Mesoporous Silica Coatings through Triblock-Copolymer Templated Processing

"Ongoing research is reported aimed at improving the properties of mesoporous silica-based coatings on various substrates for optoelectronic or medical applications. Tetraethylorthosilicate (TEOS) was selected as the silica precursor, and amphiphilic triblock copolymers poly( ethylene oxide)- poly(propylene oxide)poly( ethylene oxide) as the surfactant micellar template or structure-directing agents. Cetyltrimethylammonium chloride (CTAC) was also used as a control agent. The effect of the templating agent and type of substrate (glass, Si, and Ti) on the mesoporosity, particularly on the alignment of the mesochannels, has been investigated. Three · different treatments (thermocalcination, photocalcination, and solvent extraction) have been also studied to remove the organic templates.IntroductionThe fabrication of mesoporous silicate-based materials through the utilization of a sol-gel process, where cooperative organization of organic and inorganic species takes place, provides a versatile approach to nanoscaled structures with potential applications in fields such as catalysts, optoelectronics, biomaterials, etc. Compared to conventional low molecular weight surfactants, self assembly of amphiphilic·block copolymers can result in mesostructured materials with larger pore sizes (up to 30 nm).1 Most of the synthetic strategies use silicon alkoxides as the silica precursor, although non-silicate metal alkoxides, e.g; Ti, Zr, Al, and B, have been also used to obtain different mesoporous materials, or even mixed metallic oxide systems. 2 Recently, Yang et al. 3 • 4 were able to synthesii:e a great variety of mesoporous metal oxides ID nonaqueous media using inorganic precursors (metal chlorides) and block copolymers as structure-directing agents."