Time-Temperature-Transformation (TTT) Diagram of Caustic Calcined Magnesia

"The conversion of cryptocrystalline magnesite to caustic magnesia was studied experimentally at temperatures of 400–1,200°C and for calcination times of up to 8 h. A differential thermal analysis– thermal gravimetric analysis showed that decomposition begins at temperatures as low as 340°C and is completed at 600°C. Specific surface area, iodine adsorption number, crystallite size, and loss on ignition were measured to characterize the product quality. It was found that high-quality caustic calcined magnesia can be produced in a narrow temperature (600–650°C) and time range (1–4 h).RÉSUMÉ La conversion de magnésite cryptocristalline en magnésie caustique a été étudiée de manière expérimentale à des températures de 400 à 1200 °C et pour des temps de calcination atteignant 8 heures. Une analyse thermique différentielle – analyse thermique gravimétrique montre que la décomposition commence à des températures aussi basses que 340 °C et qu’elle est complète à 600 °C. La surface spécifique, l’indice d’adsorption de l’iode, la taille des cristaux et la perte au feu ont été mesurés afin de caractériser la qualité du produit. Il a été trouvé qu’une magnésie caustique calcinée de grande qualité peut être produite dans un petit écart de température (600 à 650 °C) et dans une période de temps variant entre 1 et 4 heures."