The Alpha Solubility Limit And The First Intermediary Phase In The Copper-Silicon System

DURING an investigation of the copper-rich portion of the copper-silicon-iron system as part of an extensive research program on P.M.G. alloys, which was begun in 1937 in the research laboratory of the Phelps Dodge Corporation, it became apparent that the binary copper-silicon system below 7 per cent Si needed revision, therefore an investiga-tion was undertaken. Both X-ray methods and microscopic technique were employed. Despite the many investigations that have the clarification of this sys-tem as their object, no two successive reports on the system have agreed in placement of the alpha-phase solubility limit, and uncertainty about the secondary phase first to appear has been voiced several times.3,4,5 It was therefore not surprising, when T. Isawa's6 and M. Okamoto's7 works were reported at the time we were finishing up our experimental work, to find essential disagreement between their results and ours. But when C. S. Smith's latest work on the copper-silicon system8 was published just as we were finishing our laboratory report, it was indeed gratifying to find that the latter's diagram and ours checked in all essen-tial features, except the temperature of the peritectic line above 830° C. Many attempts were made to retain the beta phase during the present investigation, but none was successful. Isawa,6 however, reports that he has been able to obtain X-ray photograms of the beta phase. The structure, he states, is body-centered cubic with a lattice constant of 2.848 A.. at 7.2 per cent Si. Okamoto7 and Smith8 both use the designation Kappa for the hexag-onal phase, and to avoid confusion this designation will be adhered to in the present paper.