By E. J. Nielsen, P. R. Strutt

A study has been made of the progressive changes in the distribution of etch-pit structures occurring during high-temperature creep in copper + 7 wt pct Al single crystals oriented with a [113] tensile axis. The two equally stressed glide systems with the highest Schmid factor would be expected to form subboundaries of the type predicted by Kear.2 The alignments of etch-pits on sections parallel to different (111} planes consistent with these types of boundaries were not observed. However, they were consistent with planar subboundaries (on a macroscopic scale). From an analysis of Amelinckx1 it may be shown that stable cross-grid dislocation boundaries may form in the primary slip planes. These boundaries form when dislocations with a Burgers vector not in the slip plane move into the plane by combination of climb and glide. THE geometry of subboundaries formed by the interaction of dislocations of two glide systems has been analyzed by Amelinckx,1 and the particular types produced by deforming fee crystals are predicted by ear.' In this paper types of boundaries which may be formed when climb as well as glide occur are discussed as this is relevant in high-temperature creep. It is assumed in the present investigation that the etch-pits observed in Cu + 7 wt pct A1 on surfaces parallel to {111} planes delineate the sites of dislocations. Although there is no direct evidence for this previous work on a-Cu/Al single crystals by Mitchell, Chevrier, Hockey, and Mon-aghan,3 would show this assumption to be reasonable. The alignments of etch-pits which form during creep are studied on sections parallel to each {111) plane. It is then deduced that these alignments are consistent with a specific type of planar subboundary. The Cu + 7 wt pct A1 single crystals had a [113] tensile axis and Fig. 1(a) shows schematically the relation of the slip planes and slip directions (as represented by tetrahedron ABCD) with reference to the tensile axis. The two equally stressed glide systems with the maximum Schmid factor namely ß-AD and (a-BD, from the analysis of Kear,2 would be expected to form the boundaries shown in Fig. l(a) and (b), also Fig. 5(a) and (b). EXPERIMENTAL PROCEDURE The a-Cu/Al single crystals were grown and annealed in a "gettered" argon atmosphere. Chemical analysis showed the aluminum content to be uniform in each crystal and the difference between crystals was maintained to an accuracy of ± 0.25 wt pct. The initial dislocation density and mean subgrain diameter after annealing was -106 cm-2 and 250 µ, respectively. Surfaces parallel to (111) planes were produced by specially developed electrolytic machining processes. The {111} faces were next electropolished for 5 min in a solution consisting of 25 g chromium trioxide, 113 ml glacial acetic acid and 40 ml water; the applied potential was 8 v. Dislocation etch-pits were revealed using l an etchant described by 1 ml bromine, 45 ml HCl, and - 250 ml water. RESULTS In crystals strained into secondary creep at higher stresses (443 and 750 g - mm-2 at 650° C aligned rows of etch-pits parallel to slip plane traces were evident in sections parallel to the (1111, (ill), and (111) planes, see Fig. 3. As well as the longitudinal alignments in Fig. 3, well formed randomly oriented arrays indicative of an equiaxed subgrain structure are evident. At the lower stresses (100 to 230 g . mm-2) only an equiaxed structure formed during creep. The sections in Fig. 3 are from a crystal crept for 70 hr at 650°C with a CRSS of 443 g.mm-2. Two identically oriented crystals were also deformed at the same temperature and stress for 5 min and 4 hr. In the crystal crept for 5 min, the etch-pits were randomly distributed with no tendency for directional alignment, see Fig. 2(a). As shown in Fig. 2(b) aligned arrays were evident after 4 hr creep but they were not nearly so well defined as in Fig. 3. The alignments (parallel to the arrows) in Fig. 3 are consistent with the existence of boundaries in the two main slip planes a and ß. The way in which this is deduced is seen by reference to Fig. l(c), where the existence of boundaries in the a and ß planes is verified by sectioning parallel to a,ß, and d. The (111) and ß(111) planes intersect the d(111) plane along BC [101 ] and AT [011] and alignments parallel to [101] and [011] are clearly evident in Fig. 3(c) in a section parallel to the d(111) plane. Similarly the a, and ß planes in Fig. l(a) intersect each other along DC [110] and hence there will be an alignment parallel to [110 ] in sections parallel to the a-plane and the ß-plane; this is evident in Fig. 3(a) and Fig. 3(b). It is interesting to note that alignments of etch-pits consistent with the boundaries predicted by Kear2 were not observed; see Figs. l(a) and l(b). The geometry of boundaries in {111} planes as shown in Fig. l(c) is discussed later. In Fig. 4(a) the individual etch-pits are resolved and the alignments are exactly parallel to the slip trace direction [101]. However, in some areas alignments deviate away from the slip trace direction by as much as 10 to 15 deg, this is evident in Fig. 4(b), and in Fig.

