Investigation of Pyrometallurgical Nickel Pig Iron (Npi) Production Process from Lateritic Nickel Ores

"Nickel is mainly used in stainless steel production as ferronickel. In recent years, low grade ferronickel or nickel pig iron (NPI) is used in stainless steel production to reduce expenditure of nickel price. In this study, Turkey East Anatolian region lateritic nickel ores were directly introduced carbothermal reduction to produce NPI. Firstly the raw lateritic ore that contains 0.9% Ni, 0.054% Co and 2.3% Cr was mixed with metallurgical grade coal at different stiochometric ratios. The samples were smelted at 1600-1650 °C temperature range in an induction furnace for 25 min. In the second experimental set, different processes times were carried out from 15 to 35 min. The raw material, obtained alloys and slags were analyzed by using XRD (X-Ray Diffractometer), XRF (X-Ray Fluorescence Spectrometer), AAS (Atomic Absorption Spectrometer) and EPMA (Electron Probe Micro Analyzer) techniques.IntroductionNickel is an important element that has many application areas in the industry and there are a lot of kinds of nickel products such as refined metal, powder, sponge etc. 65% of metallic nickel is used in stainless steel, 12% is consumed as superalloy and non ferrous alloy because of its superior corrosion and high temperature properties [1].Nickel is a transition metal that is mined from mainly two types of ore deposits as sulphide ores and lateritic ores. Although 73% of nickel ores are laterites, 55% of primary production is from sulphide ores [1, 2]. The importance of lateritic ores is increasing due to the increase in nickel prices and decrease in reserves of sulphide ores.There are pyrometallurgical, hydrometallurgical and combined (pyro-hydrometallurgical) methods which are used for the extraction of nickel from lateritic ores. HPAL (High temperature pressure acid leaching) is generally used to recover nickel and cobalt from laterite nickel ores. It is suitable for the plants processing ores with low magnesium oxide and aluminum oxide content. Lateritic ores are exposed to hot acidic leaching around ~250 °C to dissolve cobalt and nickel under high pressure. The main disadvantage for HPAL is the high cost of titanium autoclaves. Process is complex and difficult to control due to the high pressure and heating of the process [2, 3 and 4]."