By B. C. Allen

The solubility of chromium in liquid silver and that of molybdenum and tungsten in liquid tin have been determined by equilibrating Ike Liquid in a crucible of the solule metal. Generally the weight of solute in solulion was delermined both chemically and from crucible weight losses. The resulting weight percent solubilily of chromium in silver as a function of absolule temperature T is given by log w = -6660/T + 4.02 in the range 960° to 1445°C, and that of molybdenlttrl in tin by log w = —5050/T + 1. 79 in the range 1200° to 2200°C. The values appear unaffected by minor changes in solute composition. Calculations aye made of the parlial molar heal and excess entropy of mixing. The estimated solubility of tungsten in tin is 0.001 pct at 2000°C. Evidence is presented that molybdenwm dissolves in tin without compound for mation and that tungsten and tin form W10Sn. RECENT developments in coatings, heat transfer, and brazing require a knowledge of equilibrium solubilities in a variety of systems at elevated temperatures. Of particular interest are solid-liquid interactions in metal systems involving dilute solutions. This investigation was undertaken since little is known about the phase relations or solubility of chromium in liquid silver or of molybdenum and tungsten in liquid tin.1,2 EXPERIMENTAL WORK As indicated in Table I, high-purity metals or those of known impurity levels were used. Crucibles were machined from chromium, molybdenum, and tungsten bar stock 1.3 cm diam and 2.2 cm long. Chromium rod was prepared by arc melting and extruding iodide process crystals.3 The five chromium impurity alloys were in the form of 0.6-cm-diam swaged rod. A Cr-0.06N* alloy was prepared by exposure to NH3 at 1150°C in a closed quartz capsule for 24 hr. Because significant nitrogen was lost during annealing in argon at 1600°C,4 the estimated level was 0.01 pct N. Chromium and Mo,W crucibles were outgassed at 1200" and 1600°C, respectively, at 3 X 10-5 mm. The solvent was placed In crucibles of the solute metal- 6 g Ag in chromium, 0.4 g Ag in the five chromium impurity alloys, and 4 g Sn in Mo,W crucibles. The silver and tin series were outgassed at 900" and 110O°C, respectively, and held at the desired solution temperature in a tantalum resistance furnace under 1.05 atm 99.995 pct Ar. An equilibration time of 0.5 to 1 hr was chosen since 0.3-, I-, and 4-hr anneals at 1235°C for Cr-Ag yielded similar results. Temperatures were measured optically to +10°C under essentially black body conditions which were checked against the melting point of silver. The Cr-Ag and Mo-Sn,W-Sn series were respectively equilibrated at 990° to 1400°C and 1200" to 2000°C. Vaporization losses were generally held to <1 pct by the argon. In the 1800" and 2000°C anneals for 0.5 hr, the crucibles were placed in tightly sealed tantalum cans which kept tin losses to <5 pct. After the anneals, the specimens were furnace-cooled. One anneal was made on small Mo-0.02 C, Mo-0.5Ti-0.lZr, and tungsten crucibles containing tin at 2200°C. The metals were sealed in an electron-beam-welded tantalum can of minimum volume. After the anneal, tin was still present in each crucible, none of which was severely attacked. After equilibration, the saturated solvent metal was selectively removed from the crucible by acid leaching. Weight losses sustained by the crucibles were determined from the initial weight minus the final blank-corrected weight after acid leaching. Chemical analyses were performed on some of the samples. Hot 1:l HNO3-H2O removed silver from chromium with the blank running <0.1 mg or <0.002 pct on measured solubility. Tin was removed from molybdenum and tungsten by hot concentrated HC1 with the respective blanks amounting to -0.004 and -0.0004 pct in the presence of tin. The insoluble residues were weighed and checked for composition. The leaching solutions contained traces of the solute metals which were analyzed by colorimetric methods, Diphenyl Carbazide for chromium, Thiocyanate for molybdenum, and Dithiol for tungsten. The total of the two percentages found from the residue and leaching solution minus the blank gave the desired solubility values. On the basis of annealing empty molybdenum and tungsten crucibles, weight losses due to MoO3 or WO3 volatilization were found to be generally 10.4 mg and affect measured solubilities by <0.01pct. RESULTS AND DISCUSSION Chromium-Silver . Since no intermediate compounds are reported to form in the Cr-An system,&apos; crucible weight losses and chemical analysis of the entire melt should provide reliable measures of the chromium in solution. Values obtained by the two methods are in agreement as shown by the results for unalloyed chromium in Table II and plotted in Fig. 1. Furthermore, the results are consistent with those previously determined by melting equilibrated silver out of the crucible and analyzing calorimetrically for chromium.&apos; On the basis of limited thermal analysis data, the solubility of chromium in silver has been quoted as 8 pct at the monotectic temperature of -1445°C.1 This investigation indicates an extrapolated solubility of 1.38 pct which is believed to be more reliable. At the eu-