Jan 1, 1969

By Robert J. De Angelis, James H. Barker

An improved method for solving dynawzical dislocation problems using a digital computer is described in this paper. Interactions between two distinct types of dislocations were studied: attractive screw dislocations; and Lomer lock forming dislocations. One dislocation is positioned in the lattice and is initially at rest, while the other dislocation is moved through the lattice on an intersecting slip plane at a constant velocity in the range 0.5 to 0.999C. (C is the transverse velocity of sound.) The results obtained from these computations indicate that screw dislocations account for a small fraction of the total strain over a wide portion of the range of velocities studied. They further indicate that mixed dislocations mainly repel other dislocations in the neighborhood of the active glide plane. From this a possible explanation for cell formation is put forth. The density of Lomer locks expected to exist after a strain of 0.2 was found to be 1.4 x 106 cm-2 which is in good agreement with indirect experimental estimates. IN the past, predictions of favorable or nonfavorable dislocation reactions were based on the associated changes in elastic strain energy. Such considerations take no account of the probability of the two dislocations coming into contact to react. Venables1 was the first to approach these probabilities by considering the interactions between two moving screw dislocations on perpendicular glide planes. Because of the restrictive types of dislocations and glide plane geometry employed, his results have limited application to metallic crystals. The work to be presented here develops a general approach to solving dynamical dislocation problems; either dislocation-dislocation interactions, presented here in detail, or dislocation interactions with any other suitably defined stress field. Two types of dislocation-dislocation interactions common to face centered cubic (fee) materials are considered: those between pure screw dislocations of opposite sign on intersecting slip planes and those between mixed dislocations on intersecting slip planes, that can react to form a perfect dislocation. This latter reaction, referred to as the Lomer reaction, produces a locked product dislocation that finds it energitical favorable to disassociate into two Shockley partials and a stair-rod dislocation. This partial configuration known as a Lomer-Cottrell (L-C) lock plays a major role in work hardening of fee crystals. seeger2 names the L-C lock as the prime contributor to Stage II hardening while Kuhlmann-wilsdorf3 and Meakin and Wils- dorf4 also state that it is a significant contributor to work hardening. However, with a few notable exceptions,5-7 direct observations of the Lomer lock and the L-C lock by electron transmission microscopy are scanty, and even these are subject to other interpretations.5,6 In a study of partial dislocations present in austenitic stainless steel, whelan8 did not observe any L-C locks at the head of pile-up groups. This result contradicted existing work hardening theories and led him to postulate an alternate theory based on the stress required to break away dislocations intersecting a pile-up group, from their stacking fault nodes. Due to the importance of the Lomer reaction in producing L-C locks which are an essential feature in current work hardening theories and because there exist no data giving direct quantitative values for the density of locks, and because there has even been some doubt expressed as to whether this important reaction occurs at all, a study of the dynamic behavior of the mixed dislocations which form the Lomer lock was undertaken. Due to their ability to cross-slip with relative ease, screw dislocations play an important role in the deformation of fee crystals. For this reason, the second type of reaction considered here is between screw dislocations of opposite sign. In addition, computations in volving screw dislocation interactions are relatively simple, thus providing a convenient check on the cornputational scheme employed. DEFINITION OF PROBLEM The force exerted on a dislocation due to a generalized stress field is given by the Peach and Koehler9 equation: Here t2 and b2 are respectively the tangent and Burgers vectors of the dislocation, and T1 is the stress dyadic defining the local stress field. The stress field may be externally applied or generated internally by the presence of a lattice defect, such as a second dislocation, as is the case in this work. Frank10 has shown that an equivalent momentum, P, of a screw dislocation can be defined by: Here, EST is the total energy of a screw dislocation and ESo is its rest energy. The left side of Eq. [2] is the time derivative of momentum and the right side is the position derivative of the energy due to the dynamical nature of the dislocation. The total energy of a dislocation is the sum of the potential and kinetic energies. Weertman11 has developed the expressions which were used here; these give the potential and kinetic energies of uniformly moving edge and screw dislocations in an isotropic medium.

Jan 1, 1969

Jan 1, 1969

By M. N. Qureshy, D. D. Sarma, B. K. Verma

Kolar Gold Fields are one of the best known gold deposits in South India where gold occurs in quartz reefs in Archaean hornblende schists and shows large variation in grade. The history of mining goes back to 18th century. The workings at Nundydroog Mines, chosen for Operations Research studies, have entered a depth of 2150 meters. The gold values in these mines were thought to be erratically distributed. However, by using 10540 samples from 49 blocks of ore, it is established that the gold value properties in inch- pennyweight units follow a two parameter log-normal distribution. Emperical relationships between arithmetic means and estimates based on peripheral and internal block values have been worked out using the estimator suggested by Krige (1951) instead of 't' estimator suggested by Sichel (1952). These relations can be used in arriving at block estimates with respective standard errors. There is no significant emperical relationship between depth and the grade of ore.

