Papers - Grain Growth in Normalized Sheet Steel during Box Annealing (T. P. 941, with discussion).

In a recent paper the authors1 discussed the reactions to tempering of hypereutectoid steels quenched from 1000' C., as revealed by studies on changes in hardness, electrical resistivity, coercive force and metallo-graphic charaeteristics. The data, which related specifically to tempering temperatures of 550°, 650" and 710" C., for varying periods up to 125 hr., permitted the following important conclusions: 1. The rate of softening of the steels at the temperatures examined differed markedly although the steels were of "similar" general chemical composition. 2. The temperature of maximum softening spread over a range from about 650" C, to the eutectoid inversion. 3. The divergence in behavior was ascribed, at least in part, to a profound difference in tendency to graphitization on annealing at sub-eutectoid temperatures. 4. The mode of spheroidization of the cementite, as revealed by metallographic studies, also varied considerably in the different steels. The purpose of the present investigation is to pursue further the study of the difference in behavior of the steels on tempering over a wider range of temperature. To this end the following features have received particular attention: 1. Comparison of temperatures of maximum softening of the various steels when the quenched samples were tempered for 5 hi. and for 75 hr. followed by furnace cooling and by quenching in water. 2. Deterrnirlation of the effect of quenching temperature, prior to tempering, on the rate of softening. Quenching temperatures of 1000" and 850" C. were used in the investigations. 3. Examination of the microstructures obtained with the various heat-treatments employed.