Jan 1, 1968

By Mark D. Tabak

Measurments of the transient photoconductivity in fillns of amorphous selenium with blocking- contacts haue been used in studying the transport properties. The results shozu that the transport of free carviers cannot be explained in terms of a model using bulk trapping. Measurments of the photocurrent-applied field characteristic as a unction of sample thickness do not pvoduce the scaling lau,s approps-iate lo a range-limited model. THE investigation described here was undertaken to explore the mechanisms of transport in amorphous selenium films. These films are used in xerography, where a photoconductor is charged electrostatically and then exposed to light to form a latent image. The sensitivity that one can expect when operating in this mode is directly related to the transport properties of the photoconductor material. The study of photoconductivity at high fields in insulating materials is often complicated by contact effects. Injection from the contacts can easily mask the fundamental transport processes that are being studied. A technique is described in this paper that allows a study of photoconductivity and transport processes in amorphous selenium films without the complicating effects introduced by contacts. Accordingly, the samples are prepared using insulating films between the sample and the metal electrodes, where the electrodes are capacitively coupled to the surfaces of the sample under study. A transient measurement is performed with pulsed light, and the photocurrent measured near the beginning of the pulse before the field is distorted by polarization at the blocking elec- trodes. A similar method has been described by Manyl using pulsed electric fields in studying the high field transport in insulating cadmium sulfide. EXPERIMENTAL It is possible to eliminate undesirable contact effects and maintain uniform high fields across the sample by using blocking electrodes and measuring the current-field characteristic under transient conditions. The sample configuration is shown schematically in Fig. 1. Each of the gold electrodes is separated from the amorphous selenium film by a layer of insulating plastic (Formvar) approximately 2000~ thick. The electrode on the front surface is semi-transparent to allow illumination of the sample. The whole configuration is mounted on a KEL-F substrate, which is a transparent insulating plastic having a thermal expansion coefficient that allows low-temperature measurements without cracking the selenium film. Fig. 2 shows a block diagram of the measurement apparatus. Light was obtained from a 450-w Xenon arc lamp, the intensity of which was controlled by stainless-steel screen filters and monitored by a pho-tomultiplier which was calibrated periodically against a thermopile. A camera shutter operated at 1/200 sec provided the light pulse and a synchronized signal to the oscilloscope. The photocurrent transient is ob-served with a high-speed picoammeter (response time of 1 msec) the output of which is displayed on an oscilloscope. The applied voltage is constant throughout the transient measurement. The selenium films were prepared by evaporation of four 9&apos;s pure selenium shot supplied by Canadian Copper Refiners. Spectrographic analysis showed about 1 ppm of Te and Fe, 5 ppm of C1, and 0.05 ppm

Jan 1, 1968

By Donald F. Hammer, Donald W. Peterson

The Magma mine at Superior, Arizona, has produced over 13 million tons of ore yielding 1.5 billion pounds of copper. It is a mesathermal deposit, and, although the bulk of the ore has come from the Magma vein, most of the recent production has come from replacement deposits in limestone. The mine lies in a Precambrian and Paleozoic sequence of rocks that includes schist, diabase, quartzite, shale, and limestone; nearby, these rocks are intruded by igneous bodies of Mesozoic age that were probably the source of the ore-bearing fluids. Locally, these rocks are overlain by Cenozoic volcanic rocks and conglomerate. Layered rocks at the mine dip eastward about 30°. The area is extensively faulted, and surface faults are grouped into an earlier east-trending set and a later northtrending set. An additional set of diagonal faults that trends northwest and northeast is recognized underground. The east-trending Magma vein-fault, with its splits and branches, is the principal mineralized structure of the district. The bulk of the ore occurs in large ore shoots that plunge steeply westward and are sporadically connected by irregular ore shoots dipping gently eastward. The main ore controls apparently are selective zones of permeability related to the transverse faults. A bed of crystalline limestone near the base of the Martin Limestone (Devonian) is the host for the replacement ore bodies-discontinuous tabular pods dipping eastward parallel to the bedding. Selective permeability is again the apparent ore control, caused both by local hydrothermal solution of limestone and by deformation along faults. The principal copper minerals in the vein are chalcopyrite, bornite, enargite, tennantite, chalcocite, and digenite; these minerals vary in abundance according to a distinct zoning pattern. The upper part of the mine yielded considerable zinc as sphalerite, and the oxidized zone was rich in silver. The chief gangue minerals are pyrite, quartz, and hematite. In the limestone replacement bodies, chalcopyrite and bornite are the chief ore minerals.

Jan 1, 1968

By V. Kondic, W. M. Rumball

HUNT and Jackson&apos; have recently suggested that binary eutectics might be classified according to the entropy of fusion of the component phases. Such a classification was in fact proposed2 some time ago by the authors and the purpose of this communication is to present some supporting evidence. As pointed out by Hunt and Jackson&apos; typical metals of low entropy of fusion, ?S, tend to form normal eutectics (using Scheil&apos;s terminology3). Where one phase is metallic (low ?S) and the other nonmetallic (high AS) then anomalous structures are formed. These anomalous structures may either be regular (e.g., Bi-Sn)or irregular (e.g., A1-Si). Finally Hunt and Jackson suggest that where both phases are of high ?S regular faceted structures are formed. In the proposed classification2 the ratio of the entropies of fusion is taken as the quantitative parameter, i.e., ?Sa/?SB = E, where e > 1.0. An extensive literature survey has been carried out2,4 for reliable photomicrographs of eutectic structures. The structures, numbering 151, have been classified into two classes, viz., normal (i.e., lamellar and rodlike) and anomalous. The latter group has been arbitrarily subdivided into regular and irregular anomalous eutectics. Details and sources of the structures are given elsewhere.2,4 In the absence of better thermodynamic data the value of E has been determined for each of the systems making the following assumptions and approximations: l) The entropy of fusion of solid solutions may be calculated additively;5 ii) Inter metallic compounds are treated similarly but with the addition of the following term for fully ordered structures.5 -4.573(Ni lOg10 Nl + N2 log10 N2) where Nl and N2 are the atomic fractions. It might be argued that the entropies of fusion are meaningless as the eutectic phases form at some temperature (T,°K) below their true melting point (Ta or Tb). As AS, = Lo/To if La the latent heat of fusion of a, is assumed independent of temperature, the actual entropy change AS& is given by La/Te. The ratio of entropies of fusion then becomes Fig. 1 shows E&apos; plotted against cumulative totals for normal and anomalous systems from which it is seen that normal eutectics predominate at low values of E&apos;; e.g., some 90 pct of normal systems lie below E&apos; = 1.5 with 65 pct of anomalous systems above this value. Fig. 1 also shows that the regular anomalous structures occur mostly at low values of c&apos; possibly suggesting growth more akin to normal than anomalous growth. The choice of c as a classification parameter was based on nucleation concepts, it being observed that metals widely separated in Sundquist and Mondolfo&apos;s8 nucleation series were anomalous and those close together normal. The basis of these classification views is really outside the intended scope of this communication but it is hoped to explain them fully in the near future.7 Having arrived at this entropy of fusion classification by nucleation considerations it is interesting to note that Hunt and Jackson&apos;s ideas are based on growth considerations. Elsewhere one of the authors4 has shown that an even better classification of the metallographic structures reviewed is obtained from purely conventional heterogeneous nucleation concepts. It has been found that systems having a value of the parameter +b less than 0.28 are almost certainly normal and above this anomalous: V, is the gram atomic volume. This parameter is nevertheless closely related to c and c&apos;, these being an approximation of p. The parameter is also related to the other classification3,8,9 which have met with any success in the past. All these classifications are to be reviewed shortly by the authorsU7 A significant thing about the classifications based on

