The feasibility of applying low grade Ca-bentonite from shandong, China, to produce activated clay

"Two low grade calcium bentonite (Ca-bentonite) from Hejia (HJ) and Boteng (BT), Shandong, China, mainly contain montmorillonite and quartz, and slightly feldspar, calcite, and montmorillonite content are 32.37% and 55.90%, respectively. In order to examine the feasibility to produce activated clay to meet the standard of Chinese chemical industry (HG/T2569-2007), three types of industrial production process are proposed according to the screen test. The first process is grinding the raw bentonite to -200 mesh and then activating. The second is to activate the raw bentonite directly, and then classify the production to -200 mesh. The last one is to activate the raw bentonite after purification. Three parameters, which are sulphuric acid strength, ratio of liquid to solid and treatment time, are optimized via orthogonal test for every process. The preliminary test indicates that it is feasible to produce acid bentonite of difference quality. For the sample of HJ, milling the raw to -200 mesh first and activating afterwards, the parameter is at 9% acid strength, the ratio of liquid to solid 2, the time 4 hours, temperature 90°C, the products can meet the qualified grade for animal and vegetable oils refining. For the sample of BT, milling the raw to -200 mesh first and activating afterwards, the parameter is at 15% acid strength, the ratio of liquid to solid 2.5, the time 2 hours, temperature 90°C, the products can meet the qualified grade of high decolorization for petroleum products refining. For the sample of BT, adopting purification to -325 mesh by stirring and rubbing at first, and then activating at 9% acidity, under the conditions that the ratio of liquid to solid is 2, the time is 2 hours and the temperature is 90°C, the products can meet the first grade of high activation degree for petroleum products refining."