Microstructure Of Iron And Mild Steel At High Temperatures

THE METHOD of demonstrating the structure existing in a metal or alloy at high temperatures, by etching a polished sample after it has been heated to the desired temperature, is quite familiar to metallographists. The usual procedure1,2 is to heat the specimen, previously polished for microscopic examination, to the desired temperature, in a neutral atmosphere (hydrogen or nitrogen), then admit the etching gas. (chlorine, hydrochloric acid or similar gas) for. a few seconds, and finally, after flushing out the etching gas with the neutral one, cool the specimen in the neutral atmosphere. The pattern produced by etching at a definite temperature is usually taken as a record of the microstructure prevailing at that temperature. It has frequently been pointed out that changes in composition of the surface metal occur during the preliminary heating in the neutral atmosphere, so that the appearance produced' by the etching at high temperature may not exactly represent the condition of the interior of the specimen. To overcome this uncertainty, the heating has sometimes been done in vacuo,3 the etching gas being ad-mitted when the desired temperature was reached, then pumped out and the specimen cooled in vacuo.