Production Of Rare Earth Ferrosilicide Alloy

Rare earth ferrosilicide is a versatile alloy mainly used to control the detrimental effects of sulfur in steel and to modify graphite structures in cast iron. The aim of this study was to determine the optimum conditions to make rare earth ferrosilicon alloy using a preconcentrate produced from a bastnasite type of ore present in the Beylikahir-Eskisehir region of Turkey. This concentrate contained 23.5%REO, 41.37% CaF2, 10.69% BaSO4, 8.50% CaCO3, 4.18%Fe2O3, 2.83% Al2O3, 2.74% SiO2, 1.20% P2O5 and small amount of other oxides. The initial metallothermic reduction of this concentrate using ferrosilicon and aluminum in a graphite crucible placed in a muffle furnace gave very low recoveries due to the difficulties encountered in adjusting the slag composition, temperature and amount of additives. Therefore, two batches of rare earth oxide concentrate containing 61.1% and 81.7% cerium oxide, respectively, that were procured from a Turkish glass producer, were used to optimize with respect to temperature, duration, slag-making additives and amount of reducers. In these experiments, smelting and reduction was done in an induction furnace with graphite crucible, and, ferrosilicon and aluminum were added after melting the charge. As a result, there was no difficulty in obtaining a rare earth ferrosilicon alloy containing 35-55% RE, 5-25% Fe and 20-40% Si, with about 80% metal recovery. When the optimum conditions were applied to the preconcentrate, alloys of similar compositions were obtained with 70-80% recovery. Experiments were also done with mixtures of preconcentrate and rich concentrate, and, recoveries as high as 95% were obtained. Only in this case, to increase the recovery, mixtures had to be charged to the empty graphite crucible after heating the crucible to the required temperature.