By Chang Wei, Fan Zhang, Zhigan Deng, Minting Li, Cunxiong Li, Gang Fan, Xingbin Li

Marmatite is an important resource of zinc, which exist in forms of high iron and high indium. In order to recycle the valuable metal from these ores, the testwork of simultaneous leaching on neutral residue mixed with zinc concentrate of high iron and high indium has been conducted. The primary objectives are to leach the zinc and indium remaining in the neutral leach residue as ferrite using acid, and to reduce the ferric iron in solution to the ferrous by zinc concentrate, thereby extracting the zinc and indium in the zinc concentrate. The results indicated that in the following conditions, mass ratio of neutral residue to zinc concentrate of 1:0.25, particle size of 74-58 μm, initial sulfuric acid concentration of 150 g/L, liquid to solid ratio of 8 L/kg, temperature of 90°C, reaction time of 4h, the leaching efficiency of zinc and indium were over 95%, nearly 90% Fe was Ferrous in the leaching solution. This process effectively extracted zinc and indium and converted Fe3+ into Fe2+ in solution, and simplified the traditional process of reduction after leaching.

Jan 1, 2016

By KAGAN BENZESIK, Onuralp Yücel, Mehmet Bugdaycı, Ahmet Turan

ZrB2 and B4C are one of the most significant advanced ceramics. They are being used in various industrial areas from space technology to nuclear industry owing to their physical properties such as high melting point, high thermal/electrical conductivity and low density. Present study was conducted in two main stages: Self-propagating high-temperature synthesis (SHS) reactions and leaching. ZrO2, Carbon black, B2O3 were used as starting material to produce ZrB2-B4C powders by SHS. Also Mg powder was used as the reductant. The reaction mixtures (approximately 100 g) were mixed thoroughly 15 minutes in a turbula mixer and charged into Cu crucible and compacted. W (tungsten) wire was placed at the top of copper crucible and the reaction realized by passing current through the wire. After initiation, a highly exothermic reaction became in a self-sustaining mode and propagated throughout the SHS mixture. The samples were characterized by using AAS and X-Ray Diffraction.

Jan 1, 2016

By Yunhua Gan, Xiaowen Chen, Yang Tong

Experimental studies of electro-spraying were carried out using ethanol as fuel in a microcombustor under combined electric field. And the effects of different electro-spraying modes on the combustion efficiency were analyzed. Results showed that when ring electrode potential was invariant, there were four different electro-spraying modes with the variations of nozzle potentials, which were varying with the flow of ethanol. The cone-jet mode was the stablest one during the whole experimental process. The atomized ethanol was ignited and combusted stably near the steel mesh, the combustion efficiency increased firstly and then decreased along with the increasing of the equivalent ratios, reached the maximum values when the equivalent ratio equal to 1.0. And the maximum values were the highest at the cone-jet mode, and the lowest at the pulsed-jet mode.

Jan 1, 2016

By Mao Chen, Baojun Zhao, Zhixiang Cui, Leonel Contreras, Chuanbing Wei

Bottom blown oxygen copper smelting process developed at Dongying Fangyuan Nonferrous Metals shows many advantages such as flexible feed requirement, high productivity, low energy consumption and high direct copper recovery. However, the weak acid generated during the process is not stable which influences the waste management and continuous operation. The amount of the weak acid is determined by SO3 formed in copper smelting process. SO3 can be formed inside copper smelting furnace and boiler at different conditions. Effects of temperature and oxygen partial pressure on the formation of SO3 during copper smelting process have been discussed thermodynamically. Understanding of the mechanisms for SO3 formation will enable the operation of bottom blown copper smelting furnace to be optimized and generation of the weak acid in the process can be managed. The fundamentals developed in this study can also be applied to other copper smelting processes.

Jan 1, 2016

By Dianyuan Dang, Guihong Han, Wenjuan Wang, Tao Jiang, Yanfang Huang

In this study reduction kinetics and swelling behaviors in "two-step process” were investigated by weight-loss technique and visualizing physical changes of pellet. Results showed that reduction degree (r) increased with increasing temperature and time. According to the dynamic calculation, when reduction temperature was lower than 1000°C the reduction process was controlled by chemical reaction with apparent activation energy of 72.27 kJ/mol. When reduction temperature was higher than 1000 , the equation of t/[1-(1-r)1/3] against [1+2(1-r)-3(1-r)2/3]/[1-(1-r)1/3] followed straight lines, demonstrating that reduction was mixed-controlled. Swelling experiments indicated that the maximum swelling index increased with the increase of reduction temperature and CO content.