Jan 1, 1968

By John Chipman, Raymond L. Orr

Recently reported high -temperatlnre thermal data have been incorporated in a reuieu&apos; of the therinody-r~ar,zic propesties of iron. The recent data permit mot corlsisterlt and reliuble choices to be made for many of the pvoperties, resnlling in bettev eslablished tabrtlations of the thermodynamic functions. Values of Cp, h°t- - H°298. s°t - S2sa, and (G°T -H298/T are tabulated for -the solid and liquid phases of iron in both stable and melastable regions. Consistency of the tabulations has been maintained to the precision necessr~vg to yield the Gibbs energy change belween the bcc (a, 8) and fcc (y) phases of iron at temperatures pertinenl to alloy studies. THE importance of the metal iron has stimulated many investigations of its thermodynamic properties at elevated temperatures. Reviews and summaries of the data have appeared from time to time. Among these the 1951 paper of Darken and smith&apos; deserves highest recognition for the quality of its criticism and for the precision and thermodynamic consistency of its tabulations. These and the more recent table of Kaufman, Clougherty, and weiss2 reproduce the Gibbs energy of the (a, 6)--Y transformation with sufficient sensitivity for alloy studies. Other recent compilations of equal validity3-&apos; make no attempt to do this. Since this Gibbs energy change is not greater than 22 cal per g-atom over the temperature range 1100° to 1800°K, it is obviously desirable to tabulate values of (G°t - H298)/T to four places of decimals even though the absolute accuracy would not warrant such precision. The necessity for reconsideration of the problem is emphasized by the recent publication of several important researches on the enthalpy and heat capacity of iron. The older work is well-covered in the reviews cited and will be mentioned here only when actually employed in the tabulations. GAMMA IRON Transition temperatures are taken from the selec -tions of Elliott and Gleiser,5 based on the work of Boulanger7 and earlier workers. For the a-y (A3) transition at 1184°K we retain the value 215 cal per g-atom adopted by Darken and smith.&apos; It has received confirmation in the recent work of Dench and Kubaschewski,&apos; and of Braun8 using adiabatic calori-metry, and of Wallace, Sidles, and Danielson10 using a pulse heating technique. The enthalpy data of Olette and ferrier" and of Anderson and Hultgren12 at higher and lower temperatures may be extended to 1184°K to give the following values which are adjusted to the required value of ? 1184 Ha,1184 Ha 298 = 8030 cal per g-atom [11 hr,1184-ha298 = 8245 cal per g-atom [2]

Jan 1, 1968

By Gordon B. Brox, Joseph F. Mcaleer, Charles C. Goddard, Edward P. Shea, Robert G. Ingersoll, Lester G. Zeihen, George J. Burns, John M. Guilbert, Richard N. Miller, Charles Meyer

The Boulder batholith is a composite intrusive in which the Butte quartz monzonite is the dominant rock type. Quartz porphyry dikes intruded the quartz monzonite in directions which were subsequently followed by the eastwest- striking Anaconda system of veins, the earliest major veins in the district. Anaconda veins are faulted by northwest-striking veins of the Blue system, which are most prominent in the central third of the district. Anaconda veins are the major producers in the western third of the district and also in the eastern third, where the "horsetail" zones break off from them. Individual oreshoots are thousands of feet long as well as deep on both systems of veins, but they are generally more persistent and thicker on the Anaconda veins. Viewed broadly, the mineralization in the big veins is arranged in crudely concentric zones of zinc and manganese around a central zone of copper. Only slightly offset from these zones, but earlier structurally, is a zone in which quartz-molybdenite veinlets are prominent. This zone tops at about the 2800 level and widens downward. The pattern of distribution of Cu-Fe-S series minerals in the large veins of the copper zone is not symmetrical with respect to the metal zones. There is a fringe of chalcopyrite-bornite all around the copper front. However, within the copper zone, pyrite-chalcocite-enargitecovellite- digenite assemblages are prevalent near its eastern edge from the 3800 level to the surface, whereas deep on the large Anaconda veins in the western part of the copper zone, chalcopyrite is dominant. Here the chalcopyrite grades upward into bornite-chalcocite ores and eastward into the high-sulfur assemblages of the Leonard mine. Sericite-biotite-K-feldspar alteration envelopes, containing up to about 2 per cent copper as chalcopyrite, are present on some of the quartz-molybdenite veinlets at deep mine levels in the molybdenite zone. These envelopes contrast sharply mineralogically and chemically with the later sericitic and argillic alteration envelopes around Main Stage veins. K'0-Ar'0 ratios indicate that they may be older by about 4 m.y. Secondarily enriched copper ores are mined in the Berkeley pit in the southeastern part of the district. At the present time they account for about half of Butte's production of copper.

Jan 1, 1968

By T. R. Young, S. A. Scott

9.5-1. Introduction. The use of pipelines to transport solids has been successfully accomplished with many different materials. One of the oldest applications is the dredging and placing of hydraulic fill. Many installations have been made and operated for long periods of time with excellent dependability, low operating cost, and low maintenance. It is not the aim of this chapter to give the engineer the answers from which to design a pipeline, but rather to supply helpful information from which to start the project. There are several phases of solids pipelining which as yet have not lent themselves to quick engineering answers. Investigations have been carried on by many, with several theories advanced by the various investigators. In recent years certain notable theoretical advances in hydraulic transportation have been achieved. Vertical transport, using balanced "leg" operation, now appears competitive with other forms of vertical transportation. In addition, horizontal transport utilizing capsules has been proven experimentally to be attractive because of lower pressure drop than the conventional methods of solid transport in fluid media. With the aid of the computer, the laborious calculations associated with pumping calculations have been greatly simplified; and with this tool the pipeline engineers of the future will undoubtedly be able to develop a more comprehensive understanding of solids-fluid transport. 9.5-2. Theory. There have been many excellent studies made and information is available in the literature, but a general comprehensive theory of pipeline transportation of solids has not been advanced. The existing flow theories will give approximations for minimum and optimum flow velocities, friction head losses, energy requirements, and pump and pipe size The principles of dynamic similarity and scaling laws are well understood for the flow of pure liquids. There are no firm methods of scaling slurry pipelines of small diameter to larger diameters except for a few empirical.

