Microstructure and Mechanical Properties of Twin-Roll Cast Al-Mg Based Alloys

Al - 5.5 wt% Mg - 0.3 wt% Cu alloy strip was successfully fabricated by horizontal-type twinroll casting (TRC). For producing sound strips with no surface defect, the casting was conducted at various roll rotation speed, and the sound strip could be obtained at relatively low casting speed (3 rpm). The cast strip was homogenized at 450 °C for 10 hours, and then cold rolled with a reduction rate of 78%, followed by a final annealing at 450 °C for 1 hour. The annealed sheets showed good mechanical properties with approximately 330 MPa in tensile strength and 27 % in elongation, but exhibited strong anisotropy depending on the tensile directions. For the homogenized sheets, warm rolling was also conducted at 200, 300, and 400 °C. The tensile test results of the warm-rolled sheets showed that the rolling at medium temperature (300 °C) was proper to fabricate the sheets with relatively good mechanical properties and low anisotropy.