Papers - Effect of Cold work upon Hardness and Recrystallizing Behavior of Pure Platinum (T. P. 1167, with discussion)

It is known qualitatively that the recrystallization behavior of platinum is dependent upon the amount and particularly the nature of impurities present, the amount of prior cold-work and the annealing time and temperature, but published data are limited. A study of the effects of cold-work and annealing temperature on the hardness of a sample of very pure platinum was undertaken to supply part of this information. Conclusions 1. The platinum used in the experiments had a probable platinum content of 99.99+ per cent, and had the following mechanical properties in the completely softened condition: Vickers hardness number, 39.4; ultimate tensile strength, 19,340 lb. per sq. in.; proportioilal limit, very low; elongation, 37.5 per cent in 2 inclles. 2. The effect of cold-rolling on the hardness is shown in Fig. 1. The hardness increases rapidly up to 10 to 15 per cent reduction and more slowly up to about 75 per cent reduction, beyond which it increases more rapidly. 3. The recrystallization temperatures for a 15-min. anneal, after cold-rolling 19, 39.5, 50.8, 66, 80.5 and 89.5 per cent reduction in thickness, are approximately 765°, 700°, 635°, 600°, 545' and 425°C., respectively. 4. The recrystallized grain size of this platinum is a function of the percentage of cold reduction, being larger the lower the percentage of cold-work. 5. Little or 110 grain grourtll resulted from subjecting recrystallized samples to higher temperatures or annealing for longer times. Prior Work As already mentioned, data on the recrystallization of platinum are scarce. Gmelin'sl handbook, which summarizes data published earlier than August 1938, lists values ranging from 400' to 810°C. for the minimum temperature of recrystallization of samples with rather indefinite