Papers - Reduction of Iron Ores under Pressure by Carbon Monoxide (T. P. 1134, with discussion)

In a previous investigation1 the authors studied the effect of pressure on the reduction of iron ores by hydrogen. With hydrogen as a reducing agent, the rate of reduction was increased substantially by increasing the pressure from 1 to 2 atmospheres. The results with hydrogen prompted the present study of the effect of pressure on reduction with carbon monoxide and with mixtures of carbon monoxide and nitrogen. Features of Reduction Process The gas stream in the lower part of the blast furnace always contains sufficient concentrations of reducing gases to complete reduction provided sufficient time is allowed for the reaction to proceed. Reducing gases react immediately with the iron oxide on the surface of lumps of ore. However, as the unreduced surface recedes from the easily accessible exterior of the lump, the reaction proceeds by virtue of the diffusion of the gases into and out of individual pieces. The rate of diffusion of gases, which undoubtedly plays an important role in the reduction of iron ores, depends on several factors, most important of which are: (1) molecular weight or density, (2) pressure, (3) temperature, (4) concentration gradient. Thus, the rate of reduction of a lump of iron ore at any temperature will depend not only on the specific reaction rate but also upon: (1) available surface of unreduced iron oxide, (2) rate of diffusion of the reducing gas to the reacting surface, (3) rate of effusion of the gaseous products of the reaction from the reacting surface, (4) adsorption of the gases on the reacting surface. The various features of the reduction process were discussed in previous work and need not be reviewed. However, in order to explain