Jan 1, 1968

By Richard W. Bayley

The Atlantic City district encompasses several districts and has been previously called by different names, e.g., Atlantic gold district, Atlantic City-South Pass mining district, and Sweetwater mining district. The district is located in a terrane of folded and faulted early Precambrian metamorphic rocks which lies near the south end of the Wind River Range in Fremont County, Wyoming, Historically it is a gold district of little production, but today is an iron district of considerable importance. Gold was discovered in placer deposits about 1842 and in quartz-arsenopyrite veins about 1867, after which there occurred a mining boom lasting a few years. Minor, intermittent gold production from placers and lodes has continued to date, but the total production has probably not exceeded a few millions of dollars. Past lode mining was generally shallow ( in the oxidized zone), the deepest about 3 60 feet. The deeper, less oxidized and sulfide ores on the same lodes have not been explored. They appear to hold the only hope for future gold mining. Sedimentary iron-formation, similar to the Lake Superior taconite, occurs in the northern part of the district. Locally, where the ironformation is thickened by folds and faults, sufficient tonnages are present to be minable, as at Iron Mountain, where the U.S. Steel Corporation produces about 1.3 million tons of iron-ore pellets annually. Exploration of the iron deposits began in 1954, and the first ironore pellets were shipped to Provo, Utah in August 1962. Indicated reserves of iron-formation (about 30 per cent Fe) are reported to be about 300 million tons.

Jan 1, 1968

By Manning W. Cox

Van Stone mine area is situated at the head of Onion Creek on the northwest flank of Gillette Mountain, Stevens County, Washington. The di strict was found during World War I, but the mine did not come into production until 1952. Production to the end of 1965 was 2,242,960 tons of ore that yielded 10,700 tons of lead concentrates and 120,000 tons of zinc concentrates. The area is part of the Selkirk Mountains Zinc-Lead Belt, or Kootenay Arc, extending from near Revelstoke, British Columbia, to Colville, Washington. A thick but incomplete section of Paleozoic marine formations occurs in the Kootenay Arc and is overlain by marine and continental Mesozoic formations. Both are invaded by Late Mesozoic-Tertiary batholiths. The belt is characterized by open complex folding and extensive high-angle and local thrust faulting. Principal ore deposits occur in the highly deformed carbonate rocks of Cambrian age-the Maitlen (Laib) and Metaline formations. The Van Stone mine occurs along a steeply S-shaped fold lying between the Kaniksu Batholith on the west and the Rogers Mountain Fault, a northeast-trending fault on the west flank of the Gillette Mountain Anticline, to the southeast. The fold is cut by northeasttrending faults containing notoriously irregular lamprophyric, diabasic, and pebble dikes. The host rocks, lower Paleozoic dolomites, are decolorized, silicified, and silicated in the mine area. Jasperoid and tremolite are the common alteration minerals. Other gangue minerals are barite, pyrite, brucite, calcite, and, near the batholith, pyrrhotite. Ore minerals are galena, jamesonite, and sphalerite. Ore minerals occur in bunches and pods intergrown with tremolite and jasperoid. Zinc is roughly eight times more abundant than lead. The highest ore outcrops at 3870 feet elevation, and an undeterminable portion has been removed by glacial scour. The lowest drill hole penetration has reached 3220 feet elevation. Oxidation ranges up to several hundred feet in depth and may be most closely related to pre-glacial groundwater circulation. The area of the mine was completely over-ridden by Pleistocene continental glaciers, and the present erosion surface is nearly continuously blanketed by up to 150 feet of glacial outwash.