Jan 1, 2016

By Bo Jiang, Jiusan Xiao, Hongmin Zhu, Kai Huang, Shuqiang Jiao

Carbothermal selective reduction of simulative titanium slag and various titanium raw materials were presented and SiO2 was found to be partially reduced, forming a series of Fe-Si alloys during the process. Thermodynamic analysis of the selective reduction between TiO2 and SiO2 was performed using HSC 6.0 software, then a series of equilibrium experiments were designed and presented. The activity of Si reduced from SiO2 was affected by the presence of Fe reduced from FeOx and the generation of Fe-Si alloys, promoting the reduction of SiO2 in the whole process. The results of experiment are in great accordance with the calculated data obtained from thermodynamic analysis.

Jan 1, 2016

By Shengqin Zhang, Jagannath Pal, Yousef Mohassab, Hong Yong Sohn, Mohamed Elzohiery

The kinetics of magnetite reduction with mixtures of hydrogen and CO of various compositions has been investigated as part of the development of a flash ironmaking process at the University of Utah. This new process bypasses the cokemaking and pelletization or sintering steps required for the blast furnace. The particle kinetics were studied using magnetite concentrate particles of different sizes. Reduction degree of 60% was achieved in a few seconds in at 1350 oC using CO reductant alone and over 90% when H2 + CO gas mixture was used. The effects of reductant partial pressures, temperature, and particle size on the reduction kinetics were studied.

Jan 1, 2016

By A. De, J. S. Zuback, T. Mukherjee, T. DebRoy

For successful commercial applications of additive manufacturing, metallic parts need to be defect free, structurally sound and reliable. However, additively manufactured metallic parts are susceptible to distortion, lack of fusion defects and compositional changes. Methods to measure susceptibilities of various alloys to these defects are needed but not currently available. Here we show that the necessary theories can be developed based on a well-tested numerical heat transfer and fluid flow model and decades of research in the field of welding. The proposed theories are validated with experimental results reported in the literature.

Jan 1, 2016

By Baohua Li, Yanhui Liu, Shengping Li, Xuewei Lv, Yun Chen

There are almost ten billion tons of vanadium-bearing titanomagnetite in Panzhihua-Xichang area. However, iron ores in Hongge, which has the most abundant reserves in the four mine areas in Panzhihua, have not been utilized sufficiently so far. The reason behind this is the relatively high Cr2O3 in the ores (0.49 %~0.82 %), that due to its high melting temperature will negatively influence the blast furnace reduction and slagging process. Therefore, in the blast furnace process, Cr is hope to be reduced into molten iron, which can reduce slag viscosity problems. Slag iron reduction experiments were conducted to quantify the Cr reduction. Experimental results shows that with the increase of TiO2, the content of Cr in the hot metal is decreased when balanced. And during the initial stage of the reduction reaction, the reaction kinetic model is a first-order reaction.

Jan 1, 2016

By Guo Chen, Xuefeng Liao, Tu Hu, Shengzhou Zhang, Hongying Xia, Jinhui Peng, Libo Zhang

Pine nut shell is as raw material for preparation of high surface area activated carbon (HSAAC) by microwave induced KOH activation. The effects of microwave power, activation duration and KOH/C mass rate (R) on the iodine adsorption capability and activated carbon yield were investigated. Additionally the surface characteristics of HSAAC were characterized by nitrogen adsorption isotherms and SEM. The operating variables were optimized utilizing the response surface methodology and were identified microwave power 738W, activation duration 17 min, and R 4, corresponding to a yield of 46.28 % and an iodine number of 2154 mg/g. The key pore structure parameters of HSAAC such as the Brunauer–Emmett–Teller (BET) surface area and total pore volume were estimated to be 3819 m2/g and 2.09 mL/g, respectively. The findings strongly support the feasibility of microwave heating for preparation of HSAAC from spent pine nut shell by microwave induced KOH activation.