Jan 1, 1969

By J. S. Kirkaldy, R. C. Dorward

The solubilities of copper and gold in silicon and germanium have been determined by equilibration of the solid semiconductors with coexisting liquidus phases. The experimental results were combined with estimated activity coefficients of the liquidus alloys to determine the following partial molar enthalpies and excess entropies of solution for the systems: Solubility measurements were also carried out below the eutectic temperature of the copper-silicon system. The partial molar enthalpy and excess entropy of copper in silicon with respect to Cu3Si were determined to be 40.2 ±0.5 kcal per mole and 9.7 i 0.5 cal per mole — OK, respectively. It has been dentonstrated that nu-cleation and growth of intermediate compounds are retarded in copper-silicon diffusion couples. This points out the dangers of determining equilibrium solubilities by dijjusion methods. THE thermodynamic requirement for equilibrium between contiguous phases at constant pressure and temperature is that the chemical potential of each component be constant throughout the system. Equating expressions for the chemical potential of solute, component 2 say, in two phases, alpha and beta, gives

Jan 1, 1969

Jan 1, 1969

By P. Somasundaran Discussion by Knut L. Sandvik

Knut L. Sandvik (Mining Engineer, Mineral Dressing Laboratory, Technical University of Norway, Trond-heim, Norway) — The discovery that adsorption at solid-liquid interfaces is influenced by adsorption at other interfaces may prove very fruitful in the further development of flotation theory. Having reached the same conclusions as P. Somasundaran in some experiments with amine hydrochlorides, I would like to offer more direct evidence of the interfacial adsorption mechanism based on surface tension measurements and adsorption studies.' This evidence was derived from flotation tests carried out in a Hallimond tube at neutral pH and 60°C. The amount of amine solution and quartz surface were chosen to insure measurable concentration changes during flotation due to adsorption. Adsorption data for

Jan 1, 1969

By B. N. Das, H. E. LaBelle, G. A. Wolf

ZnxHg1-xTe and GUPxAS1-x crystals have been grown from solution by a traveling heater method (THM). In a floating zone type fashion a solution zone sandwich of liquidus composition is made to migrate through feed material of solidus composition by a slow-speed movement of <0.25 mm per hr of the total charge through a stationary radiation or rf heater. ZnxHg1-xTe of composition 0 < x < 0.3 and GUPxAS1-x of composition 0.5 < x < 0.7 have thus been grown from their solution in liquid tellurium and gallium, respectively. A simplified analysis of heat and material transport is given. In this method, Proper adjustment of the temperature distribution along the liquid solution zone axis eliminates instability of the crystal growth front and constitutional supercooling. 1) ZnxHg1—xTe: The solid-solution telluride was grown in sealed quartz tubes at a temperature of 500 to 650°C. For first Preparations mechanical mixtures SINGLE crystals of solid solutions of III-V and II-VI compounds have been grown by various techniques from the melt, from the gaseous phase, or from solutions in of ZnTe and HgTe were used. X-ray determinations showed the resulting crystals to be homogeneous throughout their entire length, except for the end sections. The homogeneity is greatly improved by reusing the ingots obtained from first Preparations as feed material in subsequent crystal growth runs. Ingots of up to 4.5 cm have thus been obtained. 2) GaPxAs1-x: Crystals were grown in a EN crucible at a temperature of 1050°C. For first Preparation a mechanical mixture of Gap and GaAs was cemented together by a minimum amount of liquid gallium through "wet" grinding of Gap and GaAs crystals in the liquid metal and subsequent exuding of excess gallium by compacting of the charge in the EN crucible. Electron microprobe measurements using P-Ka and As-Ka radiation showed uniformity over a length of 0.4 cm. Properties of the various Preparations are described. liquid metals.&apos;-&apos; Their growth from the melt by passing a liquid zone of pseudobinary liquidus composition through a solid rod of solidus composition is generally a convenient method of growth of single crystals of solid solutions of homogeneous composition. This method loses much of its usefulness, however, if the melting point or the vapor pressure of the solid solution is high. In the case of a compound having a high melting

