Part VIII – August 1968 - Papers - An X-Ray Line-Broadening Study of Recovery in Monel 400

The recovery process in 400 Monel filings was followed, principally, by using the Warren-Averbach technique of X-ray peak profile analysis. The deformation fault probability, a, was 0.006 in samples of unannealed filings. a , the twin fault Probability , was approximately 0.002 in samples of unannealed filings. Both a and 0 were found to "anneal out" at 600°F. The effective particle size and mzs strain increased and decreased in the (111) direction, respectively, with increasing annealing temperature. The actual particle size was found to be almost equivalent to the effective particle size. Tile small values of deformation and twin fault probabilities accounted for the similarity in values of the effective and actual particle sizes. Stored strain energy and dislocation density calculations based on rms strain decreased with increasing annealing temperature. The dislocation density decreased from 10" per sq cm in the unannealed filings to 10' per sq cm in the partially re-crystallized filings. The square root of the dislocation density based on strain to that based on particle size indicated a random dislocation distribution in the unannealed filings. The dislocation arrangement changed to one with dislocations in cell walls with increasing annealing temperature. THE recovery processes which occur in metals are generally thought to be a redistribution and/or annihilation of defects.' Investigators' have shown that recovery processes can be characterized by X-ray line-broadening analyses. Michell and Haig4 measured the stored energy of nickel powder by calori-metry and found the value to be greater by a factor of 2.5 than that from X-ray data obtained by the Warren-Averbach technique.= Minor increases in particle size occurred up to 752°F (recovery), while above 752°F the particle size increased greatly due to recrystalliza-tion. X-ray microstrain values decreased between room temperature and 392"F, remained constant from 392" to 752"F, and decreased from 752°F to a negligible value at 1112°F. Faulkner developed an equation for calculating stored strain energy based on X-ray line-broadening data which gave a closer correlation of measured and calculated stored strain energy based on the data of Michell and Haig. The stored strain energy released during recovery is predominately dependent on the decrease in dislocation density which was p-enerated from cold work.7 Stored energy has been measured8 in alkali halides during recovery and recrystallization and 80 pct of the stored energy was found to be released during recovery. Dislocation distributions have been studiedg in a number of fcc metals by thin-film electron microscopy. Howie and Swann" found the stacking fault energy of copper and nickel to be 40 and 150 ergs per sq cm, respectively. ~rown" has pointed out that these stacking fault energy values should be corrected to 92 and 345 ergs per sq cm, respectively. The dislocation distribution of a metal is directly dependent on the stacking fault energy of the system. Metals of high stacking fault energy such as aluminum cross-slip readily and do not form planar arrays of dislocations. Metals of lower stacking fault energy such as stainless steels" do not cross-slip readily. Cold-worked nickel has been found to form a cellular dislocation structure after annealing.13 The relatively high stacking fault energy of nickel and copperlo to a lesser extent favor cellular structures of dislocations rather than planar arrays after deformation. The present study of recovery was carried out on a Ni-Cu alloy (Monel 400) to compare with prior studies for pure nickel and pure copper. X-ray line-broadening techniques were used to measure the effect of recovery temperature on rms strain and particle size and the results were compared with previous studies on copper'4-'7 and nickel., Calculations were also made on stacking fault probabilities, dislocation density, dislocation distribution, and stored strain energy as affected by temperature. EXPERIMENTAL PROCEDURE The nominal analysis of the Monel 400 used in this investigation was: 66.0 pct Ni, 31.5 pct Cu, 0.12 pct C, 0.90 pct Mn, 1.35 pct Fe, 0.005 pct S, 0.15 pct Si. The annealed material was cold-reduced in two batches, one 50 pct and the other 80 pct. It was originally planned to conduct line-broadening studies of these bulk samples; however, rolling textures that developed produced low-intensity peaks which were not suitable for line-broadening analysis. Filings were prepared at room temperature from both the 50 and 80 pct cold-reduced specimens, series A and series B, respectively, and were not screened prior to heat treatment or X-ray studies. Heating to the annealing temperature, 200" to 120O°F, was accomplished in a matter of minutes in a hydrogen atmosphere. Following heat treatment, some of the filings were mounted and polished for microhardness measurements with a Bergsman microhardness tester, using a 10-g load. A G.E. XRD-5 diffractometer using nickel-filtered Cum radiation was used to obtain all diffraction patterns. Only (111)- (222) line-broadenin data were used in the present study since the {400f peaks were too weak to use. The Fourier analysis of the (111) and (222) peak