Wet And Dry Grinding Methods Effect On The Flotation Of Taknar Cu-Zn Sulphide Ore Using A Mixed Collector

There are interactions between different minerals from the same ore, minerals and grinding media, and the electrochemical conditions present in the system. Grinding in steel rod and ball mills is a common practice in minerals processing. It is accepted, that the electrochemical interactions between the grinding media and minerals in a grinding mill, influence the corrosive wear of balls/rods and the surface properties of the ground minerals. A complex massive sulphide, Cu-Zn, TAKNAR, Iran, was used for all the experiments. The aim of this study was to investigate the effect of grinding media (dry or wet) on the pulp chemistry and recovery of Cu and Zn in bulk concentrate. 1100 g of ore samples were milled, and mill products with d80=85 and 75 micron in wet and dry grinding methods were produced. Rougher bulk flotation experiments were performed with 550g ore samples, at 30% solids. SIPX in conjunction with Aero238 in 1:2 ratio (48 g/t), was used as mixed collector system, and copper sulphate (200g/t) and MIBC (20 g/t) were employed as sphalerite activator and frother. Lime and High purity Oxygen gas were used for adjusting pH at 8.5 and aeration. The results showed that, more positive pulp potentials were measured when the feed had been ground in a dry environment, and the difference in pulp potentials between the dry and wet ground feed was approximately 250 mV after the grinding stage. In dry grinding method, the recovery of Cu and Zn increased approximately 5 and 10%, respectively. In addition, in dry ground samples, the volume of middling and coarse particles (+100 micron) were more and Dry ground flotation feed had better agreed with using a mixture of collectors. After using copper sulphate, pulp potential increased about 50 mV in dry and 75 mV in wet grinding methods. Keywords: grinding media, pulp potential, Cu-Zn massive sulphide, bulk flotation