Jan 1, 1969

By J. G. Benford, E. B. Stanley

THERE have been numerous papers in the literature1 on the subjects of secondary and tertiary recrystalli-zation in silicon steels. Secondary re crystallization is believed to occur in silicon steel by either a surface-energy phenomenon such as in the usual development of cube texture or by a second-phase phenomenon such as in the usual production of cube-on-edge texture, (110)[001]. Tertiary recrystallization in silicon steel is thought to be a surface-energy phenomenon in which, for example, grains having a (110) plane parallel to the sheet grow at the expense of other grains in the matrix including those having a (100) plane parallel to the plane of the sheet. In all these instances, the orientations involve either a preferred (100) or (110) plane in the plane of the sheet. Until very recently, there had been no experimental evidence reported of the occurrence of a texture by secondary or tertiary recrystallization that involves a (111) plane in the plane of the sheet, although Kohler reported that grains having the (111) plane parallel to the sheet surface can also grow by a surface energy mechanism. Stickels observed a secondary texture in iron described as "near {554}(225)" about 5 deg from {lll}(211).3 Mee reported that in a vacuum-remelted commercial 3 pct Si steel {lll}(hkl) secondary recrystallization took place in a high vacuum and in pure hydrogen.4 Recently in our Laboratory, large-grained structures such as shown in Fig. 1 having an orientation near (111)[211] or (111)[2ii] have been observed. The arrows point to areas of relatively small matrix grains of the kind that the much larger (111) grains consumed while growing. It is of interest that the matrix grains of samples annealed at 2000°F were essentially the same size as those in samples annealed at 2200°F, a matrix-grain-size stability that is characteristic of secondary recrystallization processes. A torque disc taken from Grain 4 of the sample shown in Fig. 1 revealed a very flat magnetic-torque curve, as expected, with a maximum torque of 7000 dyne-cm per cu cm compared to the typical 180,000 dyne-cm per cu cm observed for conventional (110)[001] textured material. A back-reflection Laue pattern for Grain 4 is shown in Fig. 2 and indicates a near-perfect (111)[211] orientation. The other six numbered grains in the sample of Fig. 1 had a similar orientation. The small circles next to each number were the target areas for the X-ray beam. The starting material was an 0.011-in.-thick oriented silicon steel, (110)[001] texture, containing 3 pct Si. It was lightly pickled, cold-rolled to 0.005 in., and annealed 4 hr at 2200°F within a nickel box (not gas-tight) inside a tube furnace through which dry hydrogen was flowing. The samples were heated to 1500°F in 1 hr and then at 60°F per hr to 2200°F. There were other

Jan 1, 1969

By H. H. Keller, E. J. Couch

Damage to production wells subjected to the high temperatures associated with in-situ combustion projects has been a problem since the advent of this thermal recovery technique. Injection of water down the annulus of hot wells has been successfully utilized for cooling and prolonging the life of such wells. A mathematical model that is suitable for predicting the effectiveness of cooling water in a particular application is developed. Typical results for practical ranges of the various parameters involved are presented. INTRODUCTION In the normal course of in-situ combustion operations, highly damaging conditions develop in the production wells as the combustion zone approaches, and these wells are subjected to high temperatures (up to 1500F). The resulting well damage is recognized as one of the more serious operating problems unique to the in-situ combustion process. Even in operations where well completions have been specifically designed to cope with this problem, the question arises as to how this destructively high temperature can be kept within tolerable limits. A simple and economical approach to this problem is to circulate cooling water down-hole. This method has been used with some success in shallow reservoirs. At greater depths, however, the heat exchange with the overburden surrounding the well and between the fluids in the tubing and the annulus tends to equalize the temperatures of the two fluid streams so that the cooling capacity delivered to the bottom of the hole decreases with well depth. This method would provide no appreciable control over the bottom-hole temperature at great depths. In order to delimit the condition under which cooling by water circulation is effective, the wellbore temperature must be related to the water inlet rate and temperature; to the reservoir depth, production rate, and initial temperature; and to the combustion at at bot tom-hole depth. A model that meets these requirements and that will offer an approach for developing engineering solutions to practical design and operating problems is described in this paper. MATHEMATICAL MODEL Previous studies of temperature distributions include those for flowing wells1p2 and those for hot fluid injection. Adams and Haddenhorst 6 presented solutions for the down-hole circulation of hot oil in the treatment of paraffin-deposition problems. In this paper the thermal model presented by Ramey 4 is adapted to the flow system shown schematically in Fig. 1. Water at temperature Ti is injected at a rate wi and flows down the annulus outside the tubing. It mixes at bottom-hole depth D with the fluids produced at race w from the hot reservoir at temperature T. This mlxtureJ. of injected water and reservoir fluids flows up the tubing and is produced at the surface at TI,. In order to describe the temperature response in this system, we make use of the usual conservation of

