Preparation of M003 from Ammonium Tetramolybdate in Microwave Fields

"Decomposition of ammonium tetramolybdate to prepare Mo03 using silicon carbide crucible in microwave fields was investigated. The results were analyzed Using TG-DTG and X-ray diffraction. Meanwhile, the effects of heating rat, material thickness, socking time, socking temperature on the structure of preparing Mo03 were studied. TG-DTG curves show that the decomposition process of ammonium tetramolybdate is only one stage, in the temperature range 300-350°C, whose begin to decompose when temperature increases beyond 300°C. The molybdenum trioxide was prepared by thermal decomposition. The quality ofMo03 was not affected under the heating rat is 12°C/min. It was beneficial for decomposition ratio with the lower material thickness, longer soaking time, and higher soaking temperature. XRD curves showed that it is viable method for preparation of Mo03 by decomposition from ammonium tetramolybdate in microwave fields.IntroductionMolybdenum is widely used in national defense, aviation, industrial and agricultural production as rare refractory metal. Molybdenum trioxide is vital raw materials for the process of preparation of molybdenum. The traditional production technology of molybdenum oxide is that ammonium tetramolybdate is calcined in rotary kiln or 4-tube furnace [J,2J. But the longer production time, the higher production cost, the lower furnace thermal efficiency, and bigger the energy consumption, especially the powder is easy to leak, the working environment is poor by using rotary kiln [ 3 l _ The particle of molybdenum oxide is non-uniform by using 4-tube furnace because of the uneven temperature of every tube and the poor exhaust of boat bottom [4l _ However microwave heating is quick and uniformity, it is a meaningful research that the microwave is used in the process of calcining ammonium tetramolybdate."