Mechanical Activation Of Monazite Processing By Simultaneous Ball-Milling And Leaching

The present work deals with a study of the mechanical activation of processing of Egyptian monazite by its simultaneous ball-milling and pressure leaching in order to improve the recovery of thorium and lanthanides from monazite. Experiments of simultaneous ball-milling and alkaline leaching of monazite contrary to autoclave leaching were carried out in stainless steel ball-mills of cylindrical shape under different conditions of temperature, pressure, time and alkali amount and strength. The ball-mills were heated and mechanically rotated in an electric furnace by means of roll mechanism. The effective rotation speed was fixed at 130 rpm in all tests. The charge of steel balls of different diameters was equivalent to 45% of the total mill volume. Monazite was charged in ball-mill without preliminary grinding. It is found that high rate of monazite leaching by ball-milling leaching method is achieved at lower temperature, shorter time and lower expense of alkali than in autoclaves. The results obtained show that complete recovery of thorium and lanthanides from monazite (99.8%) by simultaneous ball milling and alkaline leaching is attained at 140°C within 2 h. It is concluded that processing of monazite by its simultaneous ball-milling and leaching is mechanically activated and accelerated as a result of grinding action of steel balls that caused the continuous removal of the hydroxide product from reacting particle surfaces. This leads to the exposing of fresh and activated monazite particles surfaces to alkali leach solution and consequently the acceleration of the reaction of monazite processing.