Research On Deep Reduction And Magnetic Separation Of Marine Placer Based On Carbon Composite Pellet

Basic characteristics of marine placer were systematically studied by chemical analyze, scanning electron microscope and X-ray diffraction in this paper. It could be found that the marine placer mainly consists of titanomagnetite and titanohematite. A series of experiments were performed to investigate reduction-magnetic separation for Fe and Ti from the marine placer. Effects of reduction temperature, reduction time, carbon ratio, magnetic density, and grinding fineness on the reduction-magnetic separation process were investigated. And the optimal process parameters were obtained as follows: the reduction temperature 1300􀄇, the reduction time 30 min, the carbon ratio 1.1, the magnetic density 50mT, and the grinding fineness of 0.074μm 86.34%. Under such conditions, the metallization rate, iron grade of magnetic substance and iron recovery reached to 94.23%, 97.19% and 90.28% respectively, and the titanium grade in non-magnetic substance and recovery of was 57.94% and 87.22% respectively. The effective separation of iron and titanium could be achieved in reduction-magnetic separation process.