New York Paper - Temperature Problems in Foundry and Melting Room

Considerable work has been done in developing a pyrometer to measure the temperature of molten brasses, bronzes, and aluminum in the crucible. On account of the high melting points and the amount of zinc and sulfurous fumes given off from molten brasses, the conditions are somewhat severe for a thermocouple of standard design; but satisfactory results are obtained with a portable pyrometer, 3 ft. (0.9 m.) of connecting lead wire, and a special 5-ft. nickel-nickel chromium thermocouple, composed of rods 1/4in. (6.35 mm.) in diameter. The lower 12 or 24 in., as desired, may be made detachable so that new tips may be connected at little trouble or expense. The portable instrument need not be of the extreme high-resistance type, as the movable parts of the galvanometer of a lower resistance instrument may be better constxucted to withstand the continuous handling such an instrument receives. Platinum-platinum rhodium thermocouples, protected with porcelain and graphite tubes, have been used, but the lag in registering the temperature is too great. It has been found that the range of temperature for various brasses is as follows: Red brasses...............2200-2250" F. (1205-1234" C.) Yellow brasses............2250-2400" F. (1234-1318' C.) Bronzes..................2300-2550" F. (1260-1400" C.) A recent test with a portable pyrometer having a range of 2600" F. with a bare 1/4 in. heavy exposed couple 5 it. long and a handle attached at the upper end showed that the temperatures of molten aluminum under varying conditions in an oil-fired crucible furnace and one of the Simplex type were as follows: CRUCIBLE, OIL-FIRED FURNACE SIMPLEX FURNACE Temperature of metal in furnace....... 1540" F. (837" C.) 1530" F. (834" C.) Temperature in ladle after skimming at furnace......................... 1480" F. (805" C.) 1440" F. (784" C.) Temperature in ladle after skimming at floor near mold................... 1440" F. (784" C.) 1430' F. (778" C.)