Jan 1, 1968

By S. G. Epstein

Using the capillary-reservoir technique, electromi-gvation rates of cadmium and indium in liquid bismuth were measured at several temperatures. The electric mobility of cadmium Jrom 305° to 535°C and indium from 310° to 595°C can be expressed as a function of temperature by the equations UIn = 1.52 x 10-3 exp sq caz per v-sec Migraion of both solutes was cathode-divected at a rate rnore than four tiMes tHAt previously found for siluer in liquid bisnmth. The electric mobilities of cadmium and indiulrz in liquid bismuth at 500° C are nearly identical with their respective mobilities in mercury at room temperature. AS part of a systematic study of the variables which are considered to control electromigration in liquid metals, the electromigration rates of cadmium and indium in liquid bismuth have been measured. Mass transport properties of silver in liquid bismuth have been reported previously,&apos; and measurements of tin and antimony in liquid bismuth are forthcoming. Comparisons will be made with literature values for these same solutes in mercury.2&apos;3 This series of solutes was selected to determine the effect of the solute valence on its electromigration. Silver, cadmium, indium, tin, and antimony have nearly equal atomic masses but have chemical valences ranging from +1 to +5. They are all fairly soluble in bismuth above 300°C and all have radioactive isotopes, which are an aid in making analyses. EXPERIMENTAL TECHNIQUE Electromigration of cadmium and indium in liquid bismuth was measured by the modified capillary-reservoir technique previously described.&apos; In this method irradiated cadmium or indium is added to bismuth to form alloys containing about 1 wt pct solute (<2 at. pct solute). Several quartz or Pyrex capillaries: 1 mm ID and 5 cm long, vertically oriented, are simultaneously filled in the reservoir of the liquid alloy. A direct current is passed through two of the capillaries, which contain tungsten electrodes sealed in the upper end. The other capillaries sample the reservoir during the experiment. After a measured time interval the capillaries are removed from the reservoir and rapidly cooled. The glass is then broken away from the solidi- fied alloy, which is then weighed, dissolved in acid, and analyzed for solute content by chemical and radiochem-ical techniques. An electric mobility (velocity per unit field) can be calculated from the amount of solute entering or leaving each capillary by the simplified expression1 in which Ui is the electric mobility of the solute, ?mi the solute weight change, Ci the solute concentration of the reservoir, I the current, p the alloy resistivity, and l the duration of the experiment. This expression is valid as long as the experiment is terminated before a concentration gradient develops across the capillary orifice. Earlier experiments showed that the concentration gradient formed initially at the electrode changes with time and eventually reaches the orifice, due to back-diffusion. This condition produces a solute exchange between capillary and reservoir by diffusion or convection, opposing the electromigration, which results in a lower measured value for the electric mobility. To determine if the concentration gradient had reached the orifice, the capillaries used in some of the experiments were sectioned at 1-cm intervals and the solute content of the alloy from each section was radiochemically determined. A typical concentration profile for an experiment with indium in bismuth is shown in Fig. 1; cadmium in bismuth showed similar behavior. As illustrated in the graph, very little back-diffusion has occurred in the capillary containing the cathode, since the concentration gradient is confined to the upper 1 cm of the capillary. In the capillary containing the anode, however, the concentration gradient is much broader, extending nearly to the orifice, even though the net change in solute concentration is nearlv the same in both capillaries. Since cadmium and indium probably lower the density of bismuth when alloyed, depletion of the solute from the alloy adjacent to the anode would increase the density of the liquid in the uppermost region of the capillary. This would give rise to convective mixing within the capillary, causing the broadened concentration gradient. Conversely, the alloy adjacent to the cathode should have a reduced density as the solute concentration is increased by migration, explaining the "normal" concentration profiles found in these capillaries. This disparity was not found for electromigration of silver in bismuth. Both metals have similar densities at the operating temperatures, and nearly symmetrical concentration profiles were found in the two capillaries of each exueriment. This density effect was also apparently encountered when an attempt was made to measure diffusion coefficients for indium in liquid bismuth by the same technique which was successfully used to measure diffusion of silver in bismuth.&apos; Capillaries 1 mm ID and 2 cm

Jan 1, 1968

By R. T. Moolick, John E. Neill, O&apos

In selecting a particular stripping method the ultimate aim is the removal of material at the least possible cost. Accomplishment of this goal requires the careful consideration of many factors including geologic and topographic information, proximity of the stripping operation to waste disposal areas, possible problems of land reclamation, types of suitable equipment available, and auxiliary equipment requirements. 4.2-1. Selection of Stripping Methods. The size of an orebody and the distribution of values within that orebody normally will limit the variety of economical stripping methods which need to be considered. Much may depend upon the selectivity required in the mining due to the relationship between ore and overburden, as well as the character of the overburden itself. The following factors concerning the geologic nature and environment of an orebody, as well as the production requirements, must be determined before any selection of equipment is made: 1. The size of the orebody and distribution of the values within that orebody. Is the ore massive or scattered, bedded or disseminated, thick or thin? 2. The nature of the overburden to be removed. Is it a hard dense rock, bedded rock (thick or thin), friable material, earth, sand, elay, marsh, etc.? 3. The character and significance of geologic structures (fractures, faults, shear zones, etc.) associated with the ore occurrence. Are there water bearing formations with resulting water disposal problems? 4. In considering the nature of the overburden, including its alteration products, the physical or chemical conditions which, when combined with anticipated climatic conditions, may render certain equipment inoperable during unfavorable seasons.

Jan 1, 1968

By E. N. Aqua, C. M. Owens

The microstructure in cold-rolled Zircaloy-4 sheet has been characterized by transmission electron microscopy and X-ray diffraction line-broadening techniques. The rate of work hardening is measured in terms of microstrains, particle sizes, micro hardness, the tensile yield strength. The tensile yield strength of Prestrained (less than 10 pet) Zircaloy-4 sheet is found to be a linear function of the square root of the dislocation density, us predicted by work-hardening theories. ZIRCALOY is one of the most important structural alloys for nuclear reactor applications.&apos;&apos;2 In order to understand the effects of the nuclear environment on Zircaloy structural members, the preirradiation microstructure must be characterized. This report will describe the substructure existing in cold-rolled Zircaloy-4 sheet as observed by electron microscopy and by X-ray diffractometry. I) EXPERIMENTAL PROCEDURE Commercial Zircaloy-4 strip was cold-rolled and annealed in argon at 760°C for 1 hr. The annealed sheet was again cold-rolled to a maximum of 50 pct reduction in thickness with segments of the strip being retained after 2.5, 5, 10, and 20 pct reductions. One-inch-square portions were chemically polished (50 parts HNO3, 50 parts H2O, 10 parts HF) and mounted onto lucite blocks using double-sided tape to prevent bending during handling. Thin foils suitable for transmission electron microscopy were prepared from each of the sheet samples. The sheets were mechanically polished through 600-grit paper to a 3 to 4 mil thickness and were chemically polished by immersion for 1 to 2 min in a solution containing: 50 parts HNO3, 50 parts H2O, and 10 parts HF, and rinsed in distilled water. The final metallographic procedure was to electropolish for less than 10 sec with an electrolyte of 10 parts perchloric acid and 90 parts glacial acetic acid, at 20 v, at room temperature using stainless-steel point cathodes and a vigorous stirring action. These foils were examined in a Philips EM 200 electron microscope using a 100-kv accelerating voltage.

