Low-Temperature Pressure Leaching Kinetics of Zinc Sulphide Concentrate

"The leaching kinetics of zinc sulphide concentrate was studied under total pressures ranging from 0.3 MPa to 0.5 MPa and leaching temperatures ranging from 358 K to 378 K. The apparent activation energy of leaching reaction under different total pressures was calculated. The results show that for the extraction of zinc at low-temperature pressure leaching is controlled by an interfacial chemical reaction. This was supported mineralogical analysis of the leaching residue. The kinetic equation for low-temperature pressure leaching of zinc sulphide concentrate was further established by quadratic regression on the basis of shrinking core model.INTRODUCTIONThe Roast-Leach-Electrowinning Process (RLE) is the primary route for zinc production and responsible for more than 85% of the total zinc production (Souza et al., 2007). During the roasting of zinc concentrates, fugitive SO2 causes pollution. The prevention of SO2 emissions from the RLE process can be one of the challenges to this technology (Deller, 2005). In the 1980s, the Zinc Pressure Leach (ZPL) process changed the concept of zinc hydrometallurgy, in which zinc sulphide concentrate is directly leached at approximately 423 K and approximately 0.7 MPa oxygen overpressure and the sulphidic sulphur is oxidized into elemental sulphur so that the pollution by SO2 is completely avoided. Since 1981, five zinc plants have adopted the ZPL process either for expansion by integration with existing roasting facilities, or for the production of zinc without any roasting at all (Collins et al. 1994; Barth et al. 1998). The innovation of the ZPL process has made the zinc industries more competitive although it needs an autoclave. The direct leaching technology of zinc is still in development."