Part VI – June 1968 - Papers - Microstrain Compression of Beryllium and Beryllium Alloy Single Crystals Parallel to the [0001]- Part II: Slip Trace Analysis and Transmission Electron Microscopy

The slip mode activated during the c axis compression of single crystals of commercial-purity ingot SR beryllium, high-purity (twelve-zone-pass) beryllium, and Be-4.4 wt pct Cu and Be-5.2 wt pct Ni alloys in the temperature range of 25° to 364°C was determined using two-surface slip trace analysis, slip-step height analysis, and electron transmission microscopy. All three techniques indicated the occurrence of copious pyramidal {1 122) (1123) slip in the alloys over the entire temperature range, the amount increasing with temperature. Pyramidal slip was also indicated in the high-purity beryllium by slip trace analysis and electron transmission microscopy, but the amount was somewhat less than in the alloys. For the commercial-purity ingot crystals, only a very small number of pyramidal slip lines were observed, and these were in the immediate vicinity of the fracture surface. No pyramidal dislocations could be detected by electron transmission microscopy in this material. Dislocatransmissiontions with Burgers vectors [0001] and +(ll20) were identified by electron transmission microscopy inthe (1122) slip bands, as well as those with the j (1123) vector. This was interpreted to indicate that the edge components of the 3(1123) vector dislocations activated during c axis compression dissociate upon unloading according to the reaction i (1123) — [0001] + 3(1120) THE microstrain c axis compression of single crystals of commercial-purity ingot SR beryllium (99.6 pct), high-purity twelve-zone-pass beryllium (99.98 pct), Be-5.24 pct Ni and Be-4.37 pct Cu alloys was described in a previous paper.1 This paper covers in detail the analysis of slip traces observed on two mutually perpendicular lateral surfaces of these specimens, and a detailed description of transmission electron microscopy studies performed on foils cut from the bulk crystals after they had been deformed to fracture in the c axis compression. Observation of slip traces on single surfaces of deformed single crystals are generally insufficient to positively identify slip or twinning modes. The use of two carefully cut and oriented perpendicular surfaces can greatly aid in the positive identification and index- ing of slip traces, although even this technique may be quite inadequate if more than one type of slip system operates and if an insufficient number of traces are observed on the surfaces. The problem is greatly simplified for symmetric cases like that for c axis compression of an hep crystal such as beryllium, in which the operating slip systems are all equally inclined to the direction of the applied stress, and each slip system of a given slip mode has an equal chance of operating. For such cases, the traces of any given slip mode observed on the surfaces cut parallel to the c axis are symmetrically tilted about the c axis. It is therefore possible to quickly determine whether one or more slip modes are operating. Confirmatory evidence in support of the observations made on the external surfaces can be obtained from foils cut from the deformed crystals and examined by transmission electron microscopy. This latter technique serves to identify not only the operating slip plane but also the Burgers vector of the dislocations which participate in the slip. For this purpose, a simplified technique based upon a double tetrahedron notation is used in the present paper. The planes and directions in the hep lattice are all designated by letters rather than indices and extinction conditions are easily determined if the Burgers vector lies in the plane contributing to the diffraction. RESULTS 1) Slip Trace Analysis. The standard (0001) stereo-graphic projection of beryllium is shown in Fig. 1. The two mutually perpendicular, lateral surfaces of the compression specimen are represented by the diametrical planes AA' and BB', also referred to as surface A and surface B. For the specific case represented (a Be-5.24 pct Ni specimen deformed by c axis compression at room temperature), the A surface is tilted 5 deg to the (10i0') plane and the B surface is tilted 5 deg to the (1120) plane. Two surface trace analyses may be facilitated by examining in turn the intersection of various great circle traces of specific pyramidal planes with two surfaces and comparing the angles made with the (0001) plane with those actually observed on the two surfaces. One then identifies the slip traces by trial and error on a best-fit basis. The (1122) type planes (it was found that slip occurred on these planes) are shown plotted on the stereographic projection in Fig. 1. One obtains directly the angles between the (0001) plane and the {1122) traces by measuring the angle from the periphery to the point of intersection along the lines