Jan 1, 1968

By Burt Hartmann

The nation&apos;s ever-expanding construction and mining activity has placed an increasing demand upon engineers and geologists to design and construct stable slopes in earth materials-soil and rock. Man&apos;s attempt to handle these slope stability problems has been based primarily on practical experience and the resulting theories formulated to explain the phenomena. Too many instances occur when man is faced with a slope stability problem that has not yet been experienced and doesn&apos;t lend itself to solution by any existing theory. At this point he must extend himself in using his engineering judgment to arrive at a reasonable and safe design. As past experience has shown, all of the "safe designs" are not really safe. Sometimes they result in embarrassing failures. Measurements provide the key to understanding and controlling natural phenomena. We cannot hope to gain control of the slope stability problem until we understand the causes of slope failure, their behavior with respect to time and their relative magnitudes. Measurements required for an adequate definition of any slope problem must be of the highest reliability because of the importance of decisions which must be based on them. For this reason, direct measurements of movement, shear strength, water pressure, etc. of the unstable mass are preferable to indirect measurements of other physical properties. Movement instruments which can be positioned inside of the slope mass (within boreholes) are among the most useful in diagnosis and/or monitoring of slope movements. The higher the sensitivity and il-measurement precision possible with borehole instruments, the quicker the required information can be obtained and the more exactly may hazardous conditions be observed. A high density of measuring points in a single drill hole is deemed essential for diagnostic purposes. Behavior gradients may thus be obtained. The Pressure Meter (Fig. 1) can be used to measure a relative strength

Jan 1, 1968

By T. E. Scott, R. P. Zerwekh

The charactevistics of the deformatiotz of fcc thorium were examined between 78 and 473 K. Activation energy, actiuation volume, and the temperature dependence of the flow stress were determined and conlpared uith several theories for the rate-controlling mechnnistn of the tempemture-dependent component of the flou~ stress. It was established that the Cottrell-Stokes law does not hold, even approximately, for thorium. Through consideration of the above factors and other parameters, it was concluded that the vandom solute barrier theory proposed by Friedel demonstrates the best agreement with experimental observations of the deformation of thorium below ambient temperature. THORIUM, the first metal in the actinide series of rare-earth elements, is interesting and important from two points of view. In the more practical vein, it is a potential reactor fuel. As such, it is important to know its properties. Of specific interest here are the mechanical properties of thorium. Second, no detailed information concerning the deformation characteristics of the actinide elements has been gathered to date. In view of the interesting physical and chemical properties of these metals, their mechanical behavior might reveal characteristics which could improve our understanding of the mechanisms controlling deformation of the more common metals. For example, it has been shown1 that thorium exhibits a yield point which is greatly enhanced by interstitial solute elements such as carbon. This is not a normal occurrence in fcc metals. The goal of this investigation, therefore, was to characterize the deformation of polycrystalline thorium. MATERIAL AND PROCEDURES Thorium, made by the magnesium intermediate alloy process described by Peterson et al.,2 was rolled and swaged to 0.065-in.-diam wire. The metal analysis is given in Table I. After preparation, the oxygen and nitrogen contents had risen to 308 and 60 ppm, respectively. The 0.065-in.-diam wires were cut into 2-in. lengths and annealed in a vacuum of lo-&apos; Torr at 750°C for 1 hr, producing a grain size of 2735 grains per sq mm. The ends of the 2-in. sections were masked off so that a 1-in. gage length could be electropolished. Specimens were polished at 35 v in a solution of 6 pct perchloric acid in methanol which was maintained at 0°C . The gage diameters after polishing were about 0.0625 in. The tests were run on a screw-driven tensile machine at a constant crosshead speed corresponding to a strain rate of 0.005 min-&apos;. The strain rate was changed rapidly after each 0.01-in. extension between 0.005 min-&apos; and one of three higher strain rates which were selected in order to achieve strain-rate ratios of 5, 10, and 20. Tests were run at several temperatures from 78" to 473°K; most were tested at 423", 300°, 215", and 78°K. EXPERIMENTAL RESULTS Flow Stress vs Strain and Temperature. Typical true stress-true strain curves for thorium are shown in Fig. 1 for several temperatures over the range 473" to 78°K. The curves for 78", 215", 300") and 423°K were obtained from strain-rate change tests using the lower (0.005 min-&apos;) or base strain-rate values of stress. Additional tests, using the same base strain rate at different strain-rate ratios, gave curves which virtually superposed on those shown, indicating that strain-rate changes did not materially influence the work-hardening characteristics at the base strain rate. The curves for 273") 373") and 473°K were standard tensile tests at 0.005 min-&apos;. The behavior of the flow stress with temperature is

Jan 1, 1968

By Joseph M. Jacisin

Fatigue tests were conducted on 2017-T4 alumium in alloy in an u1lrcthig.h vacuum of 2 x 10-lo Torr and in air. The vatio of vacuum-to-air faligue life for this ~malerial varied Jrom 3.5:1 at a strain of 2.5 X 1O-3 ill. pegr in. to 8:l at a strum of 3.3 x X ill. per 171. Sotlze pvelivtlinary data were also obtained on the faligue life of the alumirnum alloy in a dvy-nitrogen atmosphere. A dark deposit observed on the fracture surfaces of the aiv-tested specimens was identified as oxides of tr~angarzese and magnesium This observalion, and the close correlalion betaveen results obtained in vaCuum and dry-nitrogen environtments, tend to confirm that air stvongly influences the fatigue mechanism by a covrosion process. THE fatigue life of certain metals is known to increase when the atmospheric pressure is reduced. Gough and Sopwith1-2 postulated that this is due to a joint chemical and mechanical process operating in air at the surface of the metal with oxygen and water vapor playing significant roles. Wadsworth and Hutchings3 observed that aluminum is mainly affected by the presence of water vapor. Very little information is available on the fatigue properties of structural aluminum alloys in a vacuum environment. This report describes work performed on 2017-T4 aluminum alloy in an ultrahigh vacuum (2 x 10-loTorr) and in air. Some preliminary data are also presented on the fatigue life of the alloy in a dry-nitrogen environment. 1) EXPERIMENT 1.1) Test Material. The material tested was commerciaT 2017-T4 aluminum alloy which, in addition to aluminum, has an approximate composition of 4 pct Cu, 1 pct Fe, 0.8 pct Si, 0.5 pct Mg, 0.5 pct Mn, plus smaller amounts of other elements.* Some typical naturally age to a substantially stable condition. Specimens were then machined from these rods and ground to a No. 8 microfinish. In order to minimize variation in material characteristics, specimens were made from rods procured from the same lot. 1.2) Apparatus. The apparatus and test specimen used in the fatigue tests are shown in Fig. 1. The device utilized a single-cantilever beam with rotating-bending loading. Bending stress was applied to the fatigue test specimen by placing a spacer beneath the bearing support, thereby providing a constant deflec-

