The Effect of Kyanite and SiC addition on Properties of Andalusite Based Low Cement Castable for using in Pig Iron Ladle

During the last few years, low cement castable refractories found more application in industry, because of good low and high temperature mechanical properties.In the case of alumina based castables ,usually fume silica or reactive alumina are used as superfines in the matrix to form mullite at high temperature which depends to source of alumina . Mullite network formation improves the hot mechanical properties and thermal shock resistance of bodies. The mullitisation of andalusite (so called primary mullite) also produces a certain amount of rich silica glass, part of it being expelled out of the grain. This phenomenon restrict the application of andalusite low cement castable in pig iron ladle. In this research, firstly 8 pig iron ladles from ESC(esfahan Steel company) with different conditions selected and monitored during usage to determine of main factors affecting on corrosion of refractories. Results showed that tap to tap time and undischarged pig iron are the main ones.Therefore monolithic refractories such as castables which increase thermal shock resistance could be substituted. Regarding to ternary phase diagram of Al2O3-SiO2-CaO ,fumed silica was selected as fine particle.After optimization of particle size distribution by using of modified andreasen equation and rehological properties ,different mixture were composed with andalusite ,fume silica, reactive alumina,secar 71 ,SiC and kyanite.All aggregates system components were mixed dry for 1 min in hobart mixer .After water addition wet mixing was continued until getting flowing about 4 min.The ready mixes were poured in the moulds of of 25mm X 25mm X 140mm with vibrations .After demoulding the samples were cured for 24 hrs and dried at 110OC/18hrsand then fired at 1100-1500OC. Physical ,mechanical ,phase analysis(XRD) and microstructure studies (SEM)were carried out according to ASTM standards. Results showed that by addition of kyanite ,more mullite phase formed through the matrix but,because of expansion occured during this phase transformoration, some cracks formed and mechanical properties decreased.By SiC addition the silica film on the surface of SiC lead to improvement of mechanical properties at high temperature