipitate and the elastic interaction affects the shape of the end of the precipitate. The interface anisotropy causes uneven growth in different directions and the elastic interaction influences its preferential growth orientation. By combining the interface anisotropy and elastic interaction in the phase field modeling, the results showed that the precipitate phase has a lath-shape with lozenge ends, which is in agreement with experimental observations.

Jan 1, 2013