Some observations on the annealing behavior of a Cold-Rolled Low Carbon steel

The paper is founded on the results of an investigation on the softening behavior of a cold-rolled low carbon steel. This specimen, originally cold rolled 15 , 30 , 50 and 75% reduction in thickness, were annealed at several temperatures ranging from 481 to 687ªC. A temperature-time range was encountered over which strong competition between these processes was evident. An interpretation on the effect of test variable on determining which one of the competing processes dominated during annealing is presented.