Thermoelectric Properties Of Boron-Rich Cluster High Temperature Materials

Novel rare earth boron icosahedral compounds are investigated as potential high temperature thermoelectric materials. REB50-type compounds and REB22C2N compounds were synthesized and the thermoelectric properties measured. Seebeck coefficients in excess of 200 V/K are observed at temperatures above 1000 K for the REB50-type compounds. Strikingly, n-type behavior was observed for REB22C2N. Up to now, non-doped B12 icosahedral compounds have all been p-type. The discovery of an n-type compound is extremely important in terms of the potential development of this class of compounds as viable thermoelectric materials. Low thermal conductivities of < 0.03 W/cm/K at room temperature was observed for these rare earth boron cluster compounds.