Papers - Creep and Fracture Tests on Single Crystals of Lead (With Discussion)

For several years there has been in progress in the Materials Testing Laboratory of the University of Illinois an investigation of creep and fracture of lead and lead alloys. In the course of this investigation it has been shown that the phenomenon of creep occurs in part at the grain boundaries of lead and lead alloys. To study the occurrence of creep and the development of fracture within crystalline grains, two series of tests of single crystals of lead have been carried out. The first of these, a preliminary series, by Mr. Betty, has been described.l,2 The second, pursued by Mr. Baker for his doctoral dissertation, was carried out under the direction of Professor Moore, with the assistance of Prof. G. L. Clark in the X-ray work, and the cooperation and advice of Mr. Betty. This paper is based on the test data obtained in this second series. Single crystals of a very pure commercial lead have been prepared, some of them tested to measure creep, others tested to fracture under long-continued steady load, and still others tested under cycles of repeated tension. An interpretation of the test data of these single-crystal tests is offered, which is a combination of parts of several well-known theories. Specimens The single-crystal specimens were made from a piece of very pure commercial lead sheathing. A spectroscopic analysis of one of the single crystals showed the presence of 0.005 per cent Bi, 0.0001 per cent Cu and 0.0003 per cent Ag. Preparation.—The Bridgman method of casting single-crystal specimens was used.3 The specimens were cast to the shape and size shown in Fig. 1 (dimensions in Fig. 4c) in a duralumin mold. Molten lead does not stick to duralumin. Fig. 1 shows the mold and the blast flames for heating. After the mold had been heated to the temperature of molten