Viscosities Of FeNO-MgO-SiO2 And FeNO-MgO-CaO-SiO2 Slags (2ac3a2ff-8b6a-455b-99e0-64c885cdd714)

In the present work, the viscosities of molten FenO-MgO-SiO2 and FenO-MgO-CaO-SiO2 semi-synthetic slags for nickel flash smelting were measured in the temperature range from 1473 to 1723K by a rotational viscometer. The ratio of Fe to Si02 was fixed at 1.2, calcium and magnesium oxide contents varied in the range from 2 to 8 mass% and 9 to 12 mass%, respectively. The results showed that silicate anions became smaller by increasing CaO content, which results in a decrease of the viscosity of the slag. In the case of MgO addition the viscosity behavior was complicated. At MgO content below II mass%, the viscosity increased with the increase of MgO at all temperatures tested. However, when the MgO content was above II mass%, the viscosity decreased slightly for FenO-MgO-CaO-SiO2 system. At higher MgO contents, low-viscosity slags can be obtained by adding CaO. At a given composition, .the viscosity decreased with increasing temperature. The higher the temperature, the more MgO can be added before saturation. The effect of Fe3O4 on the viscosity was quite significant. The viscosity of slag increased by 300mPa-s at 1573K when Fe3O4 content varied from 3 to 9 mass%. The viscosity values are presented as the functions of temperature and composition. A comparison between FenO-MgO-SiO2 and FenO-MgO-CaO-SiO2 systems is given in this study.