Jan 1, 1969

By Carl F. Cline, Richard R. Vandervoort, Willis L. Barmore

THE objective of this investigation was to determine the high-temperature plastic deformation behavior of stoichiometric uranium mononitride as a function of stress and temperature. Interest in the properties of this material stems from its potential use in high-temperature nuclear reactor systems. The creep of other refractory compounds containing uranium (e.g., U02, UC) has been studied by various investigators.1"4 Fassler et al.4 have studied the creep of UN in vacuum from 1100° to 1350°C at stresses of 6000 and 8000 psi. In the present work, the creep of stoichiometric UN was investigated from 1500° to 1800°C at stresses from 2000 to 5000 psi in a partial pressure of 200 mm of nitrogen. The specimens were prepared by hot isostatic pressing of UN powder into cylinders of $ in. diam by about 1 in. high. After pressing, the specimens were heat-treated in nitrogen at 1900°C for 50 hr. The densities of individual specimens were determined by the water displacement method. All specimens were theoretically dense, based on a value of 14.32 g per cu cm.5 Principal metallic impurities in ppm by weight were: Ca, 50; Cu, 5; Fe, 30; Mg, 5; Ni, 10; and Si, 20. Oxygen content was 400 ± 50 pprn and carbon content was 100 i25 ppm. The nitrogen content was 5.56 ±0.05 wt pct. The average grain size for five specimens, as determined by the intercept method, was 0.14 i 0.01 mm. One specimen had a grain size of 2.0 mm. This large grain size is an anomaly, since all specimens had the same chemical and thermal histories. Specimens of 1/4 in. diam by 1/2 in. high were creep-tested in compression in a clam shell furnace heated by W-25 pct Re sheet elements. Temperature was measured to ilODC by an optical pyrometer which had been calibrated by a standard source. The distance between fiducial marks on the specimen was measured before placement into the furnace. The furnace chamber was evacuated to 10-5 Torr and back-filled to 200 mm N2. After heating rapidly to temperature, the load was applied and controlled to ±2 pct by an Instron testing machine. Upon initial loading, the specimen was deformed until a constant crosshead rate was obtained, then quenched to room temperature, remeasured, and replaced in the furnace. Upon subsequent reloading at temperature, the crosshead rate was constant for the selected condition indicating steady-state creep.

Jan 1, 1969

By J. P. Neumann, Y. A. Chang

Lattice parameter measurements of the hcp phase in the system Ag-A1 near the stoichiometric composition Ag2Al were carried out for specimens quenched from 825°K, annealed for 10 days at 453°K, and annealed for 100 days at 413°K. The three heat treatments resulted in the same lattice parameters at room temperature. None of the specimens showed any superlattice lines. The lattice parameters of this alloy were also measured at temperature from 77° to 750°K. An anomaly in the temperature variation of the lattice paramete.rs occurs in the region near 400°k, which may be associated with local ordering. FROM measurements of the diffuse scattering of X-rays, it is known that the [ phase in the system Ag-A1 near the stoichiometric composition Ag2A1 ex- hibits a considerable degree of short-range order at room temperature.&apos; Moreover, based on the position of the short-range order peaks a superlattice model had been proposed in the same study and it was suggested that lowering the annealing temperature to 420°K might result in long-range order. In the present study, the diffraction patterns and the lattice parameters of three differently heat-treated specimens, i.e., quenched from 825°K, annealed for 10 days at 453°K, and annealed for 100 days at 413°K, were determined from 77" to 750°K. The purpose of these measurements was to investigate 1) whether long-range order could be established by prolonged annealing and 2) whether the lattice parameters at room temperature depended on the heat treatment, since it had been proposed earlier2 that the lattice parameters in this phase are related to the atomic arrangement. 1) EXPERIMENTAL TECHNIQUES Silver and aluminum, both 99.99 pct purity, were melted in a zirconium oxide crucible under helium in

Jan 1, 1969

By J. S. Blakemore, E. O. Hall

SERRATED yielding, commonly called the Portevin-Le Chatelier effect, is known to occur in a wide range of alloys where the moving dislocations are considered to be locked by the diffusion of solute atoms to them. From the work of Cottrell,1 an approximate relationship between strain rate, E, dislocation density, p , and solute diffusion coefficient, D, giving rise to serrated yielding is: e =Dp

