Preparation And Characterization Of Ultrafine Magnetite Powder

Ultrafine (0.1µm) spherical magnetite powder was prepared successfully by hydrothermal reaction of ferrous sulfate and sodium hydroxide with activated pyrite as reducing agent in the temperature range 120-140?. XRD and XPS analyses indicate that pH value and pyrite amount have a direct influence on the composition of the product. Stoichiometric Fe3O4 can be obtained only when pH value is 12 and the molar ratio of pyrite/ferrous sulfate is 1:1.8. The hysteresis loop of Fe3O4 shows a ferromagnetic behavior with a saturation magnetization of 75.2 emu/g and a coercivity of 152Oe.