State-of-the-art of electroslag refining and challenges in the control of ingot cleanness

Electroslag remelting (ESR) today and into the future, will still be the main process for producing high-quality ingots by suppressing segregation, not just refining chemical composition from impurities. This paper analyses state-of-the-art electroslag refining with a focus on ESR with consumable electrodes, and recent technology with liquid metal supply (ESR LM) in view of their refining abilities and development trends, taking into consideration that the size of the ingots required by industry continues to grow, and the composition of new materials sophisticates to withstand increasingly higher mechanical and temperature loads . The yield of suitable metal in large ingots produced by conventional casting is low due to problems of element segregation by height and crosssection. For example, conventional ingots for nuclear powerplant rotors today reach nearly 700 t in weight. Attempts to directly replace such giant ingots with big-diameter ESR ingots weighing approximately 400 t were also unsuccessful because of growing segregation. Modern ESR equipment and technologies produce 200–250 t of ingots of satisfactory quality, reaching 2.5 m in diameter, implementing the change of consumable electrodes during remelting to increase ingot length. Another way to mitigate segregation is to enlarge the smaller diameter ESR ingot by a 500– 800 mm coaxial layer to the desirable diameter by ESR in the current-supplying mould (CSM). Modelling and experiments prove that refining from impurities and non-metallic inclusions at ESR most effectively occurs at the slag bath and liquid metal pool interface because the ESR LM has provided the same desulfurisation. ESR’s special refining capabilities in CSM come from the much longer time of LM residence shown at titanium purification from hard-melting nitride inclusions that are unremovable in vacuum arc remelting (VAR) and electron beam melting (EBM). Implementation of ESR technologies in CSM, especially with LM supply, is prospective to produce heavy enlarged and hollow forging ingots with prevented development of segregation due to dividing cross-section and reducing overheat of solidifying metal.