Processing Of Al Alloy-AlN Metal Matrix Composites

In situ synthesis of discontinuously reinforced aluminum alloy metal matrix composites was investigated. Aluminum alloy (A356: Al-7 wt% Si) was reinforced with dispersed AlN particles. Thermodynamic calculations were made for the composition determination of various phases formed during bubbling of NH3 gas into the Al alloy melts in the temperature range 1173-1473 K. Experiments were carried out for in situ production of AlN particles with the reaction between Al melt and NH3 gas in high temperature resistance furnace at 1473 K. The products were characterized using SEM, EDS and XRD. Effect of bubbling time of NH3 gas on the AlN formed in the composites was studied. The amount of AlN reinforcement in the Al alloy composites was observed to be in the range of 5 to 35 wt%. Good agreement was observed between the experimental and thermodynamic calculated data on the composition of AlN in Al alloy composites.