Sodium Roasting Thermodynamics Of Chromium-Containing Vanadium Slag And Its Application

Chromium-containing vanadium slag (V-Cr slag) was obtained by an industrial smelting process of Hongge Ore, which is valuable vanadium-titanium magnetite to extract V and Cr in China. Sodium roasting thermodynamics of V-Cr slag in presence of oxygen were calculated to evaluate the reactivity of chemical compounds. Results showed that the oxidation of FeV2O4 was intensified in presence of Na2CO3 while the oxidation tendency of FeCr2O4 was far lower than that of FeV2O4. It was probably that reactions of impurities including Al2O3, SiO2 and Fe2O3 with Na2CO3 happened and the products can promote the oxidation of vanadium or chromium compounds in lower valence. Based on thermodynamic analysis, a two-step selective extraction process of vanadium and chromium was proposed. Extraction rate of vanadium was 88.6% while 7.0% for chromium in the first extraction step; extraction rate of 90.7% and 95.4% for vanadium and chromium, respectively, were obtained in the second step.