The Process of Acid Leaching to Synthesize Zeolitic Material from Paper Sludge Ash

We tried to convert paper sludge ash (PSA) into zeolitic product with high cation exchange capacity (CEC) through acid leaching. Typically, PSA from incineration of paper sludge contains a high percentage of calcium in the form of anorthite (CaAl2Si2O8) and gehlenite (Ca2Al2SiO7). It is difficult to convert the ash with a high Ca content into zeolites, or at least into more desirable zeolite phases. Acid leaching with HCl was applied to reduce the Ca content to synthesize zeolitic product with high CEC. The raw ash was treated with 1 M, 3 M, and 5 M HCl solution for 0.5~24 hours (the ratio of the ash to volume of HCl solution was 1/4), and then zeolitic product was synthesized from leached ash through the reaction with 2.5 M NaOH solution at 80 oC for 24 hours. During acid leaching, gehlenite is readily dissolved in a lower HCl concentration solution than anorthite. With increasing HCl concentration, the amounts of Ca, Mg, Si, Al, Fe and Ti extracted from the ash increased. Ca and Mg contents were easily extracted from ash than other elements. The contents of Ca and Mg extracted rapidly at initial stage, and then levelled off. The saturation times of Mg and Ca are almost 0.5 h using all concentrations of HCl solutions. After the synthesis from leached ashes, zeolite-A and -P were synthesized from ash leached in 1 M HCl solution, and 3 M and 5 M HCl solutions, respectively, regardless of leaching time. With in-creasing HCl concentration, the Ca content eluted from the product decreased, due to the removal of Ca via acid leaching before the synthesis, while the Na content eluted from the product increased to 3 M HCl and then decreased, which was almost similar to the CEC of the product, due to the ion exchange of Na-type zeolitic phase in the product. The change of zeolite phases in the product and the CEC of the product depend on the concentrations of Si and Al in the solution during the synthesis. The highest CEC of the product is about 220 cmol/ kg, which was synthesized from the ash leached in 3 M HCl solution.