Papers - X-ray Analysis of Hot-galvanized Heat-treated Coatings (T.P. 1224, with discussion)

Hot-dipped heat-treated zinc coatings on sheet steel were examined with X-rays. The phases identified were compared with those listed in the modern literature 01 the zinc-iron system. The zeta (FeZn13) phase is shown to correspond to the phase found by Schueler (1925) in heat-treated zinc coatings. An investigation was undertaken to determine the phases present in hot-dipped heat-treated zinc coatings on steel sheets and wire. This kind of coating on wire was studied some years ago by Schuelerl by microscopic and chemical methods. He reported a new phase, FeZn10. Later, Clark and Stillwell,2 using X-ray crystal analysis, identified a new phase in ordinary galva. nized wire, which was assumed to be the FeZn10 phase. Since the extensive review of the iron-zinc alloys presented a few years ago,3 much new work has been published, some of which5-l6 was too late to be included in the recent edition (1939) of the American Society for Metals' Handbook.4 Figs. 1 and 2 are reproductions of the latest iron-zinc diagram proposed by Schramml1 as a result of his investigations by microscopic, thermal, magnetic susceptibility and X-ray methods. Table 1 summarizes all the known published X-ray data of the phases Present. The solubility of iron in zinc has been determined by x-ray methods.10 In the same manner the homogeneity range of the P phase was studiedlo using the principle that the parameter of an intermetallic compound changes while the concentration of One of the constituents changes. Schramm10 has found some 80 alpha lines in X-ray powder photograms of phase d1, and from these he believes that this phase is related to the P phase. Previous investi-