Papers - Influence of Temperature on Elastic Limit of Single Crystals of Aluminum. Silver and Zinc (With Discussion)

Work was undertaken two years ago at the Hammond Laboratory for the purpose of determining the magnitude of the elastic range in single crystals of pure metals by means of creep tests, the assumption being made that if a true elastic range exists, the elastic limit represents the maximum stress for no creep. A sensitive extensometer was constructed, and creep tests were made on zinc single crystals at a variety of loads and temperatures1. It was soon discovered that there is no measurable elastic limit in ductile zinc single crystals at, or above, room temperature. The inference that pure metallic single crystals may not possess a definite elastic range was not justified, however, since zinc had been tested in creep only above its recrystallization temperature, and several investigator2,3,4 had already shown that above the recrystallization temperature polycrystalline metals will flow under very small stresses, while below that temperature stresses of a much larger magnitude are required. For that reason, it was decided to extend the study of the elastic limit to other metals having a higher recrystallization temperature than zinc. Aluminum and silver were selected, because of the ease of obtaining pure materials and of preparing large single crystals, and because the crystallo-graphic glide system of these metals is well known. Owing to the limited time available, the elastic range was investigated by slow tensile tests rather than by creep tests. Production of Specimens A luminum Recrystallized single crystals were prepared from 99.95 per cent aluminum supplied by the Aluminum Company of America. The ingots were melted in an Acheson graphite crucible in a gas furnace, and cast