Jan 1, 1969

By S. Dinda

A series of as -quenched 4340 bars were drawn through a carbide die to various reductions. The X-ray diffraction technique of Lopata and Kula was employed to detect preferred orientation in drawn martensitic steel bars with low amounts of deformation, as lord as 0.8 pct The specimen face of each bar examined was cut at a 45-deg angle to the bar axis. The reflecting planes in the 45-deg face were varied by appropriate rotation of the sample using a spectrogonionzeter. TIE X-ray bean of a diffractometer was reflected from the center of the bar and the diffracted intensity was delected with a proportional counter and recorded. Intensity peaks were developed by cold working for 110 planes oriented at 0 and 60 deg to the bar axis. The intensity peaks increased with increasing defortnalion us a preferred orientation with a 110 texture developed parallel to the drawing direction. The intensity peaks for deformed as-quenched specimens remain unchanged after tempering at temperatures as high as 1000°F. The same amount of preferred orienlalion was observed both inferritic (hot-rolled) and martensitic (as-quenched) structures after an equivalent amount of deformation. THE deformation of martensite with medium carbon content. less than 0.5 pct, has been studied by Breyer et a1.1,2 It was reported that changes in properties such as resistivity, carbide precipitation, and the introduction of a yield point phenomenon were produced after cold reduction of as-quenched AISI 4340 steel bars. Later, Breyer and Nachtman3 studied the effect of cold reduction upon X-ray line intensity. They showed that the integrated 110 line intensity increased with increasing deformation when the planes examined were perpendicular to the die drawing direction. The integrated 110 line intensity for planes oriented at 45 deg to the die drawing direction, in contrast, were found to slightly decrease. These changes were proposed to be consistent with the previously proposed model of a stress-induced ordering of carbon atoms in the vicinity of dislocations.1,2 Objections can be raised to the above interpretation of the X-ray results on two grounds: a) Rough structure factor calculations indicate that the intensity changes are too large (50 pct observed vs 2 pct calculated4,5) to be the result of changes in the location of iron atoms produced by the stress-induced ordering of the carbon atoms. b) The results might be explained in terms of preferred orientations, although X-ray evidence of the development of texture has not been reported in the literature for deformations as slight as 1 or 2 pct. The aim of the present work was to determine if preferred orientation was present in such cold-drawn martensitic steel bars. In drawn rod or wire there is generally a certain crystallographic direction which is aligned in the direction of the wire axis, and the crystallographic planes are distributed symmetrically around this "fiber axis".6-8 This type of cylindrical specimen, with the fiber axis located at the center, will show rotational symmetry. Lopata and Kula9 proposed an experimental method utilizing a specimen cut at 45 deg, see Fig. 1. The X-ray beam is diffracted from the center of this bar cross section. The specimen is rotated around an axis perpendicular to the bar axis and lying in the 45-deg cut face. This permits the angle between the normals to the reflecting planes and the bar axis to be varied from 0 to 90 deg.9 With this arrangement the errors due to absorption and irradiated volume compensate each other.&apos; This greatly simplifies analysis of the data and is of considerable advantage for quantitative measurements. If there is preferred orientation in the specimen, more planes are oriented in a particular direction in the bar. When the bar is rotated to the favorable Bragg condition for that particular orientation, the intensity will be higher than that for some other angle. This technique was adopted for the present investigation.

Jan 1, 1969

By D. C. Seidel, M. C. Fuerstenau, R. J. Roman

The existence of a surface charge on the alkali halide salts is shown, and a flotation mechanism involving surface charge and collector solubility is developed. Data suggest that KC1 is positively charged and that NaCl is negatively charged in saturated brines, and that the neutral molecule RNH,Cl is the collector in the amine-KC1 system, RSO, is the collector in the sulfonate-KC1 system, and RCOONa) is the collector in the fatty acid-NaCl system. A number of hypotheses have been advanced to explain the mechanism of soluble salt flotation; one of these involves exchange between collector ions and surface cations. With this mechanism Gaudin1 suggested that the differences in flotability of halite and sylvite with primary amines are due to the ionic size of the RNH;, Kt, and Na t ions. Fuerstenau and Fuerstenau expanded this hypothesis to include many other alkali halide salts. Several exceptions to this hypothesis are known. That is, this model does not explain why salts containing the same cation, or why salts of different degrees of hydration, respond differently to flotation. For example, why NaI is floated with an amine whereas NaI .2H,O is not. Further, no correlation between ionic size and flotation response can be made with sulfonate or car-boxylate as collectors. In addition, this hypothesis does not explain the effect of magnesium or lead activation, nor does it offer any explanation of the role of temperature in salt flotation. Rogers and Schulman3 realized some of the inadequacies of the ion exchange mechanism and proposed another mechanism based on the heat of solution of the salts. They concluded that weakly hydrated salts can be floated with alkyl amines and sulfonates, that strongly hydrated salts can be floated with fatty acids, and that excessively hydrated salts cannot be floated at all. Their work was not limited to the al-