Jan 1, 1968

By J. W. Leomrd, B. A. Donahue

Results of research are presented examining the extent to which the analytical characteristics of the relatively distinct coal bands from a variety of coal seams can be related to each other. This paper dis-cusses an approach for developing a practical coal petrographic quality control program based on conventional analyses, most of which is part of the standard A.S.T.M. procedure. The work is a final follow-up to Part I of this series which was prepared by the authors as an approach to applying conventional coal petrography to single coal seams. Recent published work by the authors entitled Petrography for Coal Mining and Coal Prepration: Part I dealt with interrelating various chemical and physical properties of coal1 measured using conventional analyses made on distinct petrographic bands taken from single coal seams. Since most coal production facilities process coal from a single coal seam or from very closely related coal seams in the same area,2 emphasis on interrelating the properties within a single seam appeared appropriate. The distinct petrographic bands were analyzed on the assumption that such differentiated data would be more representative of a heterogeneous coal seam than the single analytical value commonly used to characterize each property of an entire seam.34 Effort was directed at demonstrating the extent to which the interrelated chemical and physical properties 5,6 could be developed into nomographs or petrographic standardization graphs. Thus, one analysis, determined on a series of petrographic fractions separated from a single sample, was used to estimate numerous other properties in each fraction by referring to the previously established petrographic standardization graphs. This conventional approach to coal petrography was undertaken as a suggested feasible means by which a few coal analyses could be employed to develope a more penetrating knowledge of the properties of coal from any given seam in order to monitor more extensively its performance at the point of utilization. Such procedures can support development of the type of in- formation commonly sought through automated testing and through the use of computers.7 The broad knowledge which can be developed through these procedures is intended for application in the generation of an analytical profile or broad characterization of coal. These estimates were not intended as replacements for individual coal analytical tests. In this expanded second part of the research program, distinct petrographic bands from nine coal seams in the Central Appalachian Region were physically and chemically analyzed to elucidate the extent to which this concept of conventional petrography could be broadened for application to numerous coal seams. In presenting this second phase of work, the relationships developed are presented individually and not in a connecting series of nomographs or petrographic standardization graphs as in the previous work, thus leaving open the combinations of possibilities to individual interpretation and application. MATERIAL AND EXPERIMENTAL WORK Nine coal seams, representing a wide range of rank, from the Central Appalachian coal fields were used in this study. The distinct petrographic bands from the Kittanning, Pond Creek, Jawbone, Tiller, Poca-hontas No. 3, No. 2 Gas, Eagle, Winifrede, and Pittsburgh coal seams were separated by carefully removing a portion of each band at the face of the seam. The following were determined: ash, sulfur, free swelling index, heating value, bulk specific gravity, volatile matter, Hardgrove Grindability Index, and Gieseler Plastometer measurements. Determinations, where procedures were available, were carried out using ASTM standard procedures.8 Bulk specific gravity was determined using a kerosene volume displacement procedure modified from a method applied by Headlee and McClelland of the West Virginia Geological survey,9 Those bands with a bulk specific gravity greater than 1.60, which is generally above the practical specific gravity cleaning range of bituminous coals, were excluded and no analyses were performed. Much of the initial organization of this second phase of work was developed through the extensive use of a computerized statistical monitoring program (see Ref. 4). However, in order to achieve the closest possible interpretation of results, the final organization of data proceeded mainly from exhaustive trial

Jan 1, 1968

Jan 1, 1968

By J. Warner, M. J. Marcinkowski, B. Cullen, T. Prevender, J. Mcllwain, T. Carnahan, J. Pahlman, J. Demel, J. Munford

The following analysis was an outgrowth of a midterm examination given by one of the authors (M.J.M) in a course entitled Metallurgy 541 "Applications of Dislocation Theory&apos;&apos; at Iowa State University. Fig, l(a) shows the three-layer sequence of atoms lying in the (111) plane which characterizes the fully ordered AB3 fcc crystal, i.e., LI2 type. If any two-layer sequence of close-packed planes is constructed from Fig. 16)&apos; the structure would be hcp of the DO,, type. Consider for convenience that the circled atoms lie in the plane of the drawing while those shown square and triangular lie immediately above and below the plane of the drawing, respectively. It has already been shown&apos; that if a Shockley partial dislocation is passed over the plane of the paper, then the square atoms in Fig. 1(a) are displaced from their original positions as shown by the arrows in Fig. l(b). Not only is an intrinsic fault produced but the crystal is simultaneously disordered across the slip plane. In particular, 2AB bonds are converted to 1AA and 1BB bonds when referred to the area outlined by the solid line in Fig. 1. If, on the other hand, a Shockley partial is allowed to pass immediately above and immediately below the plane of the paper so as to displace the atoms in opposite directions as shown in Fig. l(c), an extrinsic fault is producedZ and twice the amount of disorder is introduced into the crystal as compared to the dislocation-produced intrinsic fault, if only broken first-neighbor bonds are counted. If an intrinsic stacking fault is produced by removing a close-packed plane of atoms in Fig. l(a) and displacing the two adjacent planes by 1/3a0[111], no wrong nearest-neighbor bonds are produced. Similarly, if an extra half plane of atoms with the same arrangement as any of those shown in Fig. l(a) is inserted between any two planes in the same figure, then an extrinsic stacking fault is produced in which once again no wrong nearest-neighbor bonds are produced. The latter two faults are bounded by Frank partial dislocations. Since, at least in the alloy CU3AU,3 nearly all of the ordering energy resides in the first nearest-neighbor interactions, intrinsic and extrinsic stacking faults and associated APB&apos;s of the Frank type are expected to have significantly lower energy than those of the Shockley type in CusAu in particular and quite likely in L1, and DO19 type alloys in general. Also, because of the higher degree of disorder plus loop interaction

