The Modification Effect of Zinc on the Morphology of Mg2Si-reinforced Magnesium Matrix Composites

In recent years, research and development of magnesium alloys have been greatly promoted by the lightweight requirements in critical industries. The use of these alloys, however, has been restricted by their limited mechanical properties especially at high temperatures. The disadvantages can be overcome by producing Mg matrix composites. The Mg?Si alloys containing in situ Mg2Si particles have found a great potential as structural materials. Unfortunately, Mg2Si compounds are prone to form undesirable coarse Chinese script morphologies, which would deteriorate the properties of the materials. Refinement of microstructure is performed for improvement of wear and corrosion resistance. This paper investigates the microstructure and corrosion behavior of pure magnesium, unmodified and modified magnesium matrix composites reinforced with Mg2Si particles. The Mg2Si/Mg composite was prepared via a normal cast route, and then various amount of zinc was added to melt in order to modify the Mg2Si reinforcement particle morphologies. The microstrucrures were characterized by optical and scanning electron microscopy followed by EDX analysis. The corrosion behavior of Mg/Mg2Si composite was investigated by using potentiodynamic polarization measurements. The results showed that by addition of zinc, the average size of the primary Mg2Si became significantly decreased from about 100µm to about 20µm, as well as its morphology changed from dendritic to a polyhedral shape. However, by adding extra amount of zinc many primary Mg2Si particles become coarse again. It was also found proper amount Zn addition increased the corrosion resistance of Mg/Mg2Si composite.