Jan 1, 1969

By E. T. Turkdogan, W. L. Worrell

The rate of reaction of hydrogen sulfide with ferrous sulfide was studied by measuring the initial rates of sulfidation of iron strips in hydrogen sulfide-hydrogen-argon mixtures at 670°, 800°, and 900" C. The time-dependent surface sulfur activity is derived from the instantaneous rate of sulfidation with the assumption that diffusion in the sulfide layer is in a pseudo-steady state with the gas-sulfide chemical reaction. The rate of sulfur transfer from hydrogen sulfide to the surface of iron sulfide is proportional to the partial pressure of hydrogen sulfide and inversely proportional to the activity of sulfur at the surface of the sulfide layer. The derived rate equation is based on the assumption that most of the surface sites on the chemisorbed layer of iron sulfide are occupied by sulfur atoms and that the slow rate-controlling reaction is the dissociation of hydrogen sulfide on the chemisorbed layer. The experimental results are in reasonable accord with this reaction model. 1 HE slow approach to parabolic growth rate in the sulfidation of iron in hydrogen sulfide-hydrogen mixtures is a manifestation of slow approach to surface equilibrium between the gas and the surface of the sulfide layer. For example, at 800°C and Fig. 7 in Part I, the parabolic growth rate begins after approximately 1 day of sulfidation time. With decreasing temperature and decreasing partial pressure of hydrogen sulfide, the time necessary to reach gas-sulfide surface equilibrium is much longer. These observations are similar to those reported previously by Turkdogan et al.&apos; on the oxidation of iron to wustite in hydrogen-water vapor mixtures. The slow approach to gas-sulfide equilibrium is well-demonstrated by the results in Fig. 1 where the square of the weight gain per unit area, ( g S per sq cmI2, is plotted against time for gas mixtures having PH g//>H = 1.0 with 0, 25, 50, and 67 pct Ar at 800°C. The value of 1.5 X lo-&apos; (g S per sq cm)&apos; corresponds to almost complete sulfidation of the iron strip (- 0.05 cm thick) to iron sulfide. The points fall on S-shaped curves. If the inflection parts of the curves are considered to be linear, thus indicating parabolic growth rate and the establishment of gas-sulfide equilibrium, their slopes would have to be the same for a fixed ratio in the gas mixture. Such is not the case, and the slopes for the "linear" parts of the S-shaped curves are lower than the value when gas-sulfide surface equilibrium is established. The subject matter of this paper is the kinetics of the surface reaction of hydrogen sulfide with iron sulfide during the early stages of sulfidation of an iron strip. EXPERIMENTAL RESULTS The apparatus and materials used were the same as those discussed in Part I. In the present experiments of relatively short duration, a purified iron strip, 5 by 2 by 0.05 cm, which was suspended in the uniform hot zone of a vertical zircon tube, reacted with a flowing gas mixture of hydrogen sulfide-hydrogen-argon. The sample was suspended from a gold chain attached to a calibrated silica spring. The amount of sulfur picked up by the iron, which formed a layer of iron sulfide, was determined by measuring the displacement of a reference point on the silica spring, using a cathetom-eter. In all cases, the degreased sample was first annealed in a stream of oxygen-free dry hydrogen for several hours to remove any impurities such as oxygen, nitrogen, or carbon which might have been present on the surface of the sample.&apos; The rate measurements were carried out at 670°, 800°, and 900° C in hydrogen sulfide-hydrogen-argon mixtures with pH2 s/Ph2 ratios from 4 to 0.1. In a few experiments of short duration no sulfur deposition was observed in gas mixtures with (comments concerning sulfur deposition at high pH s/ph ratios were made in Part I.) Typical examples of the results obtained are shown in Fig. 2 for two temperatures and two gas compositions. With the present experimental technique, reproducible rate data could be obtained only after a uniform

Jan 1, 1969

By C. Y. Cheng

THE purpose of this note is to show that the dislocation mechanism controlling the creep of Fe-4 pet Si alloy1 may equally account for the behavior of a-Fe2 over the same temperature range. A recent study of the creep behavior of a-Fe has been made by Ishida et al.2 Their results were in agreement with the mechanism of nonconservative motion of jogged screw dislocations over the entire range of temperatures investigated, from 480° to 1045°K. However, the observed creep rate was much higher than that which could be accounted for by the above model unless the authors assumed that pipe diffusion became significant below 775°K. More recently, Cheng et al.1 inves-gated the creep of Fe-4 pet Si alloy over about the same temperature range and found that the results could be correlated fairly well with a dislocation climb mechanism as represented by Eq. [l]. Proceeding as shown previously,1 if creep is controlled by a single climb mechanism, at intermediate stresses, the shear creep rate, y, can be represented by where n and K are material constants {K is independent of the temperature but dependent on the structure, that is, K decreases during the primary stage and reaches a steady-state value over the secondary stage of creep), t is the applied shear stress, G is the shear modulus, gc is the free energy of activation for creep (usually equal to that for self-diffusion, gd), and RT has the usual meaning. By solving for y, the apparent activation energy for creep, Q which can be determined experimentally, is given by where hc is the enthalpy of activation for creep which usually is also equal to that for self-diffusion, h^. By using Eq. [2], the data in Fig. 2 of Ref. 2 can be re-plotted as shown in Fig. 1. By comparing the two figures, it is seen that the slight increase in the apparent activation for creep over Region II, as noted in Fig. 2 of Ref. 2, is due to the influence of temperature on the shear modulus rather than of the stress on the

Jan 1, 1969

By J. K. Abraham

In recent years there has been interest displayed in the precipitation phenomena occurring in austenitic alloys based on the binary Fe-Ni system.1&apos;2 Previous communications have been extended covering the kinetics of clustering in the Fe-Ni-Ti system and the effect of cluster size on subsequent mechanical properties.3&apos;4 To a great extent the question of coherency, which has a dominant role in determining the mechanical properties, is dictated by the degree of misfit between the precipitate and matrix. Thus, the change in lattice parameter of the matrix with composition is an important variable that should be examined. The lattice parameter, ao, of austenite was determined for Fe-29.75 Ni-1 to 6 Ti and Fe-27 Ni-1 to 10 Ti alloys in this study. The alloys used in this investigation were melted in a vacuum induction furnace from a starting stock of plast iron (99.95), electrolytic nickel (99.9), and ti- tanium sheet (99.5) in a MgO crucible. The alloy compositions in atomic percent are given in Table I and their relative position in the Fe-Ni-Ti ternary is indicated in Fig. 1. The chemical analyses were taken from the homogenized bulk materials treated in a manner related earlier.3 A diamond file was used to obtain powder from the bulk. To remove the stresses induced by filing, the powders were austenitized at 1875°F for

