Institute of Metals Division - The Nature of the Fiber-Texture Component in Extruded Aluminum Rods

The (001) fiber-texture component, found in aluminum rods extruded at subzero temperatures, consists of particles of various sizes having extremely irregular shapes dispersed in a nonuniform way throughout a matrix of the (111) orientation. Apparently the (001) texture component is not a result of recrystallization but rather is due to the presence of reimanents of the original grains which fragmented from the main body of material as it reoriented towards the (111) orientation during the extrusion process. Both X-ray line-broadening measurements and electron-microscopic observatwns indicate that, after extrusion, regions having (001) orientations are in a state of relatively less strain and distortion than (111) regions, suggesting that the former have undergone less plastic deformation. A (001) fiber-texture component is also found after complete recrystallization of extruded specimens. Approximately one third of the recrys-stallized volume has this orientation. The (001) fragments, formed during the extrusion process, act as nuclei for recrystallization; i.e., the pain boundaries separating these fragments from the matrix are capable of migrating during annealing. Electron-transmission microscopic observations and X-ray line-broadening measurements indicate that (001) regions recover at a much more rapid rate than (111) regions at annealing temperatures up to 187°C. DURING the extrusion of a rod or the drawing of a wire the individual grains comprising the piece tend to reorient towards a preferred orientation (texture) which is of the fiber type where a particular crys-tallographic direction, (uvw), in each crystallite tends to be aligned parallel to the longitudinal axis