Institute of Metals Division - The Diffusivity and Solubility of Carbon in Alpha-Iron

The rate of motion of the boundary between a single-phase a-iron region and a two phase a-iron plus ?-iron, or a-iron plus cementite region has been measured on decarburization at several temperatures between 500" and 865°C. These data, together with data for the carbon content of a-iron at the boundary, yield the diffusivity of carbon in a-iron. The activation energy for carbon diffusion is 19.8 kcal per mole for the temperature range —50° to 150°C and increases to an average value of 23.0 kcaL per mole for the temperature range 727" to 865°C. AS part of an investigation of the diffusivity of carbon in iron using a steady-state method,' the diffusivity of carbon in a-iron was determined at the temperatures 802" and 851°C. The diffusion constant thus obtained was larger, by nearly a factor of two, than that predicted from the combined results of stanley2 and of Wert.3 It seemed desirable, therefore, to continue the investigation. Since the temperature range in which the steady-state method can be conveniently used is limited, we have chosen a decarburization method, based on the laws of diffusion in metal accompanied by a phase change.4,5 If the initial carbon content of the Fe-C alloy is such that two phases coexist at the decar-burizing temperature* and decarburization is car- ried out such that the surface is maintained at substantially zero wt pct. C, the carbon distribution after a time, t, will be as shown in Fig. 1. The boundary between the single-phase and two-phase regions moves from y = 0 to y = x in the time, t, where x is proportional4 to tl". If the initial carbon (content of the sample is Ci, and CB is