Jan 1, 1969

By C. C. Harris

An analytical solution of the integro-differential equation of batch grinding is proposed as a first appoximation to the xYt surface. The size distribution equation (xY plane) is a three parameter equation previously suggested. Possible refinements are outlined. Comminution kinetics research is presently following several related courses. Some are equivalent, in that they represent different ways of viewing the same facet of the problem, though the entire endeavor cannot be described as being completely integrated. The purpose of this note is to propose and discuss a framework into which the various approaches might be fitted. This must clearly be founded upon an analysis of the xYt surface.&apos; (See also Fig. 1 of Reference 26.) The investigations referred to above comprise mainly researches into the following: (1) The kinetics of the creation of the finer sizes during relatively small grinding times. This is the Fahrenwald-Arbiter-Bhrany 2-3 approach which leads to equations equivalent to a special case of the charles4 relationship. It emerges that initial production of fines follow essentially zero order* kinetics. (2) Disappearance kinetics of the coarser fractions. This appears to be a first order relationship.5-6 (3) Prediction of the xYt surface via the selection and breakage functions utilizing computer-programmed or approximate solutions of the integro-differential equation of batch grinding.5,8-17 A recent discussion by Mika et al.5 references the relevant literature up to about 1966. In addition to these main-stream researches there is some work on the minor topic of extremely long grinding time considered as a limiting case.18-19 The field is supported by investigations into the size distribution of fragments produced by breakage processes, some of this work being most valuably statistical-mechanical in nature.20-25 Better fitting equations, however, are obtained by statistical and curve-fitting methods.26 This

Jan 1, 1969

By A. Rosenzweig, M. M. Karnowsky

The generalized binary diagram of the Au-Sn-Pb system is presented. The chief characteristic is the pseudobinary between lead and AuSn. On the high-gold side of the pseudobinary, four reaction isotherms were found at 363°, 274°, 225°, and 204°C. On the low-gold side of the pseudobinary, three reaction isotherms at 277°, 205°, and 176°C were found. A vertical section from the eutectic solder composition to gold was developed from the isothermal sections generated. METALLURGICAL problems arising from the intentional or accidental formation of Au-Sn-Pb alloys in soldering applications have indicated a need for information on the phase equilibria in this ternary system. The literature indicates that a complete diagram presenting this information has not been prepared. Even the recent excellent work by prince&apos; entitled "The Au-Pb-Sn Ternary System" actually extends only to the AuSn or 50 at. pct Au range. There are more events in the 50 to 100 at. pct Au than in the less than 50 at. pct range. This article by Prince furnished much guidance in preparing this report. Initial efforts with the isopleth from the eutectic solder composition 61.9 wt pct Sn-38.1 wt pct Pb and 0 to 90 wt pct Au indicated that extensions of the work to the whole of the diagram (even if in less detail) were necessary to understand this system. In undertaking the construction of such a diagram, this study used differential thermal analyses (DTA) and metallography with verification and identification of phases by electron microprobe analyses. EXPERIMENTAL PROCEDURE The procedure began with the development of a cell which would be unreactive with lead, tin, and gold, retain its strength to 1100°C, exclude oxygen, and also furnish a suitable well for insertion and protection of a thermocouple to monitor temperature changes in the material. Such a cell would make it possible to reuse the sample should a repetition of determination be desired. Fig. 1 is a photograph of two such quartz cells as finally developed. The specimens have been run many times. The cell is made up of an inner sample bucket and an outer capsule with a thermocouple well which the sample surrounds. The DTA unit was an assembly devised from available instrumentation. The sample holder was a 3-in.-long cylinder of nickel, 2 1/2 in. in diam, fitted securely in a vertical tube furnace. Two holes 7/8 in. in diam were symmetrically located to receive the quartz cells. A dummy cell with nickel powder was used as the reference. The absolute temperature was recorded with a Pt/Pt 10-pct Rh thermocouple with an automatic Kaye ice bath compensator. (Calibration indicated the compensator to be accurate to better than ±0.5° over the 100° to 1000°C range.) The absolute temperature was measured in the sample and recorded on an L&N mul-tirange recorder with a full-scale display of 1 mv and automatic ranging of 99 mv. The differential signal between the sample temperature and the reference temperature was amplified with an L&N microvolt amplifier and recorded on an L&N Speedomax G recorder. Since two charts were obtained, the chart speeds were equalized and each event was noted on the differential chart, and the temperature at that time was obtained from the temperature record.

Jan 1, 1969