The Modification of Pyrite and Arsenopyrite Specific Surface and Porosity at Thermal Decomposition

"The paper contains the results of studying about modification of pyrite and arsenopyrite specific surface and porosity at their thermal decomposition. The studying of specific surface was carry out by B.E.T. – adsorption of nitrogen at his boiling-point. In our work were using the electron-microscopical, X-ray structure analysis and chemical analysis. There was established that the decomposition of pyrite and arsenopyrite accompany by increasing of pores volume from 0.303 · 10-3 to 1.23 · 10-3 at increasing of pyrite degree of decomposition about 41 % and then decrease about 0.131 · 10-3 m3/g at degree of decomposition near 100 %. The surface area of pores increase from 0.31 to 1.085 m2/g with following lowering due to enlargement and confluence of minor, small pores. Increasing of porosity accompany with increasing of particles windage that appear the result of heightened dust-furnace partially decomposing pyrite and arsenopyrite particles by air flow from furnace reaction zone. This explains heightened contention of sulfide sulfur in roast dust of sulfide concentrate. 1. INTRODUCTION As a result of ore base exhaustion of ferrous and nonferrous metallurgy at metallurgical treatment are involving more complicated and less qualitative ores. Magnetiting ores content considerable quantity of pyrite complicative the technology of iron extraction. At the same time the pyrite concentrates wining at dressing content different nonferrous metals in industrial quantities. Extracting ores of nonferrous metals are contenting considerable quantity of arsenic at the present time. Extraction of base metals from complicated raw materials demands new technologies. Arsenic contenting in ores is necessary to utilize (waste burial) in more ecological compatible form. Arsenic on acting metallurgical and chemical enterprises from technological cycle is withdrawing in the form of arsenate – arsenite cakes, burial of their may lead to seriously ecological problems as times goes by. In Kazakh National Technical University is carry out the cycle of researching by pyrite, arsenopyrite and arsenate – arsenite cakes treatment with the object of arsenic withdrawal in sulfide form – in more ecological and safe form and with the object of preparation of initial ore raw materials to following pyro- and hydrometallurgical treatment. As a result of sulfidizing of arsenate – arsenite cakes by pyrite are forming the volatile arsenic forms and pyrrhotite of variable structure."