Jan 1, 1968

By J. E. Hanlon, S. R. Butler, R. J. Wasilewski

It is known that stoichiometric NiTi transforms to a structure of lower symmetry near room temperature. The present investigation deals primarily with the changes in the electrical and magnetic properties which occur at the transformation. The effects of composition and various heat treatments on electrical properties are also discussed. In recent investigations by Purdy and Parr,&apos; Wang et a1.,2 Dautovich and Purdy,~ Dautovich et a1.,4 and the authors, ~,&apos; NiTi has been observed to undergo a martensitic phase transformation from the ordered CsCl (B2) structure to one of lower symmetry. The crystal structure of the low-temperature modification is still not completely worked out. This transformation occurs near room temperature for the stoichiometric composition. The thermodynamic, elastic, crystallographic, and microstructural characteristics of this transformation for some compositions have been previously reported.&apos;-= In the present investigation, the changes in the electrical transport properties and magnetic susceptibility of NiTi when it undergoes the martensitic phase transformation have been measured. The approximate composition range covered is 48 to 52 pct Ti.* *All compositions are given in atomic percent._____________________ EXPERIMENTAL PROCEDURES AND RESULTS 1) Sample Preparation. The NiTi alloys were prepared from iodide titanium (>99.92 pct Ti) and vacuum-premelted carbonyl nickel (>99.95 pct Ni) by repeated arc melting under gettered argon and casting in a water-cooled copper mold. After the cast buttons were hot-forged at 800" to 950°C, the oxidized surface was removed by grinding and etching. Samples were cut from the worked polycrystalline buttons. After fabrication, the samples were annealed 1 hr at 900°C and water-quenched. The composition of the alloys was assumed to be the same as in the initial feed. This assumption was supported by material balance checks on 100-g arc-melted buttons which demonstrated quantitative recovery to within k0.02 pct. The oxygen content of the alloys was &apos;150 ppma (weight) and the carbon content was 30 to 50 ppm. 2) Electrical Resistivity and Hall Effect. The electrical resistivity was measured over the composition range 48 to 52 pct Ti for temperatures varying from 4.2"K to 900°C. The high-temperature and many of the low-temperature experiments were carried out using conventional 4-probe dc techniques.7 The Hall coefficient and ac resistivity were measured at 20 cps using the apparatus shown schematically in Fig. 1. The equipment is basically an ac potentiometer: The resistive or Hall voltage of the sample is balanced by a comparison voltage provided by a dividing network across a standard series resistance. The off-balance signal is amplified by a Tektronix 122 amplifier and detected by a Princeton Applied Research (PAR) phase-sensitive detector. The precision of the resistivity and Hall coefficient measurements is i0.1 and i3 pct, respectively. The uncertainty in the data is increased by i2 pct from the precision limits because of uncertainty in dimensions and possible end effects. The temperature dependence of the electrical resistivity and Hall effect for a stoichiometric (50.0 pct Ti) NiTi sample are illustrated in Fig. 2. Above 75"C, this sample has essentially the B2 structure, while below about 0°C it is completely in the low-tempera-

Jan 1, 1968

By J. L. Smith, A. L. Albee

This article presents a series of guidelines by which the geologist can evaluate the likelihood of surface faulting and its probable extent at any given site in Southern California and Nevada. The information is intended primarily for geologists concerned with establishing design criteria for proposed nuclear plants. The geologic problems involved in the location of a nuclear power plant are fundamentally no different from those for other types of installations. They fall into four main categories: foundation stability, landslides and slope stability, shaking due to earthquakes, and surface faulting. For problems in the first three categories the foundation engineer, the geologist, and the seismologist can provide criteria for plant location and design, and these problems can generally be economically handled by appropriate design measures for a project of the magnitude of a nuclear plant. However, problems in the last category — surface faulting — are more difficult to handle and require a unique evaluation. Accordingly, this paper will deal primarily with the problem of establishing design criteria for surface faulting, particularly as it affects nuclear facilities. A nuclear reactor is a power source that for greater safety is contained in a heavy, air-tight structure, just as gas, oil, water, and other power sources must be contained. Surface faulting is significant in that it may reduce the integrity of the containment by affecting critical exterior piping or by breaching of the containment. A similar significance exists relative to dams or tanks for the storage of water, gas, or oil, except that in these latter examples the breaching of the container automatically releases the fluids to do their damage. This is not necessarily the case with the rupture of a reactor containment structure because the function of the containment is totally protective, i.e., it is necessary only in the event that radioactive products are released from the reactor, and there are many other safeguards to pre- vent this release even if the containment is ruptured. At the present time, nuclear power plants must be located near large sources of water for cooling the steam generated. The construction of an industrial facility of any kind on the coast line is esthetically distasteful to most people since, unfortunately, there is not enough coast to fulfill all the needs and all the desires of all the people. In most cases where industrial facilities encroach on the lives of citizens, there is no mechanism other than zoning laws by which a person can effectively protest. But in the case of a nuclear facility, the public hearing required by the Atomic Energy Commission provides a forum for dissent, as in recent case histories, and the question of safety provides objectors with a weapon for fighting the construction of the plant. The nature of a public hearing for a nuclear plant is such that the prospective owner and operator must prove that there is no undue hazard, whereas the objectors need only demonstrate that there is a reasonable doubt. It is in this situation that geology becomes the Achilles Heel of nuclear power plant location. For his investigation, the geologist has natural exposures of rock at the ground surface and a limited number of trenches and drill holes to give him a fairly complete picture of the distribution of the various rock types. From the surficial data, he must infer three more dimensions — depth below the surface, past time, and future time. Unlike many problems faced by engineers, the geologist has only this one set of data from which to reach a conclusion — he is unable to reproduce the natural sequence of events in order to obtain another set of data for comparison. Hence, by the very deductive nature of a geologic conclusion, it is difficult to prove a geologic conclusion beyond a reasonable doubt even to other geologists — and perhaps one should say especially to other geologists because the experience and background of a geologist will strongly influence his conclusion, and no two geologists have exactly the same experience and training. The engineer and the public official would like the geologist to conclude that faulting cannot occur at a given site or to assign a numerical value to the probability of its occurrence — but no responsible geologist can do either of these things. Since government officials and others must make decisions that affect the public safety, it would seem that the geologic profession must attempt to establish criteria and

Jan 1, 1968