Study And Development Of The Physical Treatment Of Spent Batteries In An Integrated Recycling Process

Recovery of metals contained in the electrode materials of batteries was studied considering an integrated recycling process constituted by physical and chemical operations. The physical treatment included the shredding of the spent batteries, followed by a wet sieving operation of the fragmented material. The physical behavior of Ni-Cd and Zn-Mn based (alkaline and saline) system batteries was studied and compared. In that sense, shredding operation was performed and the sieving of shredded fractions was accomplished to evaluate the efficiency of the separation of electrodes and scrap. For Ni-Cd batteries the loss of electrode material with the supra fraction (scrap) after the shredding operation was lesser than the Zn-Mn batteries. Especially for saline-type batteries, the electrode attached to the scrap was substantial leading to important losses. This difference can be explained by the composition of the case materials and the internal physical constitution of the electrodes. The wet sieving studies carried out allowed optimizing the separation of the electrode fine fractions from the scrap materials through the analysis of selectivity Cd/Fe or Zn/Fe. For Ni-Cd batteries, maximum selectivity was achieved for the granulometry of 1.4 mm, while for alkaline and saline systems best selectivity were obtained at 2.8 mm and 5.6 mm, respectively. This process allowed the recovery of about 70% of electrodes for Ni-Cd and alkaline systems, and 50% for saline batteries, with less than 5% of scrap as contaminant. This physical step can be considered as a pre-treatment of this type of waste material envisaging its valorization by chemical treatment, as improves the concentration of the elements of interest and decreases the iron content.