Part VII - Papers - C. Norman Cochran

Quantitatiue studies of the deformation texture in drawn tungsten wives were made by the X-vay dif-fractottletetr. Experimental results show that the diffraction Intensities are equal to tilose pvedicted from the (1 10). fiber lexlure but the angxla), spreads of. diffraction peaks in the pole distribution curres are different for different diffraction planes and directions. For this reason a modified (110) fiber lextuve model, in which a kind of anisotropy is assumed, is proposed to explain the results. According to this model the poles lying on a line directing front the (110) to the (110) poles in the (1 10) standard stereograpllic projection should show spreads which are different from those lyitlg on a line directing from the (001) to the (001) poles, which is confirmed by the experiments. The anisolvopy and the spveads of the pole positions are large at the outer part of the wires and decrease gradually lowards the inside of the wire. The possibilily of occurrence of such anisolropy in irrelals with fcc stvuctures is discltssed. THE deformation texture of drawn tungsten wires has been assumed by different investigators to be the simple ( 110) fiber texture.' Recently, however, Leber2,3 has shown that a swaged tungsten rod has a cylindrical texture. It changes gradually to the (110) fiber texture by drawing through dies. However, even after drawing to 0.25 mm in diam, the cylindrical texture can still be found in wires together with the (110) fiber texture. This was deduced from the pole figures obtained from the longitudinal section of these wires. Use was made also of quantitative measurements of the pole distribution curves. Leber stated that the angular spread of the pole distribution curves (henceforward called dispersions) are quite different for (400) 45 deg and (400) 90 deg: the former is always larger than the latter. This inequality is accompanied by deviations of the diffraction intensities from the theoretical values for the ( 110) fiber texture. Bhandary and cullity4 have reported similar results on iron wire and explained them by assuming a cylindrical texture. Both Leber3 and Bhandary4 used only the results of the (400) reflection for the determination of the dispersion. The pole figures found by Leber3 and by Rieck5 are largely different. The model given by Leber to explain the effects is in the authors' opinion in some respects unsatisfactory, especially if one looks at other than the (400) reflections. Intensities and dispersions of diffraction peaks are conclusive factors for the determination of the fine structure in wire textures. For this reason we studied them extensively to come to a model which is more suitable to fit the facts. In the following, after giving the experimental set-up, we report about measurements of X-ray diffraction on drawn tungsten wires. Different models to describe the experimental results will be discussed. EXPERIMENTAL GO-SiO2-A12O3 doped tungsten wires drawn to 0.18 mm in diam were used for the measurements. The wires were chemically etched to various diameters down to 0.03 mm. Measurements were carried out for the different wires in order to determine the dependence of the texture on the radius. The wires were cut to pieces of 10 mm length and fixed with paste closely against each other on a flat, polished glass plate. Parallelism of the wires with the surface of the glass plate should be adequate. For the diffraction studies three different X-ray sources were applied, respectively, giving the CuK,, FeK,, and FeKp emission. The measurements were carried out with a diffrac-tometer with a GM counter. The latter was fixed to a certain diffraction angle 20hkl and the diffraction intensity was recorded as a function of the angle of rotation of the specimen around the axis, lying in the specimen surface and perpendicular to the wire axis, as shown in Fig. 1. Measurements were also done with the detector at angles slightly deviating from the diffraction maxima The measured intensities in this case were taken to be equal to the background level. The deviations were chosen as small as possible but large enough to eliminate the influence of the diffraction maxima. The useful range of the rotation angle x of the specimen is generally limited by the wavelength of the X-rays. We have: where and cp is the angle between the wire axis and the normal of the diffraction plane. Intensity measurements were made to find the necessary corrections for counting loss of the GM counter and for distortion resulting from such effects as absorption of X-rays and from inclination of the reflection plane under study with respect to the surface of the specimen. The counting loss was esti-