Part X – October 1968 - Papers - Segregation and Constitutional Supercooling in Alloys Solidifying with a Cellular Solid-Liquid Interface

Dilute alloys of silver and of thallium in tin have been solidijzed unidirectionally under controlled conditions, to study the segregation associated with a cellular interface under conditions where both thermal and solute convection are present. Autoradiography and radioactive tracer counting techniques were combined with electron-probe microanalysis to study both macro- and microsegregation. It was found that, for concentrations giving only small amounts of constitutional supercooling, cell formation had little effect on the macroscopic distribution of solute along the specimen. At higher concentrations the effective distribution coefficient was higher than that expected for a smooth interface. Node spacing was independent of initial solute content at lower concentrations, becoming greater as keff increased. Silver content at the segregation nodes of silver in tin alloys was independent of initial concentration and considerably in excess of the eutectic composition. SINCE the investigation of cell formation at advancing solid-liquid interfaces by Rutter and Chalmers,' a large volume of work has been dedicated to the determination of solidification conditions under which a planar interface will break down into cellular form. Early experiments were explained satisfactorily by the concept of constitutional supercooling,2 but, due to poor measurement of temperature gradients in the liquid, lack of accurate data on liquid diffusion and equilibrium distribution coefficients, and uncertainty about the effects of thermal and solute convection, these experiments cannot be used as proof for the theory. More recent work, however, has shown that under conditions where convection is eliminated or can be ignored good correlation is observed.3,4 Investigations into segregation at cell caps5 and at cell nodes6-'' have been made, but no measurements appear to have been done on the overall, macroscopic segregation down a unidirectionally solidified rod of material which has solidified with a cellular substructure. This has practical importance in casting, where regions of material with cellular substructure are often encountered, and also in zone refining where the thermal conditions necessary for a planar interface are unattainable. Further, as will be shown, the macroscopic segregation can give information on the following question. Granted that a cellular solid-liquid interface develops from a planar one when the conditions for constitutional supercooling are exceeded, how much supercooling is present after the cells have formed? EXPERIMENTAL PROCEDURE AND RESULTS Specimen Preparation. Specimens 25 cm long with a square cross section 0.6 by 0.6 cm were grown in graphite boats by solidification from one end. Alloy compositions are given in Table I. Two specimens of each composition were grown. The tin was 5-9 grade and the silver and thallium both 4-9 grade. Ag110 and Tl204 were used as tracers. Each composition had the same quantity of tracer so that auto radiographs of specimens containing different concentrations of the same element could be easily compared. Thermocouples inserted through the lid of the boat into a dummy specimen showed that, over the first 10 cm of growth, thermal conditions were quite steady, with a rate of interface advance of 5.8 cm per hr and a temperature gradient in the melt ahead of the interface of 3.0°C per cm. The specimens were seeded from tin crystals of a common orientation to eliminate orientation effects. Dilution of the specimen by seed material was minimized by the provision of a narrow neck between specimen and seed crystal. Macrosegregation. After growth, the specimens were sectioned with a spark cutter. The rods of silver alloy were cut into 1-cm lengths and analyzed for Ag110 using a y -ray counter with fixed geometry. The specimens containing thallium were cut into 2-cm lengths and analyzed for T1 204 by taking 13 counts from each end of the cut lengths through an aperture in lead sheet approximately 0.4 cm square. The results are summarized in Figs. 1 and 2. To find the effective distribution coefficient for the silver in tin alloys under smooth interface conditions, the region of substructure at the bottom surface of one of the 10 ppm specimens, see Fig. 3, was removed by spark machining before counting. Autoradiography. For both alloy systems the samples were polished on sections taken alternately parallel and perpendicular to the growth direction, and autoradiographed by placing the polished surfaces in contact with Kodak "Process Ortho" film. Figs. 3 and 4 show the structures revealed. The alloy containing 10 ppm Ag showed substructure only after a few centimeters of growth, and then substructure was limited to a narrow layer at the base. The "speckled" substructure reported previously in this system4 is here clearly seen to be an intermediate stage between planar and cellular interface conditions. The other samples show a remarkable similarity considering