Research on Desilication Technology from Acid Leaching of High-Grade Silic Stone Coal

"A new type of desilication agent (PA-2) was selected by experiment based on the analysis of the characters of silica gel, and the influence of desilication type, desilication dosage, pH value, temperature and aging time on the desilicating effect was studied. The test results showed that on the conditions that pH was 2.0, temperature was 20""C, aging time was12 hours and the dosage of desilication agent was 0.23%, the desilication rate was higher than 93% in solution.IntroductionVanadium is an important strategic resources, which applies to steel industry and petrochemical industry. The main materials for vanadium product are steelmaking vanadium slag, stone coal and containing vanadium waste catalyst, etc. And stone coal is a low-grade carbonaceous silicified vanadium resource, which is unique material for vanadium extraction in China. Meanwhile, our stone coal reserves is No.l throughout the world.The silica acid solution containing vanadium is produced by acid leaching of raw stone coal or its roasted ore. The silica content of this solution is mostly high, besides, when pH is higher than 2 , the solution is unstable. Furthermore, it is very easy to generate gel substance with the increasing of pH value and standing time. 'Ibis silica gel is composed of colloidal particles with the size in 0.001 - 0.1 um. As a result, it is very hard even impossible for the following operation of solution."