Jan 1, 2016

By Sedef Pinar Basag, Onuralp Yucel, Ahmet Turan

Niederschlag process is commonly used to produce metallic antimony. The process is a metallothermic process which is conducted in one step for metallic antimony production. Using this method Sb2S3 is mixed with coal and metallic iron and subjected to reduction. During heating, antimony sulfide is decomposed and sulphur combines with iron to form the matte phase. Metallic antimony is collected at the bottom of the crucible. In this study, evaluation of Sb2S3 concentrate, extracted and obtained from West Anatolian Region of Turkey was investigated by using Niederschlag process. The reductant stoichiometry, reduction temperature and duration were carried out in the experiments. Chemical analysis methods by using atomic absorption spectrometry (AAS) and X-ray diffraction spectrometry (XRD) techniques were used for the characterization of the concentrate, metallic nuggets and matte phases.

Jan 1, 2016

By Yuanbo Zhang, Ruijun Wang, Qian Li, Zhao Jing, Guanghui Li, Zhengwei Yu, Chen Liu

The high content of sodium and potassium in sinter is harmful for blast furnace ironmaking. Reductive sintering technology can remove more alkali metals than conventional sintering process. In order to improve the removal ratios of Na and K, reductive sintering with both CO-containing flue gas circulation and carbon-bearing pellet was conducted in this study. Experimental results show that all indexes except the VSV and P were improved in reductive sintering with CO circulation. Flue gas circulation technique combined with carbon-bearing pellets were beneficial to reductive sintering, because it could maintain good sintering indexes and enhance the removal of Na, K. The best removal ratios of Na, K and reduction degree of iron oxides were 20.37%, 63.73% and 23.76%. In reductive finished sinter, silicate mineral becomes the important binder phase, and main iron mineral phases are wustite (FexO) and magnetite (Fe3O4).

Jan 1, 2016

By Linfeng Zhou, Rong Sun, Guanghui Li, Zhiwei Peng, Tao Jiang

The effects of microwave roasting on separation of rhenium (Re) and molybdenum (Mo) from a molybdenite concentrate have been investigated based on evaluation of the heating characteristics of the concentrate in the microwave field. The results show that a variety of operating variables, namely microwave power, sample weight, sample geometry, roasting temperature, roasting time and atmosphere significantly impact on the volatilization rates of Re and Mo. The optimum conditions for Re-Mo separation are microwave power 1300 W, sample weight 20 g, sample geometry pellets, temperature 600 oC, time 1.5 h, and atmosphere 20%O2. Under these experimental conditions, the volatilization rate of Re reaches 88.12%, while that of Mo is just 5.15%. Microwave-assisted roasting provides an alternative route to separating Re and Mo from molybdenite concentrate.

Jan 1, 2016

By Pengcheng Li, Wei-Tong Du, Yu Wang, Gang Wen

Carbon dioxide could be utilized as a weak oxidant and a kind of coolant to oxidize elements, meanwhile, helping control the temperature during the converter vanadium extraction process. However, the optimum content of CO2 and the cooling effect of CO2 at low content have not been reported. In this study, experimental research based on the influence of different CO2 contents from 0% to 25% injected to the vanadium-containing hot metal was carried out, as well as contrast experiments of O2-N2 mixed blowing. The results indicated that the optimum content of CO2 was 15%. Under the optimum condition, the oxidation of [C] was the lowest and the oxidation rate of [V] was 96.9%, while the temperature was also lower than the O2-N2 mixed blowing. This paper provide a potential property for utilizing CO2 during the converter vanadium extraction process.

Jan 1, 2016

By Jintao Gao, Zhancheng Guo, Chong Li

A new approach to enrich MFe and RO phase from the converter slag by super gravity was investigated. The samples obtained by the gravity coefficient G=600 and cooling rate V=5K/min from 1623K to 1373K appeared significant stratification and the MFe gathered at the bottom of sample. With the help of metallographic microscopy and X-ray diffraction, it is found that large quantity of white RO phase gathered at the lower part of the sample as the concentrate, with volume fraction appearing gradient distribution along the direction of super gravity, while the upper part was mainly composed of dicalcium silicate as the tailing. The mass fractions of the FeO, MgO and MnO in the concentrate are up to 40.46%, 6.9% and 3.91%, while that in the tailing are just 11.65%, 2.15% and 1.55%. The recovery ratios of FeO, MgO and MnO in the concentrate are 60.35%, 58.45% and 72.24%, respectively.

