Preparation and Characterization of Porous Ni-Ti Alloys

"Porous Ni-Ti alloy has many applications in a wide range of engineering areas. The porous NiTi alloys were prepared from Ti and Ni powders in sintering process under argon atmosphere. The major chemical compositions of the sintered Ni-Ti body were Ni Ti, Nh Ti4O and Nh Ti, respectively, the internal pore structures were characterized by image analysis technique, which were dependent on various processing parameters such as sintering temperature, amount of poreforming agent, forming pressure, etc. The results show that the porous alloy samples had the characteristics of uniform pore and high open porosity; pore-forming agent and sintering temperature are important factors in porous; pressure affected the sintered products' pore, by affecting the combination of alloy powder with pore-forming agent.IntroductionPorous Ni-Ti alloy materials exhibit not only excellent shape-memory and superelasticity, high yield strength and ductility, good corrosion resistance and biocompatibility, but also have low density, low stiffness, and high energy absorption rate due to their porous structures [1]. In recent years, these porous Ni-Ti alloys have found applications in a wide range of engineering areas, such as bone implants [2-4], impedance-matching connectors [5], energy-absorbing structures [6,7], separators [8] and actuators [9], etc.Pore characteristics can play very important role in determining of the performance of porous NiTi alloys. For example, when the alloys are used to repair or replace hard tissue implant material, the pore shape and size not only determine their mechanical properties, but also have great effect on the fluid transmission of human body. The pore characteristics can also influence the stressstrain behavior of the porous Ni-Ti alloy and, thus, strongly affect their mechanical properties, superelasticity, and fracture mechanisms [10].In this study, the Ni-Ti alloys with high porosity were prepared in a powder sintering process under argon gas. The pore characteristics were investigated using SEM, XRD and image analysis techniques, especially in association with the content of pore-forming agent, sintering temperature and compacting pressure."