Institute of Metals Division - Influence of Cobalt on the Transformation of a Chromium Alloyed Austenite

The TTT curves of 0.1 pct C, 13 pct Cr steels containing up to 12 pct Co have been determined in order to establish whether the effect of cobalt is similar to that observed m plain carbon steels. It is shown that cobalt increases the incubation time and decreases the transformation rate, though not in an uniform way. The bainitic transfornation is displaced to lower temperature and overlaps partially the martensitic zone. ThE effect of cobalt on the transformation of a plain carbon austenite has been studied by many investi-gators.'-3 It was shown that cobalt displaces the TTT curves to shorter times and diminishes the harden-ability. The interpretations given for this effect of cobalt are conflicting. According to E. Houdremont,4 cobalt increases the transformation rate of austenite because it increases the diffusion of carbon as shown in the experiments of E. Houdremont and H.Schrader,' R.Smoluchowski,5 and M. Blanter.6 On the other hand, M. Hawites and R. Mehl3 deny on the basis of their own experiments any effect of cobalt on the diffusion of carbon and they assume that an explanation should be found in an eventual effect of cobalt on the mechanism of nucleation and growth of pearlite. W. C. Hagel, G. M. Pound, and R. F. Mehl7 have shown by calorimetric measurements that cobalt increases the free energy of the austenite-pearlite transformation in an eutectoid steel and this result explains qualitatively the observed effect of cobalt on the rate of nucleation and growth of pearlite. The purpose of this research was to see by determination of TTT curves, if this same effect exists in 13 pct Cr steels. EXPERIMENTAL PROCEDURES The preparation of the alloys was carried out in an