Jan 1, 2016

By XUEWEN WANG, Xingming Wang, Xuehui Liu, Mingyu Wang

The Panzhihua titanium concentrate contains high contents impurity of Mg and Al, and it is difficult to prepare high grade titanium slag. To solve this problem, a sodium salt roasting-acid leaching process was proposed for removing the impurities in titanium concentrate. Na2CO3 and titanium concentrate were mixed with the proportion of 1:4, and then the mixture was roasted at 700 for 2h. After roasting, the calcine was leached with HCl solution. The experimental results showed that the removal rate of silicon and aluminum can reach more than 85% and 80%, respectively, at leaching temperature of 70 , leaching time of 4h, HCl addition of 5ml and liquid-solid ratio of 4:1.

Jan 1, 2016

By Liangju He, Peixuan Ouyang, Peijie Li

Single-pulse laser ablation of aluminum and titanium alloys under glass confinement is investigated. Processing parameters such as laser intensity and gap width between targets and glass are varied. Surface morphologies and crater profiles of the alloys after laser ablation are studied by SEM and white-light interferometric microscope, respectively. The effects of gap width and laser intensity on surface morphologies and crater profiles of targets are systematically analyzed. In addition, the generation of porous surface structures in Ti target is regarded as the result of phase explosion in the molten surface layer of targets and the thermodynamic condition in our experiment for phase explosion is evaluated.

Jan 1, 2016

By Guangliang Wu, Dongchang Huang, Xinbin Liu

Oxidation Kinetics of SPHC was analyzed by TGA, and the curve of oxidation weight gain with different temperature was acquired. It is found that, when the oxidation temperature is between 500 and 600 , all the curves are linear; when the oxidation temperature is above 700 , the curves are close to parabolic. At the temperature of 900 , the oxidation weight gain increases dramatically. The TGA results indicate that the activation energy of SPHC steel is 146.19 kJ/mol at the temperature of 500 900 , and an oxidation kinetic model was set up for variable temperature. Based on the temperature change during rolling process, numerical simulation of oxide scales evolution was carried out for SPHC steel, and the simulation result agreed well with measured ones. It can provide a basis for estimating the scale growth and controlling the temperature on site.

Jan 1, 2016

By Dariusz Kopyci ski, Józef Dorula

The study proves that by introducing the iron powder and disintegrated steel scrap to low-sulphur cast iron still before the inoculation carried out with a conventional graphitising inoculant, the mechanical properties similar to those obtained during the inoculation treatment carried out on cast iron with the recommended high sulphur content are achieved. The said operation increases the number of crystallisation nuclei for dendrites of the primary austenite. In this case, the iron particles act as substrates for the nucleation of primary austenite, due to a similar crystallographic behaviour of the regular face centred cubic lattice The more numerous are the dendrites of primary austenite, the less free space is available in the interdendritic spaces for the formation of graphite eutectic grains, which makes the structure more refined (more eutectic grains) and the mechanical properties higher.

Jan 1, 2016

By O. G. Rivera, R. D. Moser, P. G. Allison, W. R. Whittington, P. Rivera-Soto, Z. McClelland, D. Francis

This research examined the evolving microstructure of quasi-static and dynamically loaded fully annealed metastable 301 austenitic stainless steel (SS). Experiments were performed to an interrupted strain value of 20% and to failure using a tension Kolsky bar (1000/s) and an electromechanical load frame (0.001/s). Electron Backscatter Diffraction (EBSD) identified the microstructural evolution from the as-received condition to the 20% strain level for the high and low rate interrupted samples. This material achieved over 60% elongation to failure with increasing strength as strain rate increased, as expected. Fractography analysis using SEM showed particles in the microstructure and a ductile failure mode. The 301 SS exhibited a greater amount of phase transformation from parent austenite to -martensite at the dynamic strain rate when compared to the quasi-static strain rate during the interrupted experiments. This result is indicative of the increased propensity for austenite to -martensite phase transformations at the high strain rate.

Jan 1, 2016