Minerals Beneficiation - Grangcold Pellet Process

A new method is described for the production of cold-bonded pellets using a hydraulic binder, such as portland cement. Large-scale pilot-plant tests have proved that self-fluxing pellets of high reducibility and good handling strength can be made by the method. Blast-furnace trials have shown that the pellets are an acceptable burden material, comparable with self-fluxing sinter or heat-hardened pellets. Economic factors of commercial-scale production are discussed. The Grangcold Pellet Process—for which patents have been applied or already granted in a number of coun-tries—uses a hydraulic adhesive such as portland cement, slag cements, pozzolanic cements, etc., for the production of cold-bonded pellets. The idea of using a hydraulic binder for the agglomeration of iron-ore fines is not new. Portland cement was proposed as an adhesive for cold-bonded iron-ore briquettes in patents granted more than 50 years ago.' In a report on the briquetting of iron-ore fines, published in Stahl und Eisen in 1959; it is stated that briquettes bonded with portland cement are used on a small scale at an ironwork in Germany. According to the report, the briquettes showed excellent strength in the blast furnace although their general use was made impossible because they required a long hardening time, during which they are sticky, soft, and difficult to store and handle. The Grangcold Pellet Process has overcome this particular disadvantage by mixing the balls with a suitable amount of the balling concentrate before storing them. The pellets are embedded in the concentrated during storing in such a way that they are isolated from each other and thus prevented from sticking together to form clusters. Thanks to the embedding concentrate, the pellets are subjected to a more or less uniform pressure from all sides which does not deform them. Thus, the mixture can be stored in a stockpile or in a bin until the pellets have hardened sufficiently. The concentrate is separated from the pellets by means of screening. The concentrate is returned to the balling operation and the pellets are either shipped to the blast furnace or stored for final hardening. The binder preferred for the Grangcold Pellett Process is portland-cement clinker, ground without the admixture of gypsum in order to avoid sulfur in the pellets as far as possible. Usually a 10% binder content is used. Two-thirds of the portland-cement clinker consist of lime and the rest is silica, alumina, and ferric oxide. Thus, self-fluxing or overbasic pellets are produced with this binder if the amount of silica in the concentrate used does not exceed 4%. The Grangcold Pellet Process was developed by the mineral Processing Laboratory of the Granges Co. Work started in 1963 with batch-scale tests. In 1966, a small pilot plant was put into operation in which 1800 tons of pellets were produced using 10% of rapid-hardening portland cement as a binder. Favorable results from a blast-furnace test with this batch led to the decision to erect a larger pilot plant which went into production in the summer of 1967. Since then, approximately 100,000 tons of cold-bonded pellets have been produced, mostly with 10% gypsum-free portland cement as a binder. Several full-scale blast-furnace trials have been performed with the pellets. The results of the trials indicate that the Grangcold pellets constitute a satisfactory blast-furnace feed. An industrial plant for the production of Grangcold pellets with a rated capacity of 1.5 million tpy is now under construction at the Granges Co.'s mine at Grangesberg. The plant will come into operation in the summer of 1970. Results from Laboratory Work Pellets made from iron-ore concentrate bonded with portland cement harden slowly and their handling is very critical until they have hardened enough to loose their stickiness. It is therefore especially important to study the progress of the hardening action and the factors influencing it. This is best achieved by investigating the relationship between the compressive strength of the cement-bonded pellets and the curing time under varied conditions. The general course of this relation-