Part VIII - Papers - Equilibria in the System Fe-Mn-O Involving “(Fe,Mn)O” and (Fe,Mn)3O4 Solid Solutions

Equilibrium ratios C02/C0 of a gas phase coexisting with selected phase assemblages of the system Fe-Mn-0 have been determined in the temperature range 1000" to 1300°C. The oxygen pressure for the "hfnO" +hfn30, equilibrium and for the "(Fe,hTn)O" + (Fe,Mnh 0* equilibrium at high manganese contents has been determined by electromotive force measurements using stabilized zirconia as a solid electrolyte. The notstoichometry 01' "hTnO" and of "(Fe, iM1z)O" solid solutions has been determined by ther-mog-/avi?netry and by wet-chemical analysis. The data obtained are used to derive activity-composition relations in "(Fe,hfn)O" and (Fe,Mn),O4 solid solutions. WUSTITE "FeO" and manganosite "MnO" form a continuous series of solid solution at high temperatures,' and so do magnetite Fe304 and the high-temperature, cubic modification of Mn304 (Ref. 2) (high hausmannite, -1170). The oxides "FeO" and "MnO" are cation-deficient phases.495 The nonstoi-chiometry of "(Fe,Mn)O" solid solutions has been studied by Engell and ~ohl' at two selected C02/C0 ratios at 1250°C. The two oxide end members of the spinel solid solution, FesO4 and Mn,04, however, are known to be close to stoichiometric under the experimental conditions used in the present investigation.''' The oxygen pressures of "(Fe,Mn)07' solid solutions in equilibrium with iron have been determined by Schenck and coworkers,8 by Foster and welch," and by ~n~e1l.l' The two former groups equilibrated the condensed phases in C02-CO atmospheres of lmown compositions, whereas Engell" used a galvanic cell with stabilized zirconia as a solid electrolyte. The results of these investigators are not in good agreement. Activities of FeO in manganowiistite as calculated from the results of Foster and Welch show ideal behavior, those of Engell yield a pronounced positive deviation, and those of Schenck et 01. show a moderate positive deviation from ideality. In the present work oxygen pressures for the iron + manganowiistite and manganowustite + spinel equilibria and the nonstoichiometry of manganowiistites have been measured. The data were used to calculate activities in the manganowiistite and spinel solid solutions. EXPERIMENTAL METHODS The COz/CO ratios at which manganowustite and iron are in equilibrium were determined by thermo-gravimetric and quenching methods. Experimental details are described in a previous publication.'2 In the thermogravimetric technique, incipient reduction of manganowiistite pellets to metallic iron was observed as a break in the weight vs log COZ/CO curve. In the quenching technique, manganowiistite samples were partially reduced to metallic iron, or the metallic iron of manganowustite + metallic iron mixtures was partially oxidized to manganowustite, in atmospheres of constant C02/CO ratios. After quenching the composition of the oxide phase was determined by X-ray lattice parameter measurements and comparison with a standard curve obtained from oxide solid solutions of known compositions. The nonstoichiometry of "MnO" and "(Fe,Mn)07' solid solutions was determined by chemical analysis of samples equilibrated in C02-CO atmospheres and quenched to room temperature, as well as thermo-gravimetrically by reducing (Fe,Mn),04 or Mn304 to manganowiistite or manganosite. The equilibrium between manganowiistite and (Fe,Mn),04 was measured thermogravimetrically by reducing (Fe,Mn),04 solid solutions having composition in the range of %„ l(NFe +NM) from 0 to 0.63. No experiments could be performed with this technique at higher manganese contents, because the equilibrium C02/C0 ratios are too large for accurate control. An additional difficulty arises at the higher manganese contents due to the strong increase in oxygen content of the manganowustite phase with increasing log Py near the manganowiistite-spinel boundary. Consequently a sharp break in the weight loss vs log C02/CO curve cannot be observed at the phase boundary. At high manganese contents of the manganowiistite, e.g., (NMn/(NF~ + NMn) > 0.9, electromotive force measurements with stabilized zirconia as a solid electrolyte were made to determine the equilibrium oxygen partial pressure. Experimental details are described in a previous paper.* Mixtures of "(Fe,Mn)O" and (Fe,Mn),04 were pressed to pellets, and the oxygen pressure of the equilibrated samples was compared to that of Ni + NiO mixtures in the cell The composition of the manganowiistite in the equilibrated two-phase mixture was determined by lattice parameter measurements and comparison with known standards. The oxygen pressure for the Ni + NiO equilibrium was taken from available data.l3~l4 No reliable results were obtained with the electromotive force technique on iron-rich oxides. The electromotive force drifted strongly with time in this composition range. An additional